Electrode coated with conductive carbon layer on surface and preparation method of electrode

A technology of surface coating and conductive carbon, which is applied in the direction of electrode manufacturing, battery electrodes, non-aqueous electrolyte battery electrodes, etc., which can solve the problems of performance attenuation, insufficient cycle life, and insufficient power characteristics.

Inactive Publication Date: 2016-08-24
NO 63971 TROOPS PLA
View PDF0 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when the battery is used in a relatively harsh environment, such as a device that requires high-power discharge, it often faces the problem that the power characteristics are not good enough or the cycle life is not long enough under high-power conditions.
The root cause is that under high power conditions, the battery generally has a large temperature rise, and the electrodes will inevitably react with the electrolyte, resulting in performance attenuation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electrode coated with conductive carbon layer on surface and preparation method of electrode
  • Electrode coated with conductive carbon layer on surface and preparation method of electrode

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Lithium iron phosphate is used as the positive electrode active material, according to the mass fraction of lithium iron phosphate 92%, conductive carbon black 4%, polyvinylidene fluoride binder 4% to prepare a slurry, coated on a 20 micron thick aluminum foil set On both sides of the fluid, one side is coated with a thickness of 125 microns, and dried in an oven at 125°C. According to the mass fraction, 45% of activated carbon, 15% of polyvinylidene fluoride binder, and 40% of N-methylpyrrolidone are used to make a slurry, which is coated on both sides of the pole piece prepared above, and the coating thickness on one side is 10 microns. Dry again in an oven at 125°C. After compacting the obtained electrode sheet, the compacted density is 2.05g / cm 3 , to obtain a positive electrode coated with a conductive layer on the surface.

[0020] Graphite is used as the negative electrode active material, and the slurry is prepared according to the mass fraction of graphite 92...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of battery manufacturing and particularly relates to an electrode coated with a conductive carbon layer on the surface. After the electrode is coated, the conductive carbon layer coats the surface of the electrode; and the variety of conductive carbon can be activated carbon, conductive carbon black, a carbon nano tube, graphene, mesoporous carbon, a carbon fiber and the like. The conductive carbon layer coats the surface of the battery electrode, so that the electrode impedance can be greatly reduced; an active material can be effectively protected; the stability of the electrode is improved; and the electrode is especially suitable for the field of application of a high-power battery.

Description

technical field [0001] The invention relates to the field of battery manufacturing, in particular to an electrode coated with a conductive carbon layer on the surface, which can be used to prepare primary and secondary batteries, and is especially suitable for the preparation of power batteries. Background technique [0002] With the advancement of battery technology, batteries are more and more widely used in electric vehicles and high-performance equipment. However, when the battery is used in a relatively harsh environment, such as a device that requires high-power discharge, it often faces the problem that the power characteristic is not good enough or the cycle life is not long enough under high-power usage conditions. The root cause is that under high-power conditions, the battery generally has a large temperature rise, and the electrodes will inevitably react with the electrolyte, resulting in attenuation of performance. Therefore, how to increase the conductivity of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/13H01M4/62H01M4/139H01M4/04
CPCY02E60/10
Inventor 杨裕生邱景义余仲宝李萌张松通王维坤苑克国王安邦
Owner NO 63971 TROOPS PLA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com