Prepreg, fiber-reinforced composite material, and resin composition containing particles

A resin composition and prepreg technology, applied in synthetic resin layered products, chemical instruments and methods, layered products, etc., can solve problems such as poor toughness, achieve excellent moisture resistance and heat resistance, excellent CAI and Flexural modulus, effect of maintaining glass transition temperature

Active Publication Date: 2015-11-18
JXTJ NIPPON OIL & ENERGY CORP +1
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although benzoxazine resin has excellent moisture resistance and heat resistance, it has the problem of poor toughness. We focus on compounding epoxy resin and various resin particles to make up for this shortcoming.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Prepreg, fiber-reinforced composite material, and resin composition containing particles
  • Prepreg, fiber-reinforced composite material, and resin composition containing particles
  • Prepreg, fiber-reinforced composite material, and resin composition containing particles

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～6、 comparative example 1～2

[0118] For each example and comparative example, the raw materials were heated and mixed at the ratio shown in Table 1 to obtain the first resin composition not containing particles (composition of "No. 1" in the table) and the second resin composition containing particles. (composition of "No. 2" in the table). In addition, the raw material used here is as follows.

[0119] (A) component: benzoxazine resin

[0120] F-a (bisphenol F-aniline type, manufactured by Shikoku Chemical Industry Co., Ltd.)

[0121] P-a (phenol-aniline type, manufactured by Shikoku Chemical Industry Co., Ltd.)

[0122] (B) component: epoxy resin

[0123] "CELLOXIDE" (registered trademark) 2021P (manufactured by Daicel Corporation)

[0124] (C) Component: curing agent

[0125] BPF (9,9-bis(4-hydroxyphenyl)fluorene, manufactured by Osaka Gas Chemicals Co., Ltd.)

[0126] BPC (1,1-bis(4-hydroxyphenyl)cyclohexane, manufactured by Sigma-Aldrich Corporation)

[0127] TDP (bis(4-hydroxyphenyl)sulfide, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

A prepreg (10) is provided with: a reinforcing fiber layer (3) that comprises reinforcing fibers (1) and a resin composition (2) that is used to impregnate the area between the reinforcing fibers and that comprises (A) a benzoxazine resin, (B) an epoxy resin, and (C) a curing agent that has two or more phenolic hydroxyl groups in the molecule thereof; and surface layers (6a, 6b) that are provided on the surface of the reinforcing fiber layer (3) and that comprise (A) the benzoxazine resin, (B) the epoxy resin, (C) the curing agent that has two or more phenolic hydroxyl groups, and (D) polyamide resin particles (4) having an average particle size of 5-50 µm. The polyamide resin particles (4) include polyamide 1010 resin particles.

Description

technical field [0001] The present invention relates to prepregs, fiber reinforced composites and particle-containing resin compositions for making them. In particular, the present invention relates to a fiber-reinforced composite material for aircraft, ship, automobile, sports, and other general industrial applications, and a prepreg used to obtain the composite material. Background technique [0002] Fiber-reinforced composite materials containing various fibers and matrix resins are widely used in aircraft, ships, automobiles, sporting goods, and other general industrial applications due to their excellent mechanical properties. In recent years, with the accumulation of its use results, the scope of application of fiber reinforced composite materials has been further expanded. [0003] As such fiber-reinforced composite materials, for example, Patent Documents 1 and 2 propose fiber-reinforced composite materials using benzoxazine resins. Although benzoxazine resin has e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08J5/24C08L61/34C08L63/00C08L77/06
CPCC08J5/24C08G14/06C08J2379/04C08J2463/02C08J2477/06C08K5/13C08K5/357C08L63/00C08L77/06C08G59/621C08K5/353C08L61/34C08L2205/03C08J5/243C08J5/249C08L79/04B32B27/08B32B27/38B32B2260/046B32B2262/106B32B2264/0264B32B2305/076C08J2463/00
Inventor 福田欣弘松本隆之南昌树关根尚之中岛正宪
Owner JXTJ NIPPON OIL & ENERGY CORP
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com