Composite functional reinforcing agent for rubber production and preparation method thereof

A composite function and reinforcing agent technology, applied in the field of rubber and plastic products, can solve the problems of high production cost, large resource consumption, low reinforcement effect, etc., achieve performance improvement, reduce production cost, and promote the effect of flame retardancy

Inactive Publication Date: 2016-10-12
山东沣泉环保橡塑有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the most commonly used reinforcing agents in the rubber industry are carbon black and white carbon black, but the production cost of these products is high and expensive; followed by reinforcing agents such as silica fume, calcined kaolin and modified clay. The reinforcing effect is far lower than that

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0018] Example 1

[0019] A composite functional reinforcing agent for rubber production is composed of the following raw materials: red mud, regulator and dispersant, and the weight ratio of red mud, regulator and dispersant is 10:1.0:1.0. The adjusting agent is stearic acid and gypsum mixed in a weight ratio of 1:10, and the dispersing agent is calcium phosphate.

[0020] Preparation method: mix all the raw materials uniformly, send them into the dryer for drying, the highest temperature in the dryer does not exceed 750℃, the lowest temperature is not lower than 105℃, the discharge temperature is 120±5℃, and then the materials are put into superfine grinding It is sufficient that more than 97% of the materials reach more than 700 mesh.

[0021] The performance test of the product prepared in Example 1 is as follows:

[0022] Reinforcement: The product prepared in Example 1 is used to replace the carbon black in the rubber. The substituted carbon black accounts for 1 / 3 of the total ...

Example Embodiment

[0025] Example 2

[0026] A composite functional reinforcing agent for rubber production is composed of the following raw materials: red mud, regulator and dispersant, and the weight ratio of red mud, regulator and dispersant is 8:1.2:1.2. The adjusting agent is stearic acid and gypsum mixed in a weight ratio of 1:9, and the dispersing agent is calcium phosphate.

[0027] Preparation method: mix all the raw materials uniformly and send them to the dryer for drying. The highest temperature in the dryer does not exceed 750℃, the lowest temperature is not lower than 105℃, and the discharge temperature is 130±5℃, and then the materials are put into superfine grinding It is sufficient that more than 97% of the materials reach more than 700 mesh.

[0028] Mix all the raw materials uniformly and send them to the dryer for drying. The highest temperature in the desiccant machine should not exceed 750℃, and the discharge temperature should not be lower than 100℃. Then put the materials into ...

Example Embodiment

[0033] Example 3

[0034] A composite functional reinforcing agent for rubber production is composed of the following raw materials: red mud, regulator and dispersant, and the weight ratio of red mud, regulator and dispersant is 12:0.8:0.9. The adjusting agent is stearic acid and gypsum mixed in a weight ratio of 1:8, and the dispersing agent is calcium phosphate.

[0035] Preparation method: mix all the raw materials uniformly and send them to the dryer for drying. The highest temperature in the dryer does not exceed 750℃, the lowest temperature is not lower than 105℃, and the discharge temperature is 140±5℃, and then the materials are put into superfine grinding It is sufficient that more than 97% of the materials reach more than 700 mesh.

[0036] The performance test of the product prepared in Example 3 is as follows:

[0037] Reinforcement: The product prepared in Example 3 is used to replace the carbon black in the rubber. The substituted carbon black accounts for 1 / 3 of the to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Belonging to the field of rubber plastic products, the invention in particular relates to a composite functional reinforcing agent for rubber production and a preparation method thereof. The raw materials include: red mud, a conditioning agent and a dispersing agent. The conditioning agent is stearic acid and gypsum, the dispersing agent is calcium phosphate, and the weight ratio of the red mud, the conditioning agent and the dispersing agent is 8-12:0.8-1.2:0.8-1.2. The composite functional reinforcing agent provided by the invention realizes utilization of waste red mud, has a good reinforcing effect on rubber products, can partially replace carbon black and white carbon black, can completely replace other traditional inorganic filler (like potter's clay, ordinary silicon powder and calcium carbonate, etc) in the rubber formula of rubber products, also can serve as a rubber reinforcing agent and filler. At the same time, the composite functional reinforcing agent also has vulcanization promoting and flame retardant effects, thereby reducing the dosage of carbon black, a vulcanization accelerator, a flame retardant and other expensive raw materials involved in the rubber formula, lowering the production cost of rubber products, and improving the performance of the prepared product.

Description

Technical field [0001] The invention belongs to the field of rubber and plastic products, and specifically relates to a composite functional reinforcing agent for rubber production and a preparation method thereof. Background technique [0002] At present, the most commonly used reinforcing agents in the rubber industry are carbon black and white carbon black, but these products are expensive and expensive; followed by silica fume, calcined kaolin and modified clay and other reinforcing agents. The reinforcing effect is far lower than that of carbon black reinforcing agents, and the production cost is slightly lower than that of carbon black, which has a certain market share. However, the above two types of reinforcing agents are only used as reinforcing or filling materials for rubber production, and their sources require a large amount of resources. Summary of the invention [0003] In view of the shortcomings of the existing technology, the purpose of the present invention is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L21/00C08K13/08C08K11/00C08K5/09C08K3/32C08K3/30
CPCC08K3/30C08K3/32C08K5/09C08K11/005C08K13/08C08K2003/3045C08K2003/325C08L2201/02C08L21/00
Inventor 彭栋卞江
Owner 山东沣泉环保橡塑有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap