A cold-resistant, soft, anti-pinhole drilling fleece coating adhesive for textiles and its preparation method

A technology for preventing pinholes and textiles, applied in textiles, papermaking, fiber processing, etc., can solve problems such as polluting the environment and damaging human health, achieve good results, prevent pinhole drilling, and improve fastness

Active Publication Date: 2018-01-09
LIAONING FIXED STAR FINE CHEM
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the coating adhesive of this invention is solvent-based and contains a large amount of solvent. Like pony glue, a large amount of solvent is released during the drying and film-forming process, which pollutes the environment and damages human health. Moreover, this inventive product is only suitable for nylon fabrics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A cold-resistant, soft, anti-pinhole drilling fleece coating adhesive for textiles and its preparation method
  • A cold-resistant, soft, anti-pinhole drilling fleece coating adhesive for textiles and its preparation method
  • A cold-resistant, soft, anti-pinhole drilling fleece coating adhesive for textiles and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Add polyurethane adhesive 85, defoamer 0.4 to the stainless steel kettle and stir at room temperature for 10-30 minutes, add associative polyurethane rheology additive 1.5 and stir for 30-45 minutes, add hand feeling agent 5 and stir for 20-30 minutes, filter out expected product;

[0024] Among them, the polyurethane adhesive: the water-based polyurethane emulsion FS-702 produced by Liaoning Xingxing Fine Chemical Co., Ltd. and the water-based polyurethane electrostatic flocking glue FS-5132 produced by Liaoning Xingxing Fine Chemical Co., Ltd. are uniformly mixed at a weight ratio of 60:25.

Embodiment 2

[0026] Add polyurethane adhesive 90, defoamer 0.3 to a stainless steel kettle and stir at room temperature for 10-30 minutes, add associative polyurethane rheology additive 2.0 and stir for 30-45 minutes, add hand feeling agent 9 and stir for 20-30 minutes, filter out expected product;

[0027] Among them, the polyurethane adhesive: the water-based polyurethane emulsion FS-702 produced by Liaoning Xingxing Fine Chemical Co., Ltd. and the water-based polyurethane electrostatic flocking adhesive FS-5132 produced by Liaoning Xingxing Fine Chemical Co., Ltd. are uniformly mixed at a weight ratio of 64:26.

Embodiment 3

[0029] Add polyurethane adhesive 80, defoamer 0.3 to a stainless steel kettle and stir at room temperature for 10-30 minutes, add associative polyurethane rheology additive 1.5 and stir for 30-45 minutes, add hand feeling agent 7 and stir for 20-30 minutes, filter out expected product;

[0030] Among them, the polyurethane adhesive: the water-based polyurethane emulsion FS-702 produced by Liaoning Xingxing Fine Chemical Co., Ltd. and the water-based polyurethane electrostatic flocking adhesive FS-5132 produced by Liaoning Xingxing Fine Chemical Co., Ltd. are uniformly mixed at a weight ratio of 55:25.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention is a method for preparing cold-resistant, soft and anti-pinhole drilling velvet coating glue for textiles, which is characterized in that the raw materials are mixed according to the weight ratio, and 80-90 polyurethane adhesive and 0.3-0.5 defoamer are stirred at room temperature for 10-10 After 30 minutes, add associative polyurethane rheology additive 1.5-2.0 and stir for 30-45 minutes, add hand feel agent 5-10 and stir for 20-30 minutes, filter out the material to obtain the product. Suitable for pure cotton, polyester, nylon fabrics.

Description

technical field [0001] The invention relates to an anti-pinhole-drilling coating adhesive for textile fabrics, which is a water-based coating adhesive and has the functional characteristics of being super soft, cold-resistant, and anti-pinhole-drilling. Background technique [0002] Currently, solvent-based acrylic resins are mainly used for pinhole anti-velvet fabrics in the market. Solvent-based acrylic resin, commonly known as pony glue, is soft to the touch, but it contains a lot of toluene, which will release toluene during use, pollute the environment and cause harm to the human body. Moreover, solvent-based acrylic resin has the disadvantage of hot stickiness and cold brittleness. Pinhole anti-velvet fabrics are mainly used in cold environments, and the fabric will feel hard, which will affect the wearing comfort and fail to meet the cold resistance requirements; [0003] CN103614922A discloses a "down jacket fabric anti-pinhole drilling treatment method" to solve th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M15/568D06M13/50
Inventor 唐丽党瑞东荣星宋明智
Owner LIAONING FIXED STAR FINE CHEM
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com