Oil-proof abrasion-resisting rubber

A wear-resistant rubber and oil-resistant technology, which is applied in the field of oil-resistant and wear-resistant rubber, can solve the problems that the inner liner of the marine oil-absorbing hose cannot be used, and the oil-resistant and wear-resistant performance cannot be achieved, so as to meet the performance requirements and have good oil-resistant and wear-resistant performance. Effect

Inactive Publication Date: 2015-09-09
JIANGSU HUASHEN SPECIAL RUBBER PRODS
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the oil resistance and wear resistance of traditional ordinary rubber cannot meet this requirement, so it cannot be used in the manufacture of the inner lining layer of marine oil suction hose

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0023] An oil-resistant and wear-resistant rubber used for the inner lining of marine oil-absorbing hoses, which contains the following substances by mass:

[0024] Carboxyl terminated liquid nitrile rubber 70

[0025] Nitrile (1041) rubber 50

[0026] Octylphenol resin 5.5

[0027] Zinc oxide 5

[0028] Stearic acid 1.5

[0029] N-cyclohexyl-2-benzothiazole sulfenamide 1.0

[0030] Dibenzothiazole disulfide 0.6

[0031] Dimethylthiuram disulfide 0.2

[0032] N-isopropyl-N'-phenyl-p-phenylenediamine 1.2

[0033] 2,2,4-Trimethyl-1,2-dihydroquinoline 1.2

[0034] Carbon black N660 70

[0035] Dibutyl phthalate 6.0

[0036] Sulfur 1.2

[0037] Among them, carboxyl-terminated liquid nitrile rubber is American Emerald carboxyl-terminated liquid nitrile rubber; nitrile (1041) rubber is 1041 nitrile rubber produced in Nandi, Taiwan; octyl phenolic resin is produced by Wuxi Binwang Chemical Factory; zinc oxide is produced in Yangzhou Produced by Zhenzhong Zinc Industry Co.,...

Embodiment 2

[0040] Yet another oil-resistant and wear-resistant rubber used for the inner lining of marine oil-suction hoses, which contains the following substances by mass:

[0041] Carboxyl terminated liquid nitrile rubber 80

[0042] Nitrile (1041) rubber 60

[0043] Octylphenol resin 5.3

[0044] Zinc oxide 5

[0045] Stearic acid 1.6

[0046] N-cyclohexyl-2-benzothiazole sulfenamide 1.1

[0047] Dibenzothiazole disulfide 0.5

[0048] Dimethylthiuram disulfide 0.3

[0049] N-isopropyl-N'-phenyl-p-phenylenediamine 1.3

[0050] 2,2,4-trimethyl-1,2-dihydroquinoline 1.3

[0051] Carbon black N660 75

[0052] Dibutyl phthalate 6.0

[0053] Sulfur 1.2

[0054] The rubber produced by the above formula is placed in liquid C at 40°C for 40 hours, and the volume expansion rate is 42%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses oil-proof abrasion- resisting rubber which is made of materials comprising end carboxyl liquid butadiene-acrylonitrile rubber, butyronitrile 1041, octylphenolic resin, zinc oxide, stearic acid, N-cyclohexyl-N'-phenyl-p-phenylenediamine, 2,2,4-trimethyl-1,2-dihydroquinoline, carbon black N660, dibutyl phthalate, N-cyclohexylbenzothiazole-2-sulphenamide, dibenzothiazyl disulfide, tetramethyl thiuram disulfide and sulphur. Compared with the prior art, the oil-proof abrasion-resistance rubber has the advantages that volume swelling of the rubber is less than 50% after the rubber is in a 40DEG C solution for 48 hours, oil-proof abrasion-resisting performance is good, and the oil-proof abrasion-resisting rubber is applicable to an inside liner of a marine oil suction hose.

Description

technical field [0001] The invention relates to a rubber, in particular to an oil-resistant and wear-resistant rubber used for the inner lining of marine oil-absorbing hoses. Background technique [0002] The inner liner of the marine oil suction hose is the working surface for transporting crude oil or liquid petroleum products. There are certain requirements for the oil resistance of the rubber used. It is required that the rubber should be placed in C liquid at 40°C for 40 hours, and the volume expansion rate should not exceed 60%. ; At the same time, it needs to be wear-resistant. At present, the oil resistance and wear resistance of traditional ordinary rubber cannot meet this requirement, so it cannot be used in the manufacture of the inner lining layer of marine oil suction hose. Contents of the invention [0003] In order to overcome the above problems, the object of the present invention is to provide an oil-resistant and wear-resistant rubber. Th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L13/00C08L9/02C08K13/02C08K3/22C08K5/09C08K3/04C08K5/12C08K3/06C08K5/18
Inventor 张东海王仁俊王嘉瑜徐旭张玲
Owner JIANGSU HUASHEN SPECIAL RUBBER PRODS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap