A kind of high-strength casting magnesium alloy and preparation method thereof

A technology for casting magnesium alloys and magnesium alloys is applied in the fields of Mg-Bi-Al-Zn-Sr alloys and their preparation, non-rare earth low-cost and high-strength casting magnesium alloys and their preparation fields, which can solve problems such as increasing the cost of alloys, and achieve The effect of energy saving, simple equipment and low price

Active Publication Date: 2017-09-12
HEBEI UNIV OF TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

After solid solution and aging treatment, the alloy has high mechanical properties, the tensile strength is 280-320MPa, the yield strength is 140-155MPa, the elongation is 5-12%, and the alloy also contains more precious elements (Nd 2.5 ~3.6wt%), which indirectly increases the cost of the alloy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high-strength casting magnesium alloy and preparation method thereof
  • A kind of high-strength casting magnesium alloy and preparation method thereof
  • A kind of high-strength casting magnesium alloy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] (1) Take raw material by the mass percent of alloy Mg-3.8Bi-3.2Al-0.5Zn-0.05Sr (wt%): pure Bi, pure Al, pure Zn and Mg-5Sr master alloy, all the other are Mg (per 1000 The gram target alloy can be prepared by 10 grams of Mg-5Sr, 32 grams of Al, 5 grams of Zn, 38 grams of Bi and 917 grams of Mg); and do a good job of surface treatment of raw materials (such as removing dirt, scale, etc.).

[0036] (2) First clean the melting furnace and heat it to 450°C, put the magnesium ingot preheated to 200°C into the crucible of the melting furnace, set the furnace temperature to 720°C, and slowly heat the heating rate to 20-40°C / min And maintain the set furnace temperature.

[0037] (3) After the pure magnesium ingots are completely melted, respectively add pure Bi, pure Al, pure Zn and Mg-5Sr intermediate alloys preheated to about 200°C to the magnesium melt, raise the furnace temperature to 730°C, and keep warm 5 to 10 minutes, then mechanically stirred for 3 to 5 minutes, then ...

Embodiment 2

[0042] (1) Take raw material by the mass percent of alloy Mg-6Bi-2.0Al-0.6Zn-0.08Sr (wt%): pure Bi, pure Al, pure Zn and Mg-5Sr master alloy, all the other are Mg; And do well Surface treatment of raw materials (such as removal of dirt, scale, etc.).

[0043] (2) First clean the melting furnace and heat it to 450°C, put the magnesium ingot preheated to 200°C into the crucible of the melting furnace, set the furnace temperature to 720°C, and slowly heat the heating rate to 20-40°C / min And maintain the set furnace temperature.

[0044] (3) After the pure magnesium ingots are completely melted, respectively add pure Bi, pure Al, pure Zn and Mg-5Sr intermediate alloys preheated to about 200°C to the magnesium melt, raise the furnace temperature to 730°C, and keep warm 5 to 10 minutes, then mechanically stirred for 3 to 5 minutes, then filled with argon for refining and degassing, then adjusted the furnace temperature to the pouring temperature of 720°C, stood for 2 to 10 minutes,...

Embodiment 3

[0049] (1) Take raw material by the mass percent of alloy Mg-7.0Bi-1.0Al-1.0Zn-0.08Sr (wt%): pure Bi, pure Al, pure Zn and Mg-5Sr master alloy, all the other are Mg; And do Good raw material surface treatment (such as removal of dirt, scale, etc.).

[0050] (2) First clean the melting furnace and heat it to 450°C, put the magnesium ingot preheated to 200°C into the crucible of the melting furnace, set the furnace temperature to 720°C, and slowly heat the heating rate to 20-40°C / min And maintain the set furnace temperature.

[0051] (3) After the pure magnesium ingots are completely melted, respectively add pure Bi, pure Al, pure Zn and Mg-5Sr intermediate alloys preheated to about 200°C to the magnesium melt, raise the furnace temperature to 730°C, and keep warm 5 to 10 minutes, then mechanically stirred for 3 to 5 minutes, then filled with argon for refining and degassing, then adjusted the furnace temperature to the pouring temperature of 720°C, stood for 2 to 10 minutes, a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention is a high-strength casting magnesium alloy, which is a Mg-Bi-Al-Zn-Sr alloy, and the weight percentages of its components are: Bi3-8.0wt%; Al 0.5-4.0wt%; Zn 0.1-1.0wt%; Sr 0.05-0.15wt%, the rest is Mg. In the present invention, Bi element is used as the main alloy element, and a large amount of Mg3Bi2 phase is formed through a simple alloying method, supplemented by a small amount of aluminum element and zinc element to improve the strength of the alloy, thereby developing a high-strength cast magnesium alloy in this alloy series , the tensile strength of the alloy is 276-296MPa, the yield strength is 155-170MPa, and the elongation is 5.3-7.3%, achieving mechanical properties comparable to those of rare earth magnesium alloys.

Description

technical field [0001] The invention relates to a non-rare earth low-cost high-strength cast magnesium alloy and a preparation method thereof, in particular to a Mg-Bi-Al-Zn-Sr alloy and a preparation method thereof, belonging to the field of metal materials and metallurgy. Background technique [0002] Magnesium alloy is currently the lightest metal engineering structure material in practical application, and the density of pure magnesium is about 1.74g / cm 3 , its density is about 1 / 4 of steel, 1 / 3 of zinc, and 2 / 3 of aluminum alloy. Magnesium alloys have the characteristics of high specific strength, excellent mechanical cutting performance and damping and shock absorption performance, which meet the urgent needs of the modern automobile industry for weight reduction and environmental protection. Since the 1980s, with the rapid development of the automobile industry, a large number of magnesium alloy materials have been used in automobile parts, among which the commercial...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C23/00C22C1/03C22F1/06
Inventor 赵维民孟帅举余晖秦春玲王志峰
Owner HEBEI UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap