Manufacturing method of ambroid glass artware

A technology of artificial amber and production method, applied in decorative arts, special decorative structures, etc., can solve problems such as glass bursting, large gap between cold and heat shrinkage, and separation of layers.

Active Publication Date: 2015-12-02
NANNING MILLENNIUM ARTS & CRAFTS
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the existing technology uses unsaturated resin or epoxy resin to pour into the glass model to embed various contents, which has a great quality hidden danger, because there is a big gap between the cold and hot shrinkage rates of glass and unsaturated resin or epoxy resin. Large, the products made according to this method, as the temperature changes, there will be separation between the glass and the resin, or the quality problem of glass bursting

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A method for making an artificial amber glass handicraft, comprising the following steps:

[0028] 1. Prepare a glass block with a groove, outer size: length 60*width 60*height 5cm, groove inner diameter size: 58*58*3.5cm, wash and dry;

[0029] 2. Preparation of silicone embedding resin:

[0030] The components contained in component A and their weight percentages are: hydroxyl-terminated polydioxane 45%, methyl silicone resin 35%, polydimethylsiloxane 18%, defoamer AFE-01201%, leveling agent BYK-3061%, the above substances are mixed evenly and sealed for storage;

[0031] The components contained in component B and their weight percentages are: tetraethyl orthosilicate 31.5%, polydimethylsiloxane 50%, methyltrimethylsilane 10%, leveling agent TEGOGlide4508.5%, the above substances Mix evenly and seal it for storage;

[0032] 3. Prepare conch, shells, coral branches and crushed sand as the contents, put a seascape pattern in the glass groove, mix the silicone resin ...

Embodiment 2

[0035] The manufacturing method of rose embedding glass decorative block comprises the following steps:

[0036] 1. Prepare a square hollow glass vessel, external size: 8*8*8cm, internal size: 7.5*7.5*7.5cm;

[0037] 2. Preparation of silicone embedding resin:

[0038] The components contained in component A and their weight percentages are: 50% hydroxyl-terminated polydioxane, 28% methyl silicone resin, 20% polydimethylsiloxane, defoamer AFE-01201%, leveling agent BYK-3061%, the above substances are mixed evenly and sealed for storage;

[0039] The components contained in component B and their weight percentages are: tetraethyl orthosilicate 25%, polydimethylsiloxane 55%, methyltrimethylsilane 10%, leveling agent TEGOGlide45010%, and the above substances are mixed evenly Sealed storage;

[0040] 4. Prepare plastic artificial roses, put them in glassware, fix the artificial flowers on the bottom of the glassware with quick-drying glue, mix the silicone resin evenly accordin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a manufacturing method of ambroid glass artware. The manufacturing method comprises the following steps: preparing a glass container; preparing embedding resin of ambroid, which comprises a component A and a component B, wherein the component A is organic silicon resin of which the viscosity is 2,000-4,000 mPa*s at 25 DEG C, and the component B is an organic silicon resin curing agent; and placing a content into the glass container, mixing the component A and the component B to obtain a resin mixed solution in which the weight ratio of the component A to the component B is (1-10): 1, and injecting the resin mixed solution into the glass container for curing to obtain the ambroid glass artware. By the adoption of the technical scheme, the cold and heat shrinking percentages of resin and glass are approximate, so that the quality problems of layer separation between resin and glass and burst are solved, the original appearance can be kept after long-time placement, the phenomenon of yellowing discoloration is avoided, and layer separation between resin and glass or glass burst is prevented.

Description

technical field [0001] The invention relates to a method for making handicrafts, in particular to a method for making artificial amber glass handicrafts. Background technique [0002] Artificial amber is a resin handicraft made by embedding various built-in objects such as insects, flowers, metals, wood, sea shells and snails with high-transparency polymer resin. It can be used as building decoration materials, furniture parts, home decorations and souvenirs, etc. ; Its main feature is that the product is crystal clear, true and natural, and permanently preserved. Due to the unique form of expression of the product, it has been loved by consumers since it entered the market. Glass artificial amber crafts are glass crafts that combine resin embedding with glass modeling to obtain resin embedding of various contents. [0003] At present, the existing technology uses unsaturated resin or epoxy resin to pour into the glass model to embed various contents, which has a great qua...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B44C5/06B29C39/10C08L83/04C08L83/06
Inventor 施兵
Owner NANNING MILLENNIUM ARTS & CRAFTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com