Matt polycarbonate styrene resin alloy and preparation method thereof
A styrene resin and styrene resin technology, which is applied in the field of matte polycarbonate styrene resin alloy and its preparation, can solve the problems of uneven glossiness, insufficient matteness, low glossiness of products, etc. Solve the effects of insufficient extinction, large reduction in gloss, and simple process
Active Publication Date: 2015-09-16
SHANGHAI KUMHO SUNNY PLASTICS
View PDF11 Cites 8 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0009] However, the above-mentioned technical solutions often have deficiencies such as insufficient matteness, large fluctuations in physical and mechanical properties, uneven gloss of the product, and high cost. These defects especially greatly limit the use of polycarbonate styrene resin alloys in automobiles. Applications in the field of accessories
But about a kind of matte polycarbonate styrenic resin alloy with simple process, ultra-low gloss, excellent physical and mechanical properties and its preparation method, there is no report yet
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
preparation example Construction
[0038] Its preparation method comprises the following steps:
[0039] (1) prepare materials according to the components and content;
[0040] (2) Premix the materials prepared in step (1) in a high-speed mixer for 3-10 minutes;
[0041] (3) Pass the premixed material obtained in step (2) through a twin-screw extruder, perform melt extrusion at 230-280° C., cool and granulate to obtain a matte polycarbonate styrene resin alloy.
Embodiment 2
[0044] Embodiment 2 raw material composition
[0045]
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention relates to a matt polycarbonate styrene resin alloy. The matt polycarbonate styrene resin alloy contains following raw material constituents of, by weight part, 50-80 parts of polycarbonate resin, 15-48 parts of polycarbonate resin, 2-5 parts of isocyanate chemical compounds, 0.5-2 parts of compatible agent and 0.5-1 part of processing agent. A preparation method of the matt polycarbonate styrene resin alloy includes following steps: mixing the above raw material constituents in a high speed mixer in advance for 3-10min, and then extruding and granulating the premixed materials through a double screw extruder under 230-280 degree centigrade so as to obtain the matt polycarbonate styrene resin alloy. The matt polycarbonate styrene resin alloy has the advantages that compared with the prior art, no matt master particle needs to be prepared, the polycarbonate styrene resin alloy excellent in matt effect can be directly prepared through a one step method, and the preparation method of the matt polycarbonate styrene resin alloy is simple in technical process, solves the technical problems that glossiness distribution is uneven, physical and mechanical properties are deteriorated, preparation technology is complex and the like, and can reduce cost.
Description
【Technical field】 [0001] The invention relates to the technical field of polymer material processing, in particular to a matte polycarbonate styrene resin alloy and a preparation method thereof. 【Background technique】 [0002] Polycarbonate styrene-based resin alloys have been widely used, and matte surface effects are expected in some fields such as electronic appliances and automotive interior parts, such as computer casings, keyboards, mice, and instruments in automotive interior parts. panels, sun visors, navigator frames, etc. Especially in the field of automotive interiors, in order to avoid the visual disturbance caused by the reflection of sunlight on the driver and reduce the driver's visual fatigue, so as to achieve the purpose of safe and comfortable driving, matting or matte treatment is generally carried out to reduce the interior as much as possible. surface gloss of the piece. Generally, there are mainly the following methods to reduce the surface gloss of i...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L55/02C08L33/20C08L51/00C08K13/02C08K3/22C08K3/04
CPCC08J3/242C08L69/00C08L2205/03C08L55/02C08L51/00C08K5/526C08K5/103C08L33/20
Inventor 季得运周霆罗明华辛敏琦
Owner SHANGHAI KUMHO SUNNY PLASTICS