Wood vinegar cataplasm and preparation method thereof

A technology of wood vinegar liquid and formula, which is applied in the field of medicine and achieves the effects of smooth and shiny appearance, no irritation and allergy, and improved quality

Inactive Publication Date: 2016-03-02
TIANJIN UNIV OF COMMERCE
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There is no literature report on the preparation of wood vinegar cataplasm with refined wood vinegar as the main active ingredient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The wood vinegar cataplasm of this embodiment is made from the following raw materials: kaolin 15g, water 50g, sodium polyacrylate 2.0g, gelatin 7.0g, carboxymethylcellulose sodium 1.5g, citric acid 0.09g, anhydrous aluminum chloride 0.07 g, glycerol 38g, refined wood vinegar 4g.

[0027] The preparation method is carried out according to the following steps:

[0028] (1) Heat and stir 7.0g of gelatin with 15g of water in a 54°C water bath until fully swollen, add 1.5g of sodium carboxymethylcellulose and stir until swollen, and add 2g of water to obtain solution (A);

[0029] (2) Dissolve 0.07g of anhydrous aluminum chloride and 0.09g of citric acid in 3g of water to obtain a solution (B);

[0030] (3) Put 38g of glycerol in a beaker and heat in a water bath at 54°C, add 2.0g of sodium polyacrylate into the glycerin and stir until uniformly dispersed, add 15g of kaolin and stir until uniformly dispersed, then add 30g of water, stir until fully Swell to obtain solutio...

Embodiment 2

[0034] The wood vinegar cataplasm of this embodiment is made from the following raw materials: kaolin 15g, water 50g, sodium polyacrylate 2.5g, gelatin 7.0g, carboxymethylcellulose sodium 1.5g, citric acid 0.06g, anhydrous aluminum chloride 0.05 g, glycerol 33g, refined wood vinegar 6g.

[0035] The preparation method is carried out according to the following steps:

[0036] (1) Heat and stir 7.0g of gelatin with 15g of water in a 56°C water bath until fully swollen, add 1.5g of sodium carboxymethylcellulose and stir until swollen, and add 2g of water to obtain solution (A);

[0037] (2) Dissolve 0.05g of anhydrous aluminum chloride and 0.06g of citric acid in 3g of water to obtain a solution (B);

[0038] (3) Put 33g of glycerin in a beaker and heat it in a water bath at 56°C, add 2.5g of sodium polyacrylate into the glycerin and stir until uniformly dispersed, add 15g of kaolin and stir until uniformly dispersed, then add 30g of water, stir until fully Swell to obtain solu...

Embodiment 3

[0042] The wood vinegar cataplasm of this embodiment is made from the following raw materials: kaolin 15g, water 50g, sodium polyacrylate 3.0g, gelatin 7.0g, carboxymethylcellulose sodium 1.5g, citric acid 0.06g, anhydrous aluminum chloride 0.05 g, glycerol 35g, refined wood vinegar 5g.

[0043] The preparation method is carried out according to the following steps:

[0044](1) Heat and stir 7.0g of gelatin with 15g of water in a 52°C water bath until fully swollen, add 1.5g of sodium carboxymethylcellulose and stir until swollen, and add 2g of water to obtain solution (A);

[0045] (2) Dissolve 0.05g of anhydrous aluminum chloride and 0.06g of citric acid in 3g of water to obtain a solution (B);

[0046] (3) Put 35g of glycerin in a beaker and heat it in a water bath at 52°C, add 3.0g of sodium polyacrylate into the glycerin and stir until uniformly dispersed, add 15g of kaolin and stir until uniformly dispersed, then add 30g of water, stir until fully Swell to obtain solut...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a wood vinegar cataplasm and a preparation method thereof. The wood vinegar cataplasm comprises, by weight, 15 parts of kaolin, 50 parts of water, 1.5-4 parts of sodium polyacrylate, 7-8 parts of gelatin, 1.5-2.5 parts of sodium carboxymethylcellulose, 0.03-0.09 part of citric acid, 0.01-0.07 part of anhydrous aluminum chloride, 23-48 parts of glycerol and 3-7 parts of refined pyrolignenous liquid. The wood vinegar cataplasm is proper in viscosity, flat and glossy in appearance, high in skin adherence, free of residue, non-irritant, reusable and especially suitable for treatment of intractable skin disease, and the preparation method is simple, stable and feasible.

Description

technical field [0001] The invention relates to the technical field of medicine, in particular to a wood vinegar cataplasm and a preparation method thereof. Background technique [0002] Dermatosis is one of common disease, frequently-occurring disease that seriously affects people's health, as leprosy, scabies, fungal disease, skin bacterial infection etc. Dermatosis is that after the skin is affected by internal and external factors, its shape, structure and function all change, resulting in pathological processes and correspondingly producing various clinical manifestations. The incidence rate of skin diseases is very high, most of which are relatively mild, and often do not affect health, but a few of them are severe and even life-threatening. [0003] Currently, the most widely used external ointment for skin diseases on the market is mainly corticosteroid ointment, which has a good therapeutic effect and is the mainstream drug for treating skin diseases. However, long...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61K36/00A61K9/70A61P17/00
CPCA61K9/7061A61K36/00A61K47/02A61K47/10A61K47/12A61K47/38A61K47/44A61K2236/19A61K2236/331A61K2236/53
Inventor 赵彦巧朱志勇李建颖胡燕
Owner TIANJIN UNIV OF COMMERCE