Antistatic surface protection film

A surface protection film, antistatic technology, used in film/sheet adhesives, instruments, synthetic resin layered products, etc., to achieve excellent anti-peeling static performance, less pollution, and achieve the effect of production efficiency

Active Publication Date: 2015-07-15
FUJIMORI KOGYO CO LTD
View PDF10 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the current situation, it is difficult to solve this problem in the conventionally proposed surface protection film using an adhesive layer containing an antistatic agent.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antistatic surface protection film
  • Antistatic surface protection film
  • Antistatic surface protection film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0160] Nitrogen gas was introduced into a reaction apparatus equipped with a stirrer, a thermometer, a reflux condenser, and a nitrogen introduction pipe, thereby replacing the air in the reaction apparatus with nitrogen. Then, added 100 parts by weight of 2-ethylhexyl acrylate, 3.0 parts by weight of 8-hydroxyoctyl acrylate, 10 parts by weight of polypropylene glycol monoacrylate (forming polyalkylene glycol chain The average repetition number of alkylene oxide n=12), and 60 parts by weight of solvent (ethyl acetate) was added at the same time. Then, 0.1 part by weight of azobisisobutyronitrile as a polymerization initiator was dropped over 2 hours, and reacted at a temperature of 65°C for 6 hours to obtain the acrylic copolymer solution of Example 1 with a weight average molecular weight of 500,000. To this acrylic copolymer solution, 8.5 parts by weight of acetylacetone was added and stirred, and then 2.0 parts by weight of Coronate HX (Coronate HX, an isocyanurate of a hex...

Embodiment 2～6 and comparative example 1～2

[0162] Except that each composition of the adhesive composition of Example 1 was adjusted as described in Table 1 and Table 2, the same operation was carried out as in Example 1, and the adhesives of Examples 2-6 and Comparative Examples 1-2 were obtained. binder composition.

[0163] Table 1

[0164]

[0165] Table 2

[0166]

[0167] Table 1 and Table 2 are tables that divide the entire table showing the compounding ratio of each component into two parts, and the values ​​in parentheses all represent parts by weight of each component obtained by setting the total amount of group (A) as 100 parts by weight. value. In addition, the compound names corresponding to the abbreviations of the components used in Table 1 and Table 2 are shown in Table 3 and Table 4. In addition, Coronate (コロネート, registered trademark) HX, Coronate HL, and Coronate L are trade names of Nippon Polyurethane Industry Co., Ltd. (Nippon Polyurethane Industry Co., Ltd.), and Takenate (タケネート, registe...

Embodiment 2～6

[0183] The antistatic surface protection films of Examples 2 to 6 were obtained in the same manner as in Example 1, except that each adhesive composition of Example 1 was adjusted to the adhesive compositions of Examples 2 to 6. .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides an antistatic surface protection film, the pollution to a pasted body is light, and the antistatic surface protection film is provided with excellent anti-stripping electrostatic properties without time dependent degradation. The antistatic surface protection film is formed in a way that a binder layer (2) composed of a binder composition is formed on one side of a base film (1) formed by a transparent resin, the binder composition comprises an acrylate-based polymer containing copolymers, (F) an isocyanate compound containing more than two functional groups, (G) a crosslinking accelerator and (H) a ketone-enol tautomer compound, a stripping agent layer (4) containing an antistatic agent is laminated on one side of a resin film (3) to form a stripping film (5), and the stripping film (5) is attached to the surface of the binder layer (2) through the stripping agent layer (4). The stripping agent layer (4) is formed by a resin composition, and the resin composition comprises a stripping agent taking dimethyl polysiloxane as the key component, a polysiloxane compound which is liquid under 20 DEG C and an antistatic agent, and the stripping electrostatic pressure of the binder layer (2) is lower than + / -0.6kV.

Description

technical field [0001] The present invention relates to an antistatic surface protective film bonded to the surface of optical components (hereinafter, sometimes referred to as "optical film") such as polarizing plates, retardation plates, and lens films for displays. More specifically, there is provided an antistatic surface protection film that has less contamination to an adherend, does not deteriorate over time, and has excellent anti-peeling static performance. Background technique [0002] At present, when manufacturing and transporting optical films such as polarizing plates, retardation plates, lens films for displays, anti-reflection films, hard coat films, transparent conductive films for touch panels, and optical products such as displays using them, A surface protective film is bonded to the surface of the optical film to prevent surface contamination and scratches in subsequent steps. In order to improve work efficiency by saving the labor and time of peeling o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/02C09J151/08C09J133/08C09J11/06G02B1/16
CPCB32B7/02B32B7/06B32B7/12B32B27/08B32B38/10
Inventor 长仓毅岛口龙介长谷川良小林弘幸春日充新见洋人
Owner FUJIMORI KOGYO CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com