Production technology for automobile spare tire cover plate with PP cellular board as base material

A technology of automobile spare tire cover plate and production process, which is applied in the direction of layered products, vehicle parts, synthetic resin layered products, etc., can solve the problems of not conforming to economic benefits, high product weight, high cost, etc., and meet the market consumption concept , Reduce production cost, simple production process

Inactive Publication Date: 2015-10-21
WUXI GISSING AUTO ACOUSTIC PARTS TECH CO LTD
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The current spare tire cover mainly adopts PP wood powder board, PP particle blow molding and other processes. The main problems are as follows: 1. PP wood powder board adopts hot material cold molding process. The weight is relatively high; 2. The PP particle blow molding process is complicated, the cost is high, and the weight is too heavy, which greatly increases the production cost and does not meet the economic benefits; 3. The product weight cannot meet the market's demand for reducing the weight of the car body

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Example 1 443A spare wheel cover

[0018] Spare tire cover specification: L1050×W1000×H5.5

[0019] A kind of production technology of the automobile spare tire cover plate that is base material with PP honeycomb plate, the steps are as follows:

[0020] (1) Fabric preparation: take the fabric, sprinkle glue powder on the fabric, the amount of glue is 65g / cm 2 ;After being heated in an oven at 120°C for 30s, it is naturally cooled and shaped;

[0021] (2) Fabric cutting: put the fabric obtained in step (1) on the spare tire cover cutting die of the cutting machine, and start the cutting machine to cut;

[0022] (3) Mold preheating: Preheat the knife edge of the mold to be used to 200°C;

[0023] (4) Substrate laying: Take the PP honeycomb panel, lay the cut fabric in step (2) on the PP honeycomb panel, and place the PP honeycomb panel with the laid fabric facing down on the lower mold of the mold;

[0024] (5) Compression molding: Send the mold into the molding mach...

Embodiment 2

[0029] A kind of production technology of the automobile spare tire cover plate that is base material with PP honeycomb plate, the steps are as follows:

[0030] (1) Fabric preparation: take the fabric, sprinkle glue powder on the fabric, the amount of glue is 75g / cm 2 ;After being heated in an oven at 130°C for 50s, it is naturally cooled and shaped;

[0031] (2) Fabric cutting: Put the fabric obtained in step (1) on the spare tire cover cutting die of the cutting machine, start the cutting machine to cut, and the cutting size is 1.5m*1m;

[0032] (3) Mold preheating: Preheat the knife edge of the mold to be used to 220°C;

[0033] (4) Substrate laying: Take the PP honeycomb panel, lay the cut fabric in step (2) on the PP honeycomb panel, and place the PP honeycomb panel with the laid fabric facing down on the lower mold of the mold;

[0034] (5) Compression molding: Send the mold into the molding machine for molding, the molding pressure is 12MPa, and the molding time is 7...

Embodiment 3

[0038] A kind of production technology of the automobile spare tire cover plate that is base material with PP honeycomb plate, the steps are as follows:

[0039] (1) Fabric preparation: take the fabric, sprinkle glue powder on the fabric, the amount of glue is 70g / cm 2 ;After being heated in an oven at 125°C for 40s, it is naturally cooled and shaped;

[0040] (2) Fabric cutting: put the fabric obtained in step (1) on the spare tire cover cutting die of the cutting machine, start the cutting machine to cut, and the cutting size is 1.2m*0.8m;

[0041] (3) Mold preheating: Preheat the knife edge of the mold to be used to 210°C;

[0042] (4) Substrate laying: Take the PP honeycomb panel, lay the cut fabric in step (2) on the PP honeycomb panel, and place the PP honeycomb panel with the laid fabric facing down on the lower mold of the mold;

[0043] (5) Compression molding: Send the mold into the molding machine for molding, the molding pressure is 10MPa, and the molding time is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a production technology for an automobile spare tire cover plate with a PP cellular board as a base material, and belongs to the technical field of automobile interior trim parts. The automobile spare tire cover plate with the PP cellular board as the base material is obtained through shell fabric preparation, shell fabric cutting, mold preheating, base material laying, pressing forming and postprocessing. The defects that existing spare tire cover plates are high in weight and not enough in rigidity are overcome, and the rigidity of the spare tire cover plate is improved, so that the bearing capacity of the spare tire cover plate is improved, and the weight of the spare tire cover plate is decreased so as to decrease the weight of an automobile body. Meanwhile, the production cost caused by the raw material cost is lowered. In addition, due to the fact that the production technology is simple, the rejection rate during production is lowered, raw materials are saved indirectly, and the cost for processing rejects is saved. The requirement of modern automobiles for high bearing capacity and low weight of the spare tire cover plate is met, the cost is low, the raw materials can be recycled, and the market consumption concept is met.

Description

technical field [0001] The present invention relates to a production process of automobile spare tire cover plate with PP honeycomb plate material as the base material. The PP honeycomb plate material is used to replace other materials such as PP plate of the old process, so as to increase the load capacity of the product and reduce the cost; specifically It is said that it is a production process of a spare tire cover plate for improving the rigidity of the spare plate in the trunk of the car and reducing the weight so as to increase the carrying capacity when carrying objects, and belongs to the technical field of automotive interior parts. Background technique [0002] The car spare tire cover is used as the partition layer between the spare tire and the storage in the car trunk. A platform for storage of slightly larger items and tools. Since the items stored in the trunk of a car are generally relatively large, and many of them are relatively heavy and large items, the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B60R5/04B32B37/10B32B37/12B32B3/12B32B27/06B32B7/12
Inventor 李红星
Owner WUXI GISSING AUTO ACOUSTIC PARTS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap