Low-temperature-resistant and aging-resistant chloroprene rubber composite material

A technology of neoprene and composite materials, applied in the field of neoprene, which can solve the problems of aging, poor cold resistance and limited application of neoprene, and achieve the effects of overcoming poor low temperature resistance, improving mechanical strength, and improving stress-strain performance

Active Publication Date: 2016-09-28
扬州市兴安橡塑制品有限公司
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, chloroprene rubber has poor cold resistance, and it will show a glassy state below -40°C, and it will age under the influe

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The present invention proposes a low-temperature-resistant and aging-resistant chloroprene rubber composite material, whose raw materials include by weight: 50 parts of chloroprene rubber, 35 parts of natural rubber, 15 parts of butadiene rubber, styrene-isoprene block copolymer 15 parts of synthetic rubber, 10 parts of polybutylene terephthalate, 5 parts of maleic anhydride grafted modified natural rubber, 1 part of nano-zinc oxide, 2 parts of nano-magnesium oxide, 3 parts of stearic acid, 2,5 - 0.5 parts of dimethyl-2,5-di-tert-butyl peroxide hexane, 0.5 parts of thiocyanuric acid, 0.1 parts of triallyl trimellitate, 20 parts of nano-silica, precipitated white carbon black 10 parts, 20 parts of purple carbon black, 1 part of nano-microcrystalline cellulose, 13 parts of silane coupling agent KH-550 modified montmorillonite, 0.5 parts of anti-aging agent, 0.3 parts of accelerator NA-22, 0.1 part of accelerator TE , 0.5 parts of accelerator ZIP, 0.5 parts of vinyl tris (...

Embodiment 2

[0020] The present invention proposes a low-temperature-resistant and aging-resistant chloroprene rubber composite material, whose raw materials include by weight: 85 parts of chloroprene rubber, 20 parts of natural rubber, 35 parts of butadiene rubber, styrene-isoprene block copolymer 5 parts of synthetic rubber, 25 parts of polybutylene terephthalate, 2 parts of maleic anhydride grafted modified natural rubber, 2 parts of nano-zinc oxide, 0.5 parts of nano-magnesium oxide, 1 part of stearic acid, 2,5 - 1.5 parts of dimethyl-2,5-di-tert-butyl peroxide hexane, 0.1 part of thiocyanuric acid, 0.5 part of triallyl trimellitate, 5 parts of nano-silica, precipitated white carbon black 25 parts, 5 parts of purple carbon black, 5 parts of nanocrystalline cellulose, 2 parts of silane coupling agent KH-550 modified montmorillonite, 0.8 parts of N-cyclohexyl p-ethoxyaniline, 6-ethoxy- 1 part of 2,2,4-trimethyl-1,2-dihydroquinoline, 0.7 part of 2,2'-ethylene bis(4,6-di-tert-amylphenol), ...

Embodiment 3

[0022]The present invention proposes a low-temperature-resistant and aging-resistant chloroprene rubber composite material, the raw materials of which include by weight: 80 parts of chloroprene rubber, 24 parts of natural rubber, 30 parts of butadiene rubber, styrene-isoprene block copolymer 7 parts of synthetic rubber, 21 parts of polybutylene terephthalate, 3 parts of maleic anhydride grafted modified natural rubber, 1.8 parts of nano-zinc oxide, 0.8 parts of nano-magnesium oxide, 2.5 parts of stearic acid, 2,5 - 0.7 parts of dimethyl-2,5-di-tert-butyl peroxide hexane, 0.4 parts of thiocyanuric acid, 0.25 parts of triallyl trimellitate, 15 parts of nano-silica, precipitated white carbon black 18 parts, 20 parts of purple carbon black, 3 parts of nanocrystalline cellulose, 12 parts of silane coupling agent KH-550 modified montmorillonite, 6-ethoxy-2,2,4-trimethyl-1, 1 part of 2-dihydroquinoline, 0.8 part of thiourea antioxidant, 0.25 part of accelerator NA-22, 0.2 part of acc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention discloses a low temperature-resistant and aging-resistant chloroprene rubber composite material. The low temperature-resistant and aging-resistant chloroprene rubber composite material is prepared from the following raw materials: chloroprene rubber, natural rubber, butadiene rubber, styrene-isoprene segmented copolymer rubber, polybutylene terephthalate, maleic acid grafted modified natural rubber, nano zinc oxide, nano magnesium oxide, stearic acid, 2,5-dimethyl-2,5-di-tertiary-butyl peroxide hexane, trithiocyanuric acid, triallyl trimellitate, nano silica, precipitated silica, purple carbon black, nano microcrystalline cellulose, silane coupling agent KH-550 modified montmorillonoid, an anti-aging agent, an accelerant NA-22, an accelerant TE, an accelerant ZIP, vinyl tri(beta-methoxyl ethyoxyl) silane, dioctyl azelate, dioctyl sebacate and a titanate coupling agent NDZ-201. The low temperature-resistant and aging-resistant chloroprene rubber composite material disclosed by the invention has the advantages of high strength, good low temperature resistance and excellent aging resistance.

Description

technical field [0001] The invention relates to the technical field of chloroprene rubber, in particular to a low-temperature and aging-resistant chloroprene rubber composite material. Background technique [0002] Neoprene is one of the important varieties of synthetic rubber. It has excellent mechanical properties, heat resistance and corrosion resistance. It has been widely used in the manufacture of industrial rubber products, such as wire and cable sheaths, oil-resistant hose rubber sheets, conveyor belts, Conveyor belts and various types of adhesive tape and shoe adhesives, etc. However, chloroprene rubber has poor cold resistance, and it will show a glassy state below -40°C, and it will age under the influence of oxygen, water, ozone, etc. during long-term use. These defects limit its use in some special applications. field applications. Contents of the invention [0003] Based on the technical problems in the background technology, the present invention proposes ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L11/00C08L7/00C08L9/00C08L67/02C08L51/04C08L1/04C08K13/06C08K9/06C08K3/34C08K3/04C08K3/36C08K5/09C08K5/14C08K5/12C08K5/11C08K5/10C08K5/5425C08K3/22
CPCC08L11/00C08L2205/035C08L7/00C08L9/00C08L67/02C08L51/04C08L1/04C08K13/06C08K9/06C08K3/346C08K3/04C08K3/36C08K5/09C08K5/14C08K5/12C08K5/11C08K5/10C08K5/5425
Inventor 刘洋王雅新陈雷魏茂彬张小龙寇蔷薇杨景海
Owner 扬州市兴安橡塑制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap