Calendering-type rubber surround bar rubber for brilliant white shoes, and preparation method for rubber surround bar rubber

A technology of rubber perimeter strip glue and extra white color is applied in the field of calendered extra white rubber perimeter strip glue for shoes and its preparation. The effect of stable material quality and process performance, improving fineness and gloss, and high molding efficiency of rubber compound

Inactive Publication Date: 2015-12-16
JIHUA 3537 SHOE MAKING
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When the film is released, the rubber material is not dense because it has not passed the extruder, and there are usually the following major problems: (1) The surface of the film is not fine
(2) Poor surface gloss
(3) There are fragments when the film is produced, which affects production efficiency
[0003] In the prior art, due to the existence of the above problems, it cannot meet the needs of customers for white shoes and affects the production efficiency.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Calendering-type rubber surround bar rubber for brilliant white shoes, and preparation method for rubber surround bar rubber
  • Calendering-type rubber surround bar rubber for brilliant white shoes, and preparation method for rubber surround bar rubber
  • Calendering-type rubber surround bar rubber for brilliant white shoes, and preparation method for rubber surround bar rubber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Embodiment 1 of the present invention: Calendered extra-white shoe rubber enclosure glue, calculated in parts by weight, including 55 parts of standard rubber, 45 parts of styrene-butadiene rubber, 2.2 parts of sulfur, 2.9 parts of vulcanization accelerator, and 1 part of stearic acid , 4 parts of zinc carbonate, 21 parts of spindle oil, 1.8 parts of anti-aging agent, 0.5 parts of ultramarine blue, 6 parts of brightener, 5 parts of polyethylene glycol, 56 parts of fine ultra-white light calcium carbonate, 0.16 parts of permanent violet, 36 parts Titanium dioxide, 42 parts of white carbon black and 0.4 part of peptizer DS-T-1; Described vulcanization accelerator is, every 2.9 parts of vulcanization accelerators are made up of 1.1 parts of accelerator DM and 1.8 parts of accelerator M; Described The standard glue is 1# standard glue; the anti-aging agent is that every 1.8 parts of anti-aging agent is composed of 0.3 parts of anti-aging agent KY-405 and 1.5 parts of anti-ag...

Embodiment 2

[0040] Embodiment 2 of the present invention: calendered extra-white shoe rubber enclosure glue, calculated in parts by weight, including 52 parts of standard rubber, 48 parts of styrene-butadiene rubber, 2.0 parts of sulfur, 2.7 parts of vulcanization accelerator, and 0.8 part of stearic acid , 3.8 parts of zinc carbonate, 19 parts of spindle oil, 1.6 parts of anti-aging agent, 0.4 parts of ultramarine blue, 5 parts of brightener, 4 parts of polyethylene glycol, 54 parts of fine ultra-white light calcium carbonate, 0.15 parts of permanent violet, 34 parts Titanium dioxide, 40 parts of white carbon black and 0.3 part of peptizer DS-T-1; Described vulcanization accelerator is, every 2.9 parts of vulcanization accelerators are made up of 1.1 parts of accelerator DM and 1.8 parts of accelerator M; Described The standard glue is 1# standard glue; the anti-aging agent is that every 1.8 parts of anti-aging agent is composed of 0.3 parts of anti-aging agent KY-405 and 1.5 parts of ant...

Embodiment 3

[0042] Embodiment 3 of the present invention: calendered special white shoe rubber enclosing strip glue, calculated in parts by weight, including 58 parts of standard rubber, 42 parts of styrene-butadiene rubber, 2.4 parts of sulfur, 3.1 parts of vulcanization accelerator, and 1.2 parts of stearic acid , 4.2 parts of zinc carbonate, 23 parts of spindle oil, 2 parts of anti-aging agent, 0.6 parts of ultramarine blue, 7 parts of brightener, 6 parts of polyethylene glycol, 58 parts of fine ultra-white light calcium carbonate, 0.17 parts of permanent violet, 38 parts Titanium dioxide, 44 parts of white carbon black and 0.5 part of peptizer DS-T-1; Described vulcanization accelerator is, every 2.9 parts of vulcanization accelerators are made up of 1.1 parts of accelerator DM and 1.8 parts of accelerator M; Described The standard glue is 1# standard glue; the anti-aging agent is that every 1.8 parts of anti-aging agent is composed of 0.3 parts of anti-aging agent KY-405 and 1.5 parts...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a calendering-type rubber surround bar rubber for brilliant white shoes, and a preparation method for the surround bar rubber. According to the method, a system that both rubber and styrene butadiene rubber are adopted; masterbatches are refined respectively, so that an insoluble compounding agent is fully dispersed; through adoption of 5 # spindle oil, smoothness and glossiness of the surface of a rubber material are improved, the color is stable, and a brightness reaches a desired level by regulation and control of a vulcanization accelerator system. Through the adoption of the method, the rubber refining efficiency, the rubber material forming efficiency and the rubber material quality are high, and the technological properties are stable.

Description

technical field [0001] The invention relates to the field of rubber material preparation, and relates to a calendered special white shoe rubber skirt glue and a preparation method thereof. Background technique [0002] The calendered special white shoe rubber skirt glue usually uses natural rubber as the skeleton material, and the filling system uses light calcium carbonate as the main material, and the preparation method adopts a one-time feeding method. When the film is released, the rubber material is not dense because it has not passed the extruder, and there are usually the following major problems: (1) The surface of the film is not delicate. (2) Poor surface gloss. (3) There are fragments when the film is released, which affects production efficiency. [0003] In the prior art, due to the existence of the above-mentioned problems, it cannot meet the needs of customers for white shoes and affects the production efficiency. Contents of the invention [0004] The pu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L9/06C08L71/08C08L91/00C08K13/02C08K3/06C08K5/09C08K3/26C08K3/22C08K3/36
Inventor 杜江陈松雄周川泉晋齐怀石银平田吉张世林王春桥
Owner JIHUA 3537 SHOE MAKING