Kitchen oil smoke cleaning agent liquid formula with time-delay film formation

A cleaning agent and liquid technology, applied in the field of daily chemicals, can solve the problems of different foam sizes, insufficient foaming power and detergency of glycoside surfactants, insufficient foam stability and strength, etc., and achieve the effect of beautifying the kitchen.

Active Publication Date: 2016-02-17
南京海杰亚生物科技有限公司
5 Cites 4 Cited by

AI-Extracted Technical Summary

Problems solved by technology

The foam size of fatty alcohol polyoxyethylene ether is different, and the foam stability and strength ...
View more

Abstract

The invention provides a kitchen oil smoke cleaning agent liquid formula with time-delay film formation, strong base is not used as a main component, and the formula is composed of a low-irritation nontoxic surfactant, a film forming agent, a film forming auxiliary agent, an environmental protection solvent, a brightener, an antiseptic, a pH regulator and essence. The cleaning agent is uniformly sprayed on a range hood, kitchen tiles and other hard surfaces, and oil stain can be erased timely; the cleaning agent can be sprayed on cleaned surfaces, such as walls, after the solvent is volatilized, a transparent film is formed; after a period of usage, the film can be directly tore when use feel the wall has oil stains, so that effects for cleaning and beautifying kitchen and protecting the surfaces are realized at the same time, and different requirements of users are met at the same time. The cleaning agent is different from traditional aqua, and does not flow, residuals do not appear on the surfaces, after the film is tore or wiped.

Application Domain

Non-ionic surface-active compoundsOrganic detergent compounding agents

Technology Topic

Time delaysSolvent +8

Examples

  • Experimental program(6)

Example Embodiment

[0019] Example one:
[0020] Soak 5g of polyvinyl acetate (with an average degree of polymerization of 20) in 5g of dipropylene glycol methyl ether acetate for 1 hour at room temperature, then mix it with 12g of isopropanol, and then stir and pour the resulting solution at room temperature into the dissolved 2g fatty alcohol polyoxyethylene ether AEO 3 In the propylene glycol monobutyl ether (15g) solution, fully mix and dissolve to obtain solution A for use; 2g alkyl glucoside, 2g fatty alcohol polyoxyethylene ether AEO 9 And 2g of alkyl acyl sarcosine monoethanolammonium salt were dissolved in 45g of water at 50℃ in turn, mixed and dissolved thoroughly to obtain solution B for use; then 1g of sorbitol and 0.05g of Kasson were added to 8.5g of water to dissolve, and the solution was kept at room temperature Stir and pour into solution B, stir well to dissolve, and then pour it into solution A while stirring for half an hour. After stirring for half an hour, use 0.4g potassium acetate solution (mass concentration of 1%) to adjust the pH value of the solution to pH 8.5, and finally adjust 0.4% lemon flavor to serve.
[0021] Put the above-prepared cleaning agent in a sprayer and spray it on the oily surface of the range hood, and then wipe it off with paper; after wiping clean, spray the above-prepared cleaning agent on the above surface again, and it will be finished after 15 minutes at 25°C. membrane.

Example Embodiment

[0022] Embodiment two:
[0023] Soak 7g of polyvinyl acetate (average degree of polymerization of 16) in 7g of dipropylene glycol methyl ether acetate at room temperature, then mix it with 15g of isopropanol, and then stir and pour the obtained solution at room temperature to dissolve 2.4g Fatty alcohol polyoxyethylene ether AEO 3 Propylene glycol monobutyl ether (20g) solution, fully mixed and dissolved to obtain solution A for use; 2g alkyl glucoside, 1.6g fatty alcohol polyoxyethylene ether AEO 9 And 2g of alkyl acyl sarcosine monoethanolammonium salt were dissolved in 35g of 60℃ water in turn, mixed and dissolved thoroughly to obtain solution B for use; then 0.5g of sorbitol and 0.1g of Kasson were added to 6.5g of water to dissolve, and this solution was dissolved in Stir and pour into solution B at room temperature, stir well to dissolve, and then pour it into solution A while stirring for half an hour. After stirring for half an hour, the pH value of the solution can be adjusted to pH 8.5 with 0.6g sodium acetate solution (mass concentration is 1%), and finally 0.3% green tea flavor is added to serve.
[0024] Put the above-prepared cleaning agent in a sprayer and spray it on the surface of the kitchen wall, and then wipe it off with paper; after wiping clean, spray the above-prepared cleaning agent on the surface again, and turn on the range hood when the room temperature is 5℃. , A film will be formed after 20 minutes.

Example Embodiment

[0025] Embodiment three:
[0026] 6g of polyvinyl acetate (average degree of polymerization of 17) was immersed in 6g of dipropylene glycol methyl ether acetate at room temperature, and then mixed with 14g of isopropanol, and then the obtained solution was stirred at room temperature and poured into which 1.5g was dissolved Fatty alcohol polyoxyethylene ether AEO 3 In the propylene glycol monobutyl ether (15g) solution, fully mix and dissolve to obtain solution A for use; 2g alkyl glucoside, 1.5g fatty alcohol polyoxyethylene ether AEO 9 And 2 g of alkyl acyl sarcosine monoethanol ammonium salt were dissolved in 40 g of water at 60° C., mixed and dissolved thoroughly to obtain solution B for use; then 0.5 g of sorbitol and 0.1 g of Kasson were added to 10.5 g of water to dissolve, and the solution was dissolved in Stir and pour into solution B at room temperature, stir well to dissolve, and then pour it into solution A while stirring for half an hour. After stirring for half an hour, the pH value of the solution can be adjusted to pH 8.5 with 0.6g potassium acetate solution (mass concentration of 1%), and finally 0.2% spearmint flavor is added.
[0027] Put the above-prepared cleaning agent in a sprayer and spray it on the surface of the kitchen wall, and then wipe it off with paper; after wiping clean, spray the above-prepared cleaning agent on the surface again, and form a film after 11 minutes at a room temperature of 30°C.

PUM

no PUM

Description & Claims & Application Information

We can also present the details of the Description, Claims and Application information to help users get a comprehensive understanding of the technical details of the patent, such as background art, summary of invention, brief description of drawings, description of embodiments, and other original content. On the other hand, users can also determine the specific scope of protection of the technology through the list of claims; as well as understand the changes in the life cycle of the technology with the presentation of the patent timeline. Login to view more.
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products