Nkas mixed shell fabric processing method and processing device thereof

A processing method and processing device technology, applied in the textile field, can solve the problems of reducing fabric flexibility and tension, complicated fabric preparation process, and easy pilling

Inactive Publication Date: 2015-06-24
ZHEJIANG YANA TEXTILE
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, the relatively strong fabrics used by people are prone to static electricity.
At the same time, the soft fabric is prone to pilling
[0006] The Chinese patent No. "201020157472.5" is called "a kind of fabric", which provides a processing method for cut-resistant fabrics. The fabric is divided into three layers, and the middle bonding layer is a metal mesh woven with metal wires, which can effectively Preventing the fabric from being cut by a sharp edge greatly improves the safety performance of the handbag, but the metal mesh inside increases the weight and cost of the fabric, and at the same time reduces the flexibility and tension of the fabric, which affects the comfort of people using it. Fabric preparation process is complex, not suitable for mass production of fabrics
[0008] However, it is only a fabric with a single-layer structure, and its strength is insufficient
Moreover, due to the fact that it is made of cotton, it is easy to fluff

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nkas mixed shell fabric processing method and processing device thereof
  • Nkas mixed shell fabric processing method and processing device thereof
  • Nkas mixed shell fabric processing method and processing device thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0081] Such as figure 1 As shown, the Enca silk mixed fabric includes an inner fabric 1, an intermediate bonding layer 2 and a surface fabric 3, and the intermediate bonding layer 2 is located between the inner fabric 1 and the surface fabric 3 and the three are fixed together.

[0082] The processing method of Bennka silk mixed fabric comprises the following steps:

[0083] A. Making the inner layer fabric 1, the middle adhesive layer 2 and the surface layer fabric 3: the surface layer fabric 3 is a fabric containing 70% Enka fiber.

[0084] In step A, the main manufacturing process of inner layer fabric 1 is:

[0085] 1. Select 70% Enka fiber and 15% nylon fiber, and produce 70% Enka silk through the ordinary mixed thread preparation method;

[0086] 2. Put the Enca silk on the warp and weft loom to weave the surface fabric, the thickness of the prepared surface fabric is about 0.4mm, and the warp and weft weaving density is 160*200. In this embodiment, the count of the U...

Embodiment 2

[0109] Such as figure 1 As shown, the Enca silk mixed fabric includes an inner fabric 1, an intermediate bonding layer 2 and a surface fabric 3, and the intermediate bonding layer 2 is located between the inner fabric 1 and the surface fabric 3 and the three are fixed together.

[0110] The processing method of Bennka silk mixed fabric comprises the following steps:

[0111] A. Making the inner layer fabric 1, the middle adhesive layer 2 and the surface layer fabric 3: the surface layer fabric 3 is a fabric containing 85% Enka fiber.

[0112] In step A, the main manufacturing process of inner layer fabric 1 is:

[0113] 1. Select 85% Enka fiber and 30% nylon fiber, and produce 85% Enka silk through the ordinary mixed thread preparation method;

[0114] 2. Put the Enca silk on the warp and weft loom to weave the surface fabric, the thickness of the prepared surface fabric is about 0.4mm, and the warp and weft weaving density is 160*200. In this embodiment, the count of the U...

Embodiment 3

[0137] Such as figure 1 As shown, the Enca silk mixed fabric includes an inner fabric 1, an intermediate bonding layer 2 and a surface fabric 3, and the intermediate bonding layer 2 is located between the inner fabric 1 and the surface fabric 3 and the three are fixed together.

[0138] The processing method of Bennka silk mixed fabric comprises the following steps:

[0139] A. Making the inner layer fabric 1, the middle adhesive layer 2 and the surface layer fabric 3: the surface layer fabric 3 is a fabric containing 80% Enka fiber.

[0140] In step A, the main manufacturing process of inner layer fabric 1 is:

[0141] 1. Select 80% Enka fiber and 20% nylon fiber, and produce 80% Enka silk through the ordinary mixed thread preparation method;

[0142] 2. Put the Enca silk on the warp and weft loom to weave the surface fabric, the thickness of the prepared surface fabric is about 0.4mm, and the warp and weft weaving density is 160*200. In this embodiment, the count of the U...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to View More

Abstract

The invention provides an Nkas mixed shell fabric processing method and a processing device thereof and belongs to the technical field of textiles. The Nkas mixed shell fabric processing method and the processing device thereof are used for solving the problems of the existing shell fabrics that the strength is not high and fluffing is easy. The Nkas mixed shell fabric processing method comprises the following steps: (A) manufacturing a lining shell fabric, a middle bonding layer and a surface layer shell fabric; (B) coating glue; (C) laminating the shell fabrics; (D) coating a surface layer; (E) carrying out hot-press sizing. The processing device for the middle bonding layer of an Nkas mixed shell fabric comprises a bracket, wherein the bracket is provided with a conveying belt which can move. The device further comprises a baking furnace and a degumming mechanism, wherein the degumming mechanism is fixedly connected onto the bracket, the conveying belt is located in the baking furnace, both an input end of the conveying belt and an output end of the conveying belt extend out of the baking furnace, and the input end of the conveying belt is located at the lower part of the degumming mechanism. The shell fabric is high in strength and does not fluff.

Description

technical field [0001] The invention belongs to the technical field of textiles, and relates to a processing method of Enca silk mixed fabrics and a processing device used in the processing method of Enca silk mixed fabrics. Background technique [0002] "Enkas" is a cellulose filament produced in Germany, which has high technological content and can be combined with other fibers (such as: cotton, nylon, polyester) to form a new yarn product. This product has unique properties: natural environmental protection, soft and smooth like cashmere, moisture-absorbing and breathable, no static electricity, no pilling, and easier to dye. It is widely used, especially suitable for making high-grade and comfortable fine knitted fabrics. [0003] Nylon is a polyamide fiber commonly known as Nylon (Nylon), the English name Polyamide (abbreviated as PA), and its density is 1.15g / cm3. Fatty - aromatic PA and aromatic PA. Among them, aliphatic PA has many varieties, large output and wide...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B37/06B32B37/12B32B37/18B32B27/12B32B27/40B32B7/12B32B5/26
Inventor 张新宇朱金华
Owner ZHEJIANG YANA TEXTILE