A gel pen ink and nano-pigment technology, applied in inks, household appliances, applications, etc., can solve the problems of poor stability and high ink viscosity, and achieve the effects of stable quality, good ink stability and reasonable formula.

Active Publication Date: 2016-08-03
SHANTOU WANHUI IND CO LTD
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a water-based nano-pigment type gel pen ink and its preparation method to solve the problems of high viscosity and poor stability of existing inks

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based nano pigment-type gel pen ink and preparation method thereof
  • Water-based nano pigment-type gel pen ink and preparation method thereof
  • Water-based nano pigment-type gel pen ink and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A carbon black water-based nano-pigment type neutral pen ink, comprising the following components and weight percentages:

[0028]

[0029] Wherein the average particle size of the black color paste is 100nm, mainly comprising the following components and weight percentages:

[0030]

[0031] The preparation method of black color paste comprises the following steps:

[0032] (1) First dissolve the dispersant BYK190 in deionized water, add Degussa 4# carbon black to make it fully wet, then add surfactant PE-100, ethylene glycol and defoamer and stir well;

[0033] (2) According to the weight ratio of the grinding ball and the mixed material obtained in step (1) is 7:3, add it to the sand mill for grinding and dispersing; wherein the particle size of the grinding ball is 0.3um;

[0034] (3) discharge and filter to obtain the black color paste without resin type nanometer.

[0035] The preparation method of the above-mentioned carbon black water-based nano-pigment ...

Embodiment 2

[0037] A kind of red water-based nano-pigment type neutral ink comprises the following components and weight percentages:

[0038]

[0039] Wherein the average particle diameter of black color paste is 250nm, comprises following component and weight percentage:

[0040]

[0041] The preparation method of red color paste comprises the following steps:

[0042] (1) First dissolve the dispersant DEGO740W in deionized water, add PR.254 red to make it fully wet, then add surfactant PE-100, propylene glycol and defoamer and stir well;

[0043] (2) According to the weight ratio of the grinding ball and the mixed material obtained in step (1) is 7:3, add it to the sand mill for grinding and dispersing; wherein the particle size of the grinding ball is 1um;

[0044] (3) discharge and filter to obtain the red color paste without resin type nanometer.

[0045] The preparation method of the above-mentioned red water-based nano-pigment type neutral pen ink is: fully stir and mix the ...

Embodiment 3

[0047] A blue water-based nano-pigment type neutral ink, comprising the following components and weight percentages:

[0048]

[0049] Wherein the average particle size of the blue color paste is 200nm; including the following components and weight percentages:

[0050]

[0051] The preparation method of blue color paste comprises the following steps:

[0052] (1) First dissolve the dispersant BYK190 in deionized water, add phthalocyanine blue BGS to make it fully wet, then add surfactant PE-100, propylene glycol and defoamer and stir well;

[0053] (2) According to the weight ratio of the grinding ball and the mixed material obtained in step (1) is 7:3, add it to the sand mill for grinding and dispersing; wherein the particle size of the grinding ball is 0.5um;

[0054] (3) The discharge is filtered to obtain the blue color paste without resin type nanometer.

[0055] The preparation method of the above-mentioned blue water-based nano-pigment type neutral pen ink is: ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to a water-based nano pigment-type gel pen ink and a preparation method thereof. The water-based nano pigment-type gel pen ink comprises the following components in percentage by weight: 20-40% of resin-free nano color paste, 10-30% of humectant, 0.1-3% of thickener, 0.2-3% of pH regulator, 0.05-0.5% of defoaming agent, 0.1-3% of lubricant, 0.2-2% of rust inhibitor, 0.2-2% of preservative and the balance of deionized water. The average particle size of the resin-free nano color paste is 100-250nm. The preparation method comprises the following steps: sufficiently stirring and uniformly mixing the components, and defoaming. By using the resin-free nano color paste, the ink has the advantages of favorable stability, proper viscosity, uniform particle fineness, smooth writing and uniform ink release without floating. The ink has the characteristics of bright color, light fastness, high water resistance and high stable quality after long-term storage, and can not have the phenomenon of stratification, precipitating deterioration or the like. The sand mill is used for grinding, so that the particle size of the pigment particles reaches nano scale. The preparation method is simple to operate and reasonable in technique.

Description

technical field [0001] The invention belongs to the field of fine chemicals, and in particular relates to a water-based nano-pigment type gel pen ink and a preparation method thereof. Background technique [0002] Neutral ink has the advantages of smooth writing, comfortable writing, clear writing, good color, and writing resistance to water, sunlight, and long storage time. It has been quickly accepted by consumers, and its market share has surpassed oil-based ballpoint pens. The growth trend, although my country has become the largest producer of gel ink pens, so far almost all the ink used in gel ink pens is imported, mainly from Japan, the United States, Germany and South Korea. [0003] Judging the comprehensive performance of neutral ink is rheological performance and stability. Rheological properties are not only related to factors such as the type of thickener, solvent, solution concentration, electrolyte strength, pH value, temperature, etc., but also related to the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/16C09D11/18C09D11/17
CPCC09D11/16C09D11/17C09D11/18
Inventor 胡镇奎朱贻顺
Owner SHANTOU WANHUI IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap