Stone paint mixed with glass beads and preparing method of stone paint

A technology of glass microbeads and real stone paint, applied in the direction of coating, etc., can solve the problems of brightness, color vividness and color retention, color fading, etc., achieve good clarity and color retention, strong brightness, and easy to promote Applied effect

Active Publication Date: 2016-09-07
JINING SAIDELI NEW MATERIAL
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional real stone paint mainly emphasizes its adhesion, water resistance, stain resistance, and corrosion resistance, but it is far from enough to pay attention to its brightness, color clarity, and color retention.
Traditional real stone paint often fades due to long-term light

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Example 1: A method for preparing real stone paint

[0019] Add water into the paint tank, add 0.1% hydroxyethyl cellulose, 19% silicone acrylic emulsion, 0.05% wetting agent, 0.2% dispersant, 0.03% defoamer, 0.05% while stirring Mix and stir well for 10 minutes, then add 40% natural quartz sand and 35% glass beads while stirring, mix and stir well for about 20 minutes, adjust the viscosity and color after confirming uniformity, and inspect the can .

Embodiment 2

[0020] Example 2: A method for preparing real stone paint

[0021] Fill the paint tank with water, add 0.1% hydroxyethyl cellulose, 20% modified silicone acrylic emulsion, 0.07% wetting agent, 0.3% dispersant, 0.02% defoamer, while stirring. 0.1% of the film-forming aid, fully mix and stir for 10 minutes, then add 50% natural quartz sand and 25% glass beads while stirring, mix well for about 20 minutes, and adjust the viscosity and color after confirming that it is uniform. Canned.

Embodiment 3

[0022] Example 3: A method for preparing real stone paint

[0023] Add water into the paint tank, add 0.2% hydroxyethyl cellulose, 24% modified silicone acrylic emulsion, 0.1% wetting agent, 0.4% dispersant, 0.01% defoamer, while stirring. 0.3% of the film-forming additives, fully mixed and stirred for 10 minutes, then add 35% natural quartz sand and 40% glass beads while stirring, mix well for about 20 minutes, and adjust the viscosity and color after confirming that it is uniform. Canned.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a stone paint mixed with glass beads. The stone paint is prepared from, by mass, 8-14% of water, 0.1-0.2% of hydroxyethyl cellulose, 18-24% of special emulsion, 30-55% of all colors of natural quartz sand, 20-45% of glass beads, 0.01-0.1% of a wetting agent, 0.01-0.5% of a dispersing agent, 0.01-0.05% of a defoaming agent, 0.1-0.3% of a thickening agent and 0.05-0.5% of a coalescing agent. According to the stone paint, the brightness of the stone paint is enhanced by using the reflecting and refracting effects of glass beads to light; besides, the durability of glass beads is good, the color of the stone paint is not likely to change obviously after the stone paint is used for a long time, and the stone paint has the advantage that the brightness, the boldness of colors and the color retention are not affected; in addition, glass beads are used for partially replacing natural quartz sand, and the problem of mineral resource exhaustion caused by over exploitation of natural quartz ore can be well solved.

Description

Technical field [0001] The invention relates to the technical field of architectural coatings, in particular to a real stone paint mixed with glass microbeads and a preparation method thereof. Background technique [0002] In recent years, natural stone paint has been used more and more in architectural coatings due to its simple preparation process, diverse colors, and convenient construction. Traditional real stone paint mainly emphasizes its adhesion, water resistance, stain resistance, and corrosion resistance, but it is far from enough in its brightness, color vividness and color retention. Traditional real stone paint often fades due to long-term sunlight. Based on the above status, the current research on real stone paint with strong brightness and color retention is particularly important. Summary of the invention [0003] The purpose of the present invention is to overcome the above-mentioned shortcomings of the prior art and provide a real stone paint mixed with glass ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D143/04C09D7/12
CPCC09D7/61C09D7/70C09D143/04C08L1/284C08K13/04C08K3/36C08K7/20
Inventor 吴瑞立张功国司崇殿刘国栋王宇光
Owner JINING SAIDELI NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com