One-component fluorocarbon coating and preparation method thereof

A fluorocarbon coating, single-liquid technology, applied in coatings, fibrous fillers, dyed low molecular organic compounds and other directions, can solve the problems of low hardness, poor acid and alkali resistance, improve acid and alkali resistance, reduce acid The effect of alkali destruction and affinity improvement

Active Publication Date: 2018-07-20
JIANGYIN ZHONGQIANG TECH CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the coating also has the problems of poor acid and alkali resistance and low hardness.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Single-component fluorocarbon coatings, by weight parts, include the following components: 45 parts of water-based vinyl fluorocarbon emulsion, 5 parts of butyl acetate, 0.3 parts of non-ionic wetting agent, 0.7 parts of polyacrylamide, silicone 0.3 parts of defoamer, 0.7 parts of associative thickener, 11 parts of lithopone, 16 parts of organic pigment, 21 parts of water, 2.5 parts of nano-magnesium oxide, and 2.4 parts of nano-zinc hydroxide.

[0027] The steps of its preparation method are as follows:

[0028] (1) Add nano-magnesium oxide powder and nano-zinc hydroxide powder into a ball mill and mill for 3 hours, sieve and cool to room temperature naturally to obtain nano-mixed powder, add nano-mixed powder to ten times the weight of water, stir and disperse After 4 hours, the nano-mixture was obtained;

[0029] (2) Add titanate coupling agent to absolute ethanol, ultrasonically disperse at 70 Hz for 20 minutes to obtain a coupling agent solution, adjust the pH val...

Embodiment 2

[0032] Single-component fluorocarbon coatings, in parts by weight, include the following components: 55 parts of water-based vinyl fluorocarbon emulsion, 3 parts of butyl acetate, 0.7 parts of non-ionic wetting agent, 0.4 parts of polyacrylamide, silicone 0.2 parts of defoamer, 0.8 parts of associative thickener, 10 parts of lithopone, 19 parts of inorganic pigment, 23 parts of water, 3 parts of nano magnesium oxide, 4 parts of nano zinc hydroxide.

[0033] The steps of its preparation method are as follows:

[0034] (1) Add nano-magnesium oxide powder and nano-zinc hydroxide powder into a ball mill and mill for 3 hours, sieve and cool to room temperature naturally to obtain nano-mixed powder, add nano-mixed powder to ten times the weight of water, stir and disperse After 4 hours, the nano-mixture was obtained;

[0035] (2) Add titanate coupling agent to absolute ethanol, ultrasonically disperse at 70 Hz for 20 minutes to obtain a coupling agent solution, adjust the pH value ...

Embodiment 3

[0038] Single-component fluorocarbon coatings, in parts by weight, include the following components: 50 parts of water-based vinyl fluorocarbon emulsion, 4.5 parts of butyl acetate, 0.8 parts of non-ionic wetting agent, 0.2 parts of polyacrylamide, silicone 0.4 parts of defoamer, 0.6 parts of associative thickener, 15 parts of lithopone, 18 parts of inorganic pigment, 25 parts of water, 1.5 parts of nano magnesium oxide, 2.5 parts of nano zinc hydroxide.

[0039] The steps of its preparation method are as follows:

[0040] (1) Add nano-magnesium oxide powder and nano-zinc hydroxide powder into a ball mill and mill for 3 hours, sieve and cool to room temperature naturally to obtain nano-mixed powder, add nano-mixed powder to ten times the weight of water, stir and disperse After 4 hours, the nano-mixture was obtained;

[0041](2) Add titanate coupling agent to absolute ethanol, ultrasonically disperse at 70 Hz for 20 minutes to obtain a coupling agent solution, adjust the pH v...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention provides a single-liquid-type fluorocarbon coating comprising the following components by weight: 40 to 55 parts of a fluorocarbon emulsion, 3 to 6 parts of a diluent, 0.3 to 0.4 part of a wetting agent, 0.2 to 0.7 part of a dispersing agent, 0.1 to 0.6 part of a defoamer, 0.4 to 0.9 part of a thickening agent, 10 to 15 parts of a filler, 15 to 20 parts of a pigment, 20 to 25 parts of water, 1 to 3 parts of nano magnesium oxide and 2 to 4 parts of nano-zinc hydroxide. The present invention also provides a preparation method of the single-liquid-type fluorocarbon coating. The single-liquid-type fluorocarbon coating has good acid and alkali resistance and hardness.

Description

Technical field: [0001] The invention relates to a coating, in particular to a single-liquid fluorocarbon coating and a preparation method thereof. Background technique: [0002] Fluorocarbon coatings refer to coatings with fluororesin as the main film-forming substance, also known as fluorocarbon coatings, fluorine coatings, fluororesin coatings, etc. Among all kinds of coatings, fluororesin coatings have particularly superior properties—weather resistance, heat resistance, low temperature resistance, and chemical resistance due to the high electronegativity of the introduced fluorine element and strong carbon-fluorine bond energy. , and has a unique non-stick and low friction. After decades of rapid development, fluorine coatings have been widely used in various fields such as construction, chemical industry, electrical and electronic industry, machinery industry, aerospace industry, and household products. After paint, it is one of the paints with the highest comprehens...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D127/12C09C1/04C09C1/02C09C3/08
Inventor 李晓明
Owner JIANGYIN ZHONGQIANG TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com