Ultraviolet curing transfer-printing high-gloss decoration plate and manufacturing method thereof

A manufacturing method and ultraviolet light technology, applied in building construction, covering/lining, construction, etc., to achieve the effects of good hardness and wiping performance, smooth and wear-resistant surface, and high production efficiency

Active Publication Date: 2015-10-21
中关村人居环境工程与材料研究院
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention aims to solve the problems described above

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultraviolet curing transfer-printing high-gloss decoration plate and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] The manufacture method of UV-cured transfer printing high-gloss decorative plate according to the present invention comprises the following steps:

[0058] 1) Dedusting the back of the plasterboard;

[0059] 2) Apply a 0.05mm thick sealing paint on the back of the plasterboard by single roller coating, and use a double mercury lamp curing machine for 3s UV curing;

[0060] 3) Turn over the board, and carry out dust removal treatment on the front of the plasterboard;

[0061] 4) Coat the front of the plasterboard with a 0.05mm thick adhesion primer by means of forward and reverse roller coating, and use a double gallium lamp curing machine for 3s UV curing;

[0062] 5) After the curing is completed, fine sanding and dust removal are performed on the surface of the plasterboard;

[0063] 6) Apply a 0.05mm thick white primer with a single roller, and use a double gallium lamp curing machine for 3s UV curing;

[0064] 7) Apply a 0.05mm thick sealing primer with positive ...

Embodiment 2

[0074] The manufacture method of UV-cured transfer printing high-gloss decorative plate according to the present invention comprises the following steps:

[0075] 1) Dedusting the back of the plasterboard;

[0076] 2) Apply a 0.08mm thick sealer paint on the back of the plasterboard with a single roller coating method, and use a double mercury lamp curing machine for 6s UV curing;

[0077] 3) Turn over the board, and carry out dust removal treatment on the front of the plasterboard;

[0078] 4) Coat the front of the plasterboard with a 0.08mm thick adhesion primer by means of forward and reverse roller coating, and use a double gallium lamp curing machine for 6s UV curing;

[0079] 5) After the curing is completed, fine sanding and dust removal are performed on the surface of the plasterboard;

[0080] 6) Apply a 0.08mm thick white primer with a single roller, and use a double gallium lamp curing machine for 6s UV curing;

[0081] 7) Apply a 0.08mm thick sealing primer with...

Embodiment 3

[0091] The manufacture method of UV-cured transfer printing high-gloss decorative plate according to the present invention comprises the following steps:

[0092] 1) Dedusting the back of the plasterboard;

[0093] 2) Apply a 0.12mm thick sealer paint on the back of the plasterboard with a single roller coating method, and use a double mercury lamp curing machine for 10s of UV curing;

[0094] 3) Turn over the board, and carry out dust removal treatment on the front of the plasterboard;

[0095] 4) Apply a 0.12mm-thick adhesion primer to the front of the plasterboard by means of forward and reverse roller coating, and use a double-gallium lamp curing machine for 10s of UV curing;

[0096] 5) After the curing is completed, fine sanding and dust removal are performed on the surface of the plasterboard;

[0097] 6) Apply a 0.12mm thick white primer with a single roller, and use a double gallium lamp curing machine for 10s of UV curing;

[0098] 7) Apply a 0.12mm thick sealing ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention provides an ultraviolet curing transfer-printing high-gloss decoration plate and a manufacturing method thereof. The method includes: (1) forming a primer surface on the front surface of a decoration substrate; (2) performing sizing and transfer film-printing of the primer surface, performing ultraviolet curing, and removing the transfer-printing film; (3) performing roller painting of colored paints on the front surface of the decoration substrate and performing ultraviolet curing; and (4) performing roller painting of high-gloss finishing paints on the cured colored paints and performing ultraviolet curing. The decoration plate manufactured by the method is advantaged by high-definition emulation, bright and saturated color, smooth and wear-resistant surface, light weight, and low cost.

Description

technical field [0001] The invention relates to a decorative board and a manufacturing method thereof, in particular to an ultraviolet light-cured transfer high-gloss decorative board and a manufacturing method thereof. Background technique [0002] Ultraviolet light (UV) curing is to use the photosensitivity of the photoinitiator (photosensitizer) to form excited ecological molecules under the irradiation of ultraviolet light, and decompose them into free radicals or ions, so that unsaturated organic compounds can be polymerized, grafted, and exchanged. Combined chemical reactions to achieve the purpose of curing. UV curing technology has been applied in the manufacture of decorative panels. Substrates using UV curing technology include cement pressure boards, solid wood multilayer boards, density boards, and glass magnesium fireproof boards. However, the UV-cured decorative boards manufactured with the above-mentioned types of boards as substrates cannot meet the current...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E04F13/07E04F13/14
Inventor 赵金平王弘书冯小江唐门辉刘雪婧高秀慧
Owner 中关村人居环境工程与材料研究院
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More