Technology for dyeing and finishing improved terylene polyamide lycra fabrics

A technology of nylon Lycra and fabrics, which is applied in dyeing, textiles and papermaking. It can solve the problems affecting the color fastness to washing and staining of fabrics, and achieve the effects of convenient operation, cost reduction, and improvement of breathability and hygroscopicity.

Inactive Publication Date: 2016-06-01
江阴市长泾花园毛纺织有限公司
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, cationic modified polyester is more and more popular in the textile market, and it is more and more widely used in clothing fabrics; there are differences in the dyeing of cationic modified polyester and conventional polyester. Conventional polyester is dyed with disperse dyes under high temperature and pressure. Disperse dyes When dyeing polyester and nylon fabrics, there is a problem of disperse dyes staining nylon and spandex, which affects the color fastness of the fabric to washing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] The dyeing and finishing process of the improved polyester nylon Lycra fabric of embodiment 1 comprises the steps:

[0018] S1: Degreasing and refining, the fabric is placed in a multi-slot open-width washing machine for cleaning and refining. The washing liquid is composed of 0.1 part of degreasing agent, 0.1 part of soda ash, 0.05 part of chelating dispersant, and 100 parts of water. The temperature of the washing tank is 70°C.

[0019] S2: pre-setting, the pre-setting temperature is 180°C, and the processing time is 50s;

[0020] S3: Dyeing, using cationic dyes and weak acid dyes to dye the fabric in one bath;

[0021] S4: Finished product finalization: Finish the dyed fabric with a hydrophilic finishing agent. The composition of the hydrophilic finishing agent is: 2 parts of moisture-wicking finishing agent, 0.03 parts of glacial acetic acid, 98 parts of water, and hydrophilic finishing The pH of the agent is 5.

[0022] Among them, the dyeing process in S3 inclu...

Embodiment 2

[0027] The dyeing and finishing process of the improved polyester nylon Lycra fabric of embodiment 2 comprises the steps:

[0028] S1: Degreasing and refining, the fabric is placed in a multi-slot open-width washing machine for cleaning and refining. The washing liquid is composed of 0.15 parts of degreasing agent, 0.15 parts of soda ash, 0.075 parts of chelating dispersant, and 100 parts of water. The temperature of the washing tank is 75°C.

[0029] S2: presetting, the presetting temperature is 182°C, and the processing time is 55s;

[0030] S3: Dyeing, using cationic dyes and weak acid dyes to dye the fabric in one bath;

[0031] S4: Finished product finalization: Finish the dyed fabric with a hydrophilic finishing agent. The composition of the hydrophilic finishing agent is: 2.5 parts of moisture-wicking finishing agent, 1.7 parts of glacial acetic acid, 98 parts of water, and hydrophilic finishing The pH of the agent is 5~6.

[0032] Among them, the dyeing process in S...

Embodiment 3

[0037] The dyeing and finishing process of the improved polyester nylon Lycra fabric of embodiment 3 comprises the steps:

[0038] S1: Degreasing and refining, the fabric is placed in a multi-slot open-width washing machine for cleaning and refining. The washing liquid is composed of 0.2 parts of degreaser, 0.2 parts of soda ash, 0.1 part of chelating dispersant, and 100 parts of water. The temperature of the washing tank is 80°C.

[0039] S2: pre-setting, the pre-setting temperature is 185°C, and the processing time is 60s;

[0040] S3: Dyeing, using cationic dyes and weak acid dyes to dye the fabric in one bath;

[0041] S4: Finished product finalization: Finish the dyed fabric with a hydrophilic finishing agent. The composition of the hydrophilic finishing agent is: 3 parts of moisture-wicking finishing agent, 0.1 part of glacial acetic acid, 98 parts of water, and hydrophilic finishing The pH of the agent is 6.

[0042] Among them, the dyeing process in S3 includes:

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a technology for dyeing and finishing improved terylene polyamide lycra fabrics. The technology comprises steps of oil-removing refining, pre-formalization, dyeing and finished product formalization. The technology for dyeing and finishing improved terylene polyamide lycra fabrics has the advantages of high-efficiency energy saving, emission reduction, cost reduction, and convenient operation. The technology for dyeing and finishing improved terylene polyamide lycra fabrics also increases breathable moisture absorption, antistatic property and anti-pilling performances of the fabrics.

Description

technical field [0001] The invention relates to a finishing process of textiles, in particular to an improved dyeing and finishing process of polyester nylon Lycra fabric. Background technique [0002] Cationic dyeable modified polyester is made by adding other monomers to the molecular chain of conventional polyester fiber by means of copolymerization, grafting, etc.; the structure of the modified polyester fiber becomes loose, and the flexibility of the molecular chain increases, which improves the quality of conventional polyester fiber. Excellent air permeability, hygroscopicity, static electricity and pilling properties, overcome the shortcomings of conventional polyester that is not easy to dye; at the same time, it reduces the staining of dyes on nylon fibers, improves easy cleaning and wet fastness, saves energy, and improves the color after dyeing. bright. At present, cationic modified polyester is more and more popular in the textile market, and it is more and mor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06P1/39D06P3/87D06P5/04D06P5/10
Inventor 赵军伟赵明昌
Owner 江阴市长泾花园毛纺织有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com