Polypropylene material with high strength and good moldability

A polypropylene material and formability technology, applied in the field of polypropylene materials, can solve the problem of difficult to meet high strength and better formability at the same time, and achieve improved mechanical properties, easy forming, high strength and easy formability. Effect

Inactive Publication Date: 2015-08-19
SUZHOU XISHIDA PLASTIC CO LTD
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, as an important part of engineered polypropylene materials in the automotive field, automotive bumpers, various automotive interior parts, and instrument panels made of engineered polypropylene materials, although their performance in all aspects Both can meet the corresponding requirements, but it is difficult to meet the two requirements of high strength and better formability at the same time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Embodiment 1: A polypropylene material with high strength and good formability, in parts by weight, comprising:

[0028] Polypropylene 58 parts

[0029] Talcum powder 35 parts

[0030] 24 parts glass fiber

[0031] Toughener 3 parts

[0032] 0.3 parts of coupling agent

[0033] Lubricant 0.35 parts

[0034] Heat stabilizer DSTP 0.5 parts

[0035] Heat stabilizer 3114 0.5 parts

[0036] Heat stabilizer 618 0.35 parts

[0037] Fatty acid ester compound 2 parts

[0038] Nano zinc oxide 1.8 parts

[0039] Nano titanium dioxide 2 parts

[0040] Wherein, the particle size range of the talc powder is 1-10 microns. The intrinsic viscosity of the polypropylene is 10. The glass fiber is an alkali-free glass fiber, and the toughness and rigidity of the polypropylene material are improved by adding the glass fiber. The coupling agent increases the interfacial bonding force between the glass fibers and the polypropylene matrix. The lubricant is ethylene bis stearamide, ...

Embodiment 2

[0044] Embodiment 2: A kind of polypropylene material with high strength and good formability, by weight parts, comprising:

[0045] Polypropylene 56.2 parts

[0046] Talcum powder 30 parts

[0047] 22 parts glass fiber

[0048] Toughener 2 parts

[0049] 0.2 parts of coupling agent

[0050] Lubricant 0.2 parts

[0051] Heat stabilizer DSTP 0.1 parts

[0052] Heat stabilizer 3114 0.1 parts

[0053] Heat stabilizer 618 0.1 part

[0054] Fatty acid ester compound 0.5 parts

[0055] Nano Zinc Oxide 0.5 parts

[0056] Nano titanium dioxide 0.5 parts.

Embodiment 3

[0057] Embodiment three: a polypropylene material with high strength and good formability, in parts by weight, comprising:

[0058] Polypropylene 60 parts

[0059] Talcum powder 40 parts

[0060] 26 parts glass fiber

[0061] Toughener 4 parts

[0062] 0.4 parts of coupling agent

[0063] Lubricant 0.5 parts

[0064] Heat stabilizer DSTP 1.0 parts

[0065] Heat stabilizer 3114 1.0 parts

[0066] Heat stabilizer 618 0.5 parts

[0067] Fatty acid ester compound 3 parts

[0068] Nano zinc oxide 3 parts

[0069] Nano titanium dioxide 3 parts.

[0070]The present invention is a polypropylene material with high strength and good formability, including polypropylene, talcum powder, glass fiber, toughening agent, coupling agent, lubricant, heat stabilizer DSTP, heat stabilizer 3114, and heat stabilizer; Compared with the prior art, the present invention has higher mechanical strength, is easy to form, has greatly improved dimensional stability, and has excellent comprehensiv...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The present invention relates to a polypropylene material with high strength and good moldability. The polypropylene material is characterized by comprising the following components in part by weight: 56.2-60 parts of polypropylene, 30-40 parts of talcum powder, 22-26 parts of glass fibers, 2-4 parts of a flexibilizer, 0.2-0.4 part of a coupling agent, 0.2-0.5 part of a lubricant, 0.1-1.0 part of a heat stabilizer DSTP, 0.1-1.0 part of a heat stabilizer 3114 and 0.1-0.5 part of a heat stabilizer 618. Compared with the prior art, the polypropylene material according to the present invention has higher mechanical strength and besides, is easy to mold, the size stability is substantially improved, and the combination property is excellent.

Description

technical field [0001] The invention relates to a polypropylene material, in particular to a polypropylene material with high strength and good formability. Background technique [0002] In recent years, due to the rapid development of engineering modification technology of polypropylene materials, its application in the automotive field has become more and more extensive. However, as an important part of engineered polypropylene materials in the automotive field, automotive bumpers, various automotive interior parts, and instrument panels made of engineered polypropylene materials, although their performance in all aspects Both of them can meet the corresponding requirements, but it is difficult to meet the two requirements of high strength and good formability at the same time. This is because high strength means high impact, while formability is determined by fluidity, and impact and fluidity are often contradictory. [0003] Therefore, how to solve the deficiencies in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L23/08C08K13/04C08K7/14C08K3/34C08K3/22C08K5/372C08K5/521
CPCC08L23/12C08L2201/08C08L2205/02C08L23/0815C08K13/04C08K7/14C08K3/34C08K5/20C08K2003/2296C08K2003/2241C08K5/10C08K5/372C08K5/523C08K5/524
Inventor 华昊
Owner SUZHOU XISHIDA PLASTIC CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com