Hub casting and forming technology

A casting molding and process technology, applied in the direction of casting molding equipment, casting molds, casting mold components, etc., can solve the problems of failure to meet production requirements, low service life, easy to generate pores, etc., achieve dense internal structure, prolong service life, The effect of ensuring quality

Active Publication Date: 2015-11-18
ANHUI AUHER ALUMINUM TECH
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to provide a wheel hub casting molding process to solve the problems in the prior art that the automobile wheel hub is prone to produce pores and inclusions during casting, resulting in poor quality of the wheel hub, low service life, and failure to meet production requirements. multiple defects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A wheel hub casting molding process includes the following steps:

[0017] (1) Preparation of aluminum alloy melt: it is composed of the following substances by mass percentage: 1% magnesium, 1% silicon, 2% iron, 0.5% copper, 1% manganese, 2% nickel-chromium alloy , Additives 0.5%, the rest is aluminum;

[0018] (2) Melting: Add the aluminum alloy melt in step (1) to the melting furnace and adjust the temperature to 725°C. Use an electromagnetic stirrer to stir the melt for 10 minutes to make the temperature in the molten pool uniform. Add a refining agent to the aluminum alloy The melt is refined for 10 minutes, the surface scum is removed, the temperature is adjusted to 700 ℃, and the argon gas is used for degassing and refining for 10 minutes;

[0019] (3) Casting: Put the aluminum liquid slag in step (2) to stand for 20 minutes, first preheat the mold, the preheating temperature is 180 ℃, and then hydraulically insert the aluminum into the mold for casting, the casting te...

Embodiment 2

[0023] A wheel hub casting molding process includes the following steps:

[0024] (1) Preparation of aluminum alloy melt: It is composed of the following substances by mass percentage: 3% magnesium, 3% silicon, 4% iron, 1% copper, 2% manganese, 9% nickel-chromium alloy , Additives 2%, the rest is aluminum;

[0025] (2) Melting: Add the aluminum alloy melt in step (1) to the melting furnace and adjust the temperature to 735°C. Use an electromagnetic stirrer to stir the melt for 15 minutes to make the temperature in the molten pool uniform. Add a refining agent to the aluminum alloy The melt is refined for 20 minutes, the surface scum is removed, the temperature is adjusted to 710 ℃, and the argon gas is used for degassing and refining for 15 minutes;

[0026] (3) Casting: Put the molten aluminum slag in step (2) to stand for 30 minutes, first preheat the mold, the preheating temperature is 220 ℃, and then hydraulic pressure into the mold for casting, the casting temperature is 695 ℃,...

Embodiment 3

[0030] A wheel hub casting molding process includes the following steps:

[0031] (1) Preparation of aluminum alloy melt: It is composed of the following substances by mass percentage: 2% magnesium, 2% silicon, 3% iron, 0.75% copper, 1.5% manganese, 5.5% nickel-chromium alloy , Additives 1.25%, the rest is aluminum;

[0032] (2) Melting: Add the aluminum alloy melt in step (1) into the melting furnace to adjust the temperature to 730℃, stir the melt with an electromagnetic stirrer for 13 minutes to make the temperature uniformity everywhere in the molten pool, add a refining agent to the aluminum alloy The melt is refined for 15 minutes, the surface scum is removed, the temperature is adjusted to 705°C, and argon degassing is used for refining for 13 minutes;

[0033] (3) Casting: Put the aluminum liquid slag in step (2) to stand for 25 minutes, and first preheat the mold. The preheating temperature is 200°C. The aluminum is hydraulically inserted into the mold for casting. The cast...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a hub casting and forming technology and relates to the field of automobile spare part casting. The hub casting and forming technology comprises four technology steps of aluminium alloy melting stock preparation, melting, casting and cooling and forming. The process route is simple; the process conditions are easy to meet; the appearance of a casting which is cast has no casting flaw, no pore and no impurity; the internal tissue is compact; the quality of a hub can be ensured; the service life is prolonged; and the economical benefit is improved.

Description

Technical field [0001] The invention relates to the field of auto parts casting, in particular to a wheel hub casting molding process. Background technique [0002] In the 20th century, with the development of society, the demand for automobiles is increasing. The wheel hub is an important component of the automobile. The performance of the wheel hub is directly related to the performance of the entire automobile. However, in the existing technology, the automobile The wheel hub is prone to pores and inclusions during casting, resulting in poor quality of the wheel hub, low service life, and unable to meet production requirements. Summary of the invention [0003] The technical problem to be solved by the present invention is to provide a wheel hub casting molding process to solve the problems caused by the prior art that the automobile hub is prone to pores and inclusions during casting, resulting in poor quality of the hub, low service life, and failure to meet production requir...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C1/03C22C21/00C22C21/02C22C21/08B22C9/28
Inventor 戚召建
Owner ANHUI AUHER ALUMINUM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products