A technology of lost foam casting and preparation method, which is applied in the direction of casting molding equipment, coating, casting mold, etc., which can solve the problems of difficult metal processing, high price, scrapping, etc., and achieve the effect of simplifying the production process steps and improving the strength
Inactive Publication Date: 2016-04-06
CHIZHOU ETERNAL MACHINERY MFG
View PDF4 Cites 5 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] During the production of lost foam castings, the foam will generate a large amount of gas, which will cause a large number of pores in the produced castings, and the castings will be scrapped. The traditional coating has low refractoriness, which will cause the castings to stick to sand, resulting in difficulties in gold processing or even scrapping. The low thermal strength will
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0032] A preparation method for lost foam casting coatings, comprising common coatings, quartz powder, lithium-based bentonite, white latex, CMC, active agent and water, the parts by weight of the main components are as follows:
[0033] 45 parts of quartz powder;
[0034] 3 parts of lithium bentonite;
[0035] 7 parts of white latex;
[0036] CMC0.2 copies;
[0037] Active agent 0.25-0.35 parts;
[0038] A preparation method for lost foam casting coating, the steps are as follows:
[0039] S1: Put the common paint with an appropriate amount of water in the paint bucket and stir it with a mixer for 40-90 minutes;
[0040] S2: measure the specific gravity of the coating with a Baume meter;
[0041] S3: soaking the CMC 24 hours in advance;
[0042] S4: Pour the white latex, soaked CMC and an appropriate amount of water into the paint bucket, and stir evenly with a high-speed mixer;
[0043] S5: Slowly add quartz powder into the paint bucket, and stir evenly with a high-sp...
Embodiment 2
[0049] A preparation method for lost foam casting coatings, comprising common coatings, quartz powder, lithium-based bentonite, white latex, CMC, active agent and water, the parts by weight of the main components are as follows:
[0050] 55 parts of quartz powder;
[0051] 3 parts of lithium bentonite;
[0052] 7 parts of white latex;
[0053] CMC0.2 copies;
[0054] Active agent 0.25-0.35 parts;
[0055] A preparation method for lost foam casting coating, the steps are as follows:
[0056] S1: Put the common paint with an appropriate amount of water in the paint bucket and stir it with a mixer for 40-90 minutes;
[0057] S2: measure the specific gravity of the coating with a Baume meter;
[0058] S3: soaking the CMC 24 hours in advance;
[0059] S4: Pour the white latex, soaked CMC and an appropriate amount of water into the paint bucket, and stir evenly with a high-speed mixer;
[0060] S5: Slowly add quartz powder into the paint bucket, and stir evenly with a high-sp...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a preparation method for a lost foam casting coating. The lost foam casting coating comprises a common coating, carboxy methylated cellulose (CMC), white latex, quartz powder, lithium-based bentonite, an active agent and water. The preparation method comprises the following steps that S1, an appropriate amount of water is added to the common coating, and the mixture is put in a coating bucket to be stirred through a mixer for 40-90 min; S2, a Baume meter is used for measuring the proportion of the coating; S3, the CMC is soaked 24 hours in advance; S4, the white latex, the soaked CMC and an appropriate amount of water are poured into the coating bucket to be stirred evenly through a high-speed mixer; S5, the quartz powder is slowly added into the coating bucket, and the mixture is stirred evenly through the high-speed mixer; and S6, the lithium-based bentonite is added into the coating bucket, and the mixture is stirred through the high-speed mixer for 40-60 min. Compared with other coatings, according to the preparation method, the preparation process steps are simplified, the strength of the coating is effectively improved, and the defects such as scrap inclusions, slag inclusions and sand adhesion of a casting due to the fact that in the molten iron casting process, a coating layer of a foam model is liable to fall off to generate coating scraps are overcome.
Description
technical field [0001] The invention relates to the technical field of paint preparation, in particular to a preparation method of paint for lost foam casting. Background technique [0002] During the production of lost foam castings, the foam will generate a large amount of gas, which will cause a large number of pores in the produced castings and make the castings scrapped. The low thermal strength will cause the coating on the lost foam to crack or peel off, resulting in sticky sand or coating interlayer, making the casting scrapped. Nowadays, the lost foam coating sold on the market is relatively expensive and cannot meet the production of large lost foam castings. The gas permeability, refractoriness and hot and cold strength of the lost foam coating have not yet met the requirements. Contents of the invention [0003] The purpose of the present invention is exactly in order to overcome the defective of above-mentioned prior art, has designed a kind of compound metho...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more