A spraying process of release agent in banburying workshop

A release agent and workshop technology, applied in coatings, spray booths, spraying devices, etc., can solve the problems of high viscosity of mixing adhesives, difficulties in processing and transportation, mutual adhesion, etc., achieve low single-layer rate, improve efficiency, Avoid the effect of reunion

Active Publication Date: 2018-06-26
JIANGSU GENERAL SCI TECH
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the production process of rubber products, the viscosity of the mixed rubber is relatively high, and the rubber materials will stick to each other during the processing process, resulting in difficulties in processing and transportation.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A spraying process of release agent in banburying workshop
  • A spraying process of release agent in banburying workshop
  • A spraying process of release agent in banburying workshop

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] Embodiment 1: a kind of spraying process that adopts the auxiliary machine system under the internal mixer of the present invention to carry out the release agent, specifically comprises the following steps:

[0041] (1) Dissolving graphene oxide in water to obtain a graphene oxide aqueous solution, the mass percent concentration of the graphene oxide aqueous solution is 2‰, and the graphene oxide aqueous solution remains neutral;

[0042] (2) After the compounded rubber is pressed by the tablet press, the temperature of the mixed rubber is 90°C, and it is sent to the cooling pool by the conveying device. The water temperature of the cooling pool is kept below 60°C; During the process, the fan is blown dry, and with the evaporation of water, the mixed rubber material continues to cool down; in the above process, the temperature of the water in the cooling pool should be closely monitored. If the water temperature is too high, it is necessary to replace the water in the c...

Embodiment 2

[0044] Embodiment 2: a kind of spraying process that adopts the auxiliary machine system under the internal mixer of the present invention to carry out the release agent, specifically comprises the following steps:

[0045] (1) Dissolving graphene oxide in water to obtain a graphene oxide aqueous solution, the mass percent concentration of the graphene oxide aqueous solution is 3‰, and the graphene oxide aqueous solution remains neutral;

[0046] (2) After the compounded rubber is pressed by the tablet press, the temperature of the mixed rubber is 160°C, and it is sent to the cooling pool by the conveying device, and the water temperature of the cooling pool is kept below 60°C; after cooling in the cooling pool, it is transferred During the process, the fan is blown dry, and with the evaporation of water, the mixed rubber material continues to cool down; in the above process, the temperature of the water in the cooling pool should be closely monitored. If the water temperature ...

Embodiment 3

[0048] Embodiment 3: a kind of spraying process that adopts the auxiliary machine system under the internal mixer of the present invention to carry out the release agent, specifically comprises the following steps:

[0049] (1) Dissolving graphene oxide in water to obtain a graphene oxide aqueous solution, the mass percent concentration of the graphene oxide aqueous solution is 2.5‰, and the graphene oxide aqueous solution remains neutral;

[0050] (2) After the compounded rubber is pressed by the tablet press, the temperature of the mixed rubber is 100°C, and it is sent to the cooling pool by the conveying device, and the water temperature of the cooling pool is maintained below 60°C; after cooling in the cooling pool, it is transferred During the process, the fan is blown dry, and with the evaporation of water, the mixed rubber material continues to cool down; in the above process, the temperature of the water in the cooling pool should be closely monitored. If the water temp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a lower auxiliary system and a spraying process for a mixing workshop separant. The lower auxiliary system comprises a cooling section, a separant spraying section and a drying section which are arranged in sequence, wherein each of the cooling section, the separant spraying section and the drying section is provided with a conveying device; the cooling section comprises a cooling pond and a first draught fan arranged at the discharging end of the cooling pond; the drying section is provided with a second draught fan; and the separant spraying section comprises a separant pond, wherein the separant pond comprises a separant pond body, the outside of the separant pond body is sleeved by a condensed water jacket, a condensed water inlet and a condensed water outlet are formed in the condensed water jacket, an ultrasonic generator is arranged in the separant pond body, and separant nozzles are respectively arranged above and below the separant pond. Three rows of separant nozzles are arranged above the separant pond, three rows of separant nozzles are arranged below the separant pond, and three separant nozzles are arranged in each row. A graphene oxide water solution is suitable for use as a separant, so that the cost can be reduced, and the separating effect can be improved.

Description

technical field [0001] The invention relates to a spraying process of a lower auxiliary machine system and a release agent in a banburying workshop, in particular to a spraying process in which a graphene oxide aqueous solution is used as a release agent in the tire banburying production process. Background technique [0002] In the production process of rubber products, the viscosity of the mixed rubber is relatively high, and the rubber materials will stick to each other during the processing process, resulting in difficulties in processing and transportation. Therefore, before the rubber compound is finally made into a finished product, such as before handling and storing the rubber compound, extrusion, extrusion and hot mixing, a layer of release agent will be applied to the corresponding film to prevent the film from interacting with each other. Adhesion. There are many types of release agents, which have different effects on the performance of the glue. Traditional r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B05B16/20B05D1/02B05D3/00
CPCB05B15/20B05B16/20
Inventor 朱健鹏张洪学刘宇艳崔玉叶
Owner JIANGSU GENERAL SCI TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com