A low-friction water-lubricated polymer bearing composite material

A composite material, water lubrication technology, applied in the field of composite materials, can solve the problems of poor overall lubricity, poor shock absorption performance, poor wear resistance, etc. Effect

Active Publication Date: 2018-01-09
WUCHANG SHIPBUILDING IND
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention provides a low-friction water-lubricated polymer bearing composite material, which solves the technical problems of poor wear resistance, poor shock absorption performance, poor hydrophilicity and poor overall lubricity of water-lubricated bearing materials in the prior art; Lubrication performance, technical effect of reducing dry friction and water lubrication friction coefficient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0031] Take by weight molecular weight is 4,000,000, particle diameter is 100 parts of ultra-high molecular weight polyethylene powder of 120 microns, molecular weight is 100,000, and particle diameter is 10 parts of polystyrene-ethylene-butylene triblock copolymer, The molecular weight is 150,000, 2 parts of polyvinyl alcohol with a particle size of 80 microns, 10 parts of graphite with a particle size of 2 microns, and 5 parts of molybdenum disulfide with a particle size of 0.5 microns. The above materials are mixed uniformly in a dry powder mixer. Then put it into a mold, pre-press molding under the condition of 20MPa, and then sinter in an oven at 200°C for 20 minutes, and leave it at room temperature to cool to obtain the low-friction water-lubricated polymer bearing composite material of the present invention.

example 2

[0033] Take by weight molecular weight is 6,000,000, particle diameter is 100 parts of ultra-high molecular weight polyethylene powder of 80 microns, molecular weight is 500,000, and particle diameter is 25 parts of polystyrene-ethylene-butylene triblock copolymers of 100 microns, The molecular weight is 300,000, 2 parts of polyvinyl alcohol with a particle size of 150 microns, 10 parts of graphite with a particle size of 1 micron, and 10 parts of molybdenum disulfide with a particle size of 0.5 micron, and the above materials are mixed uniformly in a dry powder mixer. Then it is put into a mold, pre-pressed at 30MPa, and then sintered in an oven at 220°C for 10 minutes. After cooling at room temperature, the low-friction water-lubricated polymer bearing composite material of the present invention is obtained.

example 3

[0035] Take by weight molecular weight is 10 million, particle diameter is 100 parts of ultra-high molecular weight polyethylene powder of 400 microns, molecular weight is 300,000, and particle diameter is 40 parts of polystyrene-ethylene-butylene triblock copolymer of 300 microns, The molecular weight is 600,000, 5 parts of polyvinyl alcohol with a particle size of 150 microns, 10 parts of graphite with a particle size of 1 micron, and 5 parts of molybdenum disulfide with a particle size of 0.5 micron. The above materials are mixed uniformly in a dry powder mixer. Then it is put into a mold, pre-pressed at 30MPa, and then sintered in an oven at 220°C for 10 minutes. After cooling at room temperature, the low-friction water-lubricated polymer bearing composite material of the present invention is obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of composite materials and discloses a low-friction water lubricating macromolecular bearing composite material which is characterized by comprising ultra-high molecular weight polyethylene, polystyrene-ethylene-butylene triblock copolymer, polyvinyl alcohol, graphite and molybdenum disulfide, wherein each 100 parts of ultra-high molecular weight polyethylene is blended with 10-40 parts of polystyrene-ethylene-butylene triblock copolymer, 2-5 parts of polyvinyl alcohol, 2-10 parts of graphite and 1-5 parts of molybdenum disulfide. The low-friction water lubricating macromolecular bearing composite material provided by the invention is formed by adopting an effective material blending scheme.

Description

technical field [0001] The invention relates to the technical field of composite materials, in particular to a low-friction water-lubricated polymer bearing composite material. Background technique [0002] Compared with traditional oil-lubricated bearings, water-lubricated bearings use water as a lubricant. They have the advantages of environmental friendliness, simple structure, low friction coefficient, and high safety performance. They are widely used in ships, ships, marine engineering, water pumps, turbines and other fields. [0003] Iron pear wood was first used in water-lubricated bearings. With the depletion of resources, rubber, fiber-reinforced phenolic resin, nylon, polytetrafluoroethylene, ultra-high molecular weight polyethylene, polyethersulfone, polyether ether ketone, polyimide, etc. Synthetic polymer alternative materials. Among all polymer materials, the special elastic behavior of rubber materials ensures its excellent vibration damping performance and s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/06C08L53/00C08L29/04C08K3/04C08K3/30B29C69/02B29L31/04
CPCB29C69/02B29L2031/04C08K2201/003C08L23/06C08L2205/03C08L2205/06C08L2207/068C08L53/00C08L29/04C08K3/04C08K2003/3009
Inventor 王才宏胡宏杰黄晓黎陈就刘忠毅郇彦杨小牛
Owner WUCHANG SHIPBUILDING IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap