A kind of wood vinegar cataplasm and preparation method thereof
A technology of wood vinegar liquid and formula, which is applied in the field of medicine and achieves the effects of good skin followability, small medicinal smell and suitable viscosity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0026] The wood vinegar cataplasm of this embodiment is made from the following raw materials: kaolin 15g, water 50g, sodium polyacrylate 2.0g, gelatin 7.0g, carboxymethylcellulose sodium 1.5g, citric acid 0.09g, anhydrous aluminum chloride 0.07 g, glycerol 38g, refined wood vinegar 4g.
[0027] The preparation method is carried out according to the following steps:
[0028] (1) Heat and stir 7.0g gelatin with 15g water in a 54°C water bath until fully swollen, add 1.5g sodium carboxymethylcellulose and stir until swollen, and add 2g water to obtain solution (A);
[0029] (2) Dissolve 0.07g of anhydrous aluminum chloride and 0.09g of citric acid in 3g of water to obtain a solution (B);
[0030] (3) Put 38g of glycerol in a beaker and heat in a water bath at 54°C, add 2.0g of sodium polyacrylate into the glycerin and stir until uniformly dispersed, add 15g of kaolin and stir until uniformly dispersed, then add 30g of water, stir until fully Swell to obtain solution (C);
[0...
Embodiment 2
[0034] The wood vinegar cataplasm of this embodiment is made from the following raw materials: kaolin 15g, water 50g, sodium polyacrylate 2.5g, gelatin 7.0g, carboxymethylcellulose sodium 1.5g, citric acid 0.06g, anhydrous aluminum chloride 0.05 g, glycerol 33g, refined wood vinegar 6g.
[0035] The preparation method is carried out according to the following steps:
[0036] (1) Heat and stir 7.0g gelatin with 15g water in a 56°C water bath until fully swollen, add 1.5g sodium carboxymethylcellulose and stir until swollen, and add 2g water to obtain solution (A);
[0037] (2) Dissolve 0.05g of anhydrous aluminum chloride and 0.06g of citric acid in 3g of water to obtain a solution (B);
[0038] (3) Put 33g of glycerol in a beaker and heat it in a water bath at 56°C, add 2.5g of sodium polyacrylate into the glycerin and stir until uniformly dispersed, add 15g of kaolin and stir until uniformly dispersed, then add 30g of water, stir until fully Swell to obtain solution (C);
...
Embodiment 3
[0042] The wood vinegar cataplasm of this embodiment is made from the following raw materials: kaolin 15g, water 50g, sodium polyacrylate 3.0g, gelatin 7.0g, carboxymethylcellulose sodium 1.5g, citric acid 0.06g, anhydrous aluminum chloride 0.05 g, glycerol 35g, refined wood vinegar 5g.
[0043] The preparation method is carried out according to the following steps:
[0044](1) Heat and stir 7.0g gelatin with 15g water in a 52°C water bath until fully swollen, add 1.5g sodium carboxymethylcellulose and stir until swollen, and add 2g water to obtain solution (A);
[0045] (2) Dissolve 0.05g of anhydrous aluminum chloride and 0.06g of citric acid in 3g of water to obtain a solution (B);
[0046] (3) Put 35g of glycerol in a beaker and heat it in a water bath at 52°C, add 3.0g of sodium polyacrylate into the glycerin and stir until uniformly dispersed, add 15g of kaolin and stir until uniformly dispersed, then add 30g of water, stir until fully Swell to obtain solution (C);
...