Polystyrene maple-imitation product and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of polystyrene and products, which is applied in the field of wood-like materials, can solve the problems of destroying the natural environment and low output of maple wood, and achieve the effects of slowing down felling, improving use safety, and reducing manpower
Active Publication Date: 2016-08-24
GUANGDONG PRACHTIG PAINT CO LTD
View PDF7 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, the output of maple wood is low, and if it is cut down in a large scale, it will destroy the natural environment. Therefore, it is of great practical significance to develop a kind of imitation maple wood product
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0026] The embodiments described below by referring to the figures are exemplary only for explaining the present invention and should not be construed as limiting the present invention.
[0027] The purpose of the present invention is to use polystyrene as a foaming raw material of waste packaging recycling materials as the main raw material to produce imitation maple furniture products, profiles and other products. A polystyrene imitation maple product, which is produced by mixing and extruding color particles of different colors and wood grain agents. The color particles include white, yellow, and brown. The parts by weight of each raw material are: white particles 20-40 30-60 parts of brown granules, 50-80 parts of yellow granules, 0.01-0.1 parts of brown wood grain agent, 0.005-0.05 parts of purple wood grain agent; the color granules are made of the following raw materials in parts by weight: polystyrene 70-80 parts of recycled material, 5-10 parts of modified polystyrene...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
density
aaaaa
aaaaa
surface
aaaaa
aaaaa
Rockwell hardness
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses a polystyrene maple-imitation product which is prepared by mixing and extruding color particles in different colors and wood grain agents. The color particles comprise, by weight, 20-40 parts of white particles, 30-60 parts of brown particles, 50-80 parts of yellow particles, 0.01-0.1 part of the coffee-color wood grain agent and 0.005-0.05 part of the purple wood grain agent; the color particles are prepared from, by weight, 70-80 parts of a polystyrene recycling material, 5-10 parts of modified polystyrene, 5-10 parts of foamed polystyrene, 1-5 parts of ABS, 1-10 parts of filler, 0.1-1 part of antioxidant, 0.1-1 part of plasticizer, 0.1-1 part of fire retardant and 1-10 parts of pigment; the wood grain agents are prepared from, by weight, 20-80 parts of modified polystyrene, 20-80 parts of ABS, 1-10 parts of polymeric carbon (PC) and 10-30 parts of pigment. According to the polystyrene maple-imitation product and a preparation method thereof, the waste packaging recycling material for polystyrene forming is utilized to be made into log-imitation products of different shapes, sizes and ratios, pollution, caused by waste materials, to the environment is reduced, and manpower for processing the waste materials is reduced.
Description
technical field [0001] The invention relates to a wood imitation material, in particular to a polystyrene imitation maple wood product and a preparation method thereof. Background technique [0002] Imitation wood materials refer to a class of materials that have similar appearance, texture, physical and mechanical strength, and mechanical processing performance to wood materials. They can replace traditional wood materials in some fields such as home furnishing, garden construction, and logistics. Traditional wood-like materials mainly include wood-like materials on the surface of reinforced concrete, wood-like steel pipe materials, wood-plastic materials, etc. Most of the reinforced concrete wood-like materials need log materials as molds to obtain surface wood texture, and the production cost is high. Such wood-like products It is close to wood products in appearance, has the properties of inorganic metal materials instead of wood products, and is mostly used in large and...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.