Heat treatment technology for aluminum product

A technology for processing aluminum materials, which is applied in the field of heat treatment of aluminum materials, can solve problems such as waste of resources, complicated procedures, failure to meet requirements, etc., achieve low processing costs and improve process efficiency

Inactive Publication Date: 2015-11-04
WUXI YANGGONG MACHINERY MFG
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current heat treatment process cannot meet the requirements, which not only wastes resources, but also complicates the process.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] The embodiment provided by the present invention is described in further detail:

[0012] A process for treating aluminum materials, the steps of which are as follows:

[0013] (1) Blank inspection: inspect the workpiece;

[0014] (2) Degreasing: Degrease the aluminum material of the workpiece until the workpiece is completely soaked;

[0015] (3) Solution treatment: heat the aluminum material to 950-1050°C and quench it in water, and keep this state at room temperature;

[0016] (4) Stress relief treatment: heating to 300-350°C and tempering to eliminate the residual stress of aluminum after cold working or welding;

[0017] (6) Cooling: Cool the workpiece with water less than 70°C.

[0018] Preferably, the water-based metal degreasing cleaning agent includes surfactant, sodium tripolyphosphate, fatty alcohol polyoxyethylene ether and sodium silicate to degrease the surface of the workpiece.

[0019] The invention has the beneficial effects of low processing cost, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a heat treatment technology for an aluminum product. The heat treatment technology comprises the following steps that firstly, blank checking is conducted, and a workpiece is checked; second, degreasing is conducted, and the workpiece aluminum product is degreased until the workpiece is completely soaked; thirdly, solution treating is conducted, particularly, the aluminum product is heated to 950-1050 DEG C and subjected to water quenching, and the state is kept until the room temperature is reached; fourthly; destressing treating is conducted, particularly, tempering is conducted after heating is conducted to the temperature of 300-350 DEG C, and heat treating of eliminating residua stress obtaineafter cold machining or welding is conducted on the aluminum product; and sixthly, cooling is conducted, and water with the temperature smaller than 70 DEG C is used for cooling the workpiece. The heat treatment technology is low in treating cost, durable in use and capable of improving the technology treating efficiency and the quality of the workpiece.

Description

technical field [0001] The invention belongs to the technical field of heat treatment, in particular to an aluminum material heat treatment process. Background technique [0002] At present, the aluminum steel pipe is a long strip of aluminum with a hollow section and no seams around it. However, the current heat treatment process cannot meet the requirements, which not only wastes resources, but also complicates the process. Contents of the invention [0003] The technical scheme of the present invention is achieved in that a kind of aluminum processing technology, its steps are as follows: [0004] (1) Blank inspection: inspect the workpiece; [0005] (2) Degreasing: Degrease the aluminum material of the workpiece until the workpiece is completely soaked; [0006] (3) Solution treatment: heat the aluminum material to 950-1050°C and quench it in water, and keep this state at room temperature; [0007] (4) Stress relief treatment: heating to 300-350°C and tempering to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22F1/04
Inventor 杨龙兴
Owner WUXI YANGGONG MACHINERY MFG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com