Tempered glass processing technology

A processing technology and tempered glass technology, applied in glass production, glass tempering, glass manufacturing equipment, etc., can solve the problems of poor control of prestress formation size, glass quality decline, easy to be unevenly heated, etc., to prevent oxidation of glass surface , improve the yield rate, and the effect of uniform force on the glass

Inactive Publication Date: 2016-09-21
HENAN HUANYU GLASS TECH CO LTD
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Tempered glass is actually a kind of prestressed glass. In order to improve the strength of glass, chemical or physical methods are usually used to form compressive stress on the glass surface. Wind pressure, cold and heat, impact, etc. In the process of using physical methods to manufacture tempered glass, it is necessary to heat up ordinary glass to the tempering temperature, and then cool it rapidly to form prestress. However, the glass is heated too fast and is prone to uneven heating. , leading to a decrease in glass quality. In addition, in the process of rapid cooling to form prestress, self-explosion is easy to occur. This is because the size of prestress formation is not easy to control. low rate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] The invention provides a technical solution: a tempered glass processing technology, which mainly includes the following steps:

[0018] A. Clean the glass surface: Use a decontamination cleaner to decontaminate the glass surface, and dry the glass surface after decontamination cleaning;

[0019] B. Preheating the glass: push the glass horizontally into the tempering furnace, and inject nitrogen gas to slowly heat the tempering furnace, so that the temperature of the glass surface rises from room temperature to 180°C, then keep the temperature for 2 minutes, and turn off the nitrogen gas;

[0020] C. Spray a layer of silica powder on the surface of the glass: pull the glass out of the tempering furnace, spray a layer of silica powder with a diameter of 0.6 microns on the surface, and then push the glass into the tempering furnace;

[0021] D. Heating the glass with high power: Slowly raise the temperature of the tempering furnace to 650°C, inject nitrogen gas during the...

Embodiment 2

[0028] The invention provides a technical solution: a tempered glass processing technology, which mainly includes the following steps:

[0029] A. Clean the glass surface: Use a decontamination cleaner to decontaminate the glass surface, and dry the glass surface after decontamination cleaning;

[0030] B. Preheating the glass: push the glass horizontally into the tempering furnace, and inject nitrogen gas to slowly heat the tempering furnace, so that the temperature of the glass surface rises from room temperature to 190°C, then keep the temperature for 2.5 minutes, and turn off the nitrogen gas;

[0031] C. Spray a layer of silica powder on the surface of the glass: pull the glass out of the tempering furnace, spray a layer of silica powder with a diameter of 0.6 microns on the surface, and then push the glass into the tempering furnace;

[0032] D. Heating the glass with high power: Slowly raise the temperature of the tempering furnace to 660°C, inject nitrogen gas during t...

Embodiment 3

[0039] The invention provides a technical solution: a tempered glass processing technology, which mainly includes the following steps:

[0040] A. Clean the glass surface: Use a decontamination cleaner to decontaminate the glass surface, and dry the glass surface after decontamination cleaning;

[0041] B. Preheating the glass: push the glass horizontally into the tempering furnace, and inject nitrogen gas to slowly heat the tempering furnace, so that the temperature of the glass surface rises from room temperature to 220°C, then keep the temperature for 3 minutes, and turn off the nitrogen gas;

[0042] C. Spray a layer of silica powder on the surface of the glass: pull the glass out of the tempering furnace, spray a layer of silica powder with a diameter of 0.6 microns on the surface, and then push the glass into the tempering furnace;

[0043] D. Heating the glass with high power: Slowly raise the temperature of the tempering furnace to 700°C, inject nitrogen gas during the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a tempered glass processing technology. The processing technology mainly comprises the following steps of glass surface cleaning, glass preheating, silicon dioxide powder spraying on the glass surface, high power heating on glass, cooling liquid spraying for cooling and natural cooling. According to the tempered glass processing technology, the production technology is simple, the made tempered glass has high surface stress and toughness, and the yield is increased; meanwhile, cooling is conducted by adopting a cooling liquid, the cooling speed can be increased, and the tempered glass cannot burst.

Description

technical field [0001] The invention relates to the technical field of tempered glass processing, in particular to a tempered glass processing technology. Background technique [0002] Tempered glass is actually a kind of prestressed glass. In order to improve the strength of glass, chemical or physical methods are usually used to form compressive stress on the glass surface. Wind pressure, cold and heat, impact, etc. In the process of using physical methods to manufacture tempered glass, it is necessary to heat up ordinary glass to the tempering temperature, and then cool it rapidly to form prestress. However, the glass is heated too fast and is prone to uneven heating. , leading to a decrease in glass quality. In addition, in the process of rapid cooling to form prestress, self-explosion is easy to occur. This is because the size of prestress formation is not easy to control. low rate. Contents of the invention [0003] The object of the present invention is to provide...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03B27/02C03B27/012
CPCY02P40/57C03B27/02C03B27/012
Inventor 焦海群
Owner HENAN HUANYU GLASS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products