Safe and harmless inorganic salt wine barrel material and preparation method thereof

A technology of inorganic salt and wine barrels, which is applied in clay products, other household utensils, transportation and packaging, etc., and can solve problems such as unsafe use, high radioactivity, and harm to human health

Active Publication Date: 2019-07-12
NANTONG TAIYING NEW MATERIAL SCI & TECH CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the inorganic salt wine barrel materials currently on the market have defects of high radioactivity, which is unsafe to use and endangers human health

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0015] The present invention also provides a method for preparing the above-mentioned safe and harmless inorganic salt barrel material, the method comprising: mixing the water, hard clay, soft soil, silicon dioxide, flux, dispersant and red clay , to prepare and mix the safe and harmless inorganic salt barrel material.

[0016] In the above preparation method, in the mixing, the mixing is carried out by means of mechanical agitation, the speed and time of the mechanical agitation can be selected in a wide range, but from the preparation efficiency of the safe and harmless inorganic salt barrel material From the perspective of energy saving, preferably, the stirring speed is 600-800rpm, and the stirring time is 1-3h.

Embodiment 1

[0019] Choose a reaction vessel, add the following raw materials in parts by weight: 33 parts of water, 56 parts of calcite, 7 parts of black mud, 6 parts of silicon dioxide, 3 parts of calcium oxide, 3 parts of water glass and 10 parts of laterite with a particle size of 53 μm Wherein, at a rotating speed of 600rpm, mechanically stirred for 3 hours to obtain the safe and harmless inorganic salt wine barrel material A1.

Embodiment 2

[0021] Choose a reaction vessel, the following raw materials by weight: 46 parts of water, 75 parts of dolomite, 18 parts of Zimujie soil, 8 parts of silicon dioxide, 7 parts of magnesium oxide, 8 parts of sodium tripolyphosphate and 10 parts of particle size 76 μm red clay was added thereto, and mechanically stirred for 1 hour at a rotational speed of 800 rpm to obtain the safe and harmless inorganic salt wine barrel material A2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The present invention discloses a safety harmless inorganic salt barrel material and a preparation method thereof; the safety harmless inorganic salt barrel material is made from the following materials: water, hard clay, soft clay, silicon dioxide, a cosolvent, a dispersant and red clay, wherein with respect to 10 parts by weight of red clay, the water is 30-50 parts by weight, the hard clay is 50-80 parts by weight, the soft clay is 5-20 parts by weight, the silicon dioxide is 5-10 parts by weight, the cosolvent is 2-8 parts by weight, and the dispersant is 2-10 parts by weight. The safety harmless inorganic salt barrel material according to the invention is low in radioactivity, safe to use and harmless to human body health.

Description

technical field [0001] The invention relates to an inorganic salt wine barrel material, in particular to a safe and harmless inorganic salt wine barrel material and a preparation method thereof. Background technique [0002] Wine barrel, a container used to hold wine. Wine is a mixed solution containing various organic substances. In order to maintain the quality of the wine contained in the barrel, we have various requirements for the performance of the barrel material. Common wine barrel materials are wood, metal and inorganic salt. For the wooden wine barrel material, the wooden wine barrel material provides a beneficial environment for the growth and reproduction of enzymes, which is conducive to the fermentation and maturation of the wine, and the wine liquid is more mellow and delicious after further fermentation. However, the wooden material is loose and has many gaps, so most of the wine barrels made of wooden wine barrel materials have the defect of wine leakage; ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/16C04B33/13B65D13/00B65D85/72
CPCB65D13/00B65D85/72C04B33/131C04B33/16C04B2235/3201C04B2235/3206C04B2235/3208C04B2235/3427C04B2235/3445C04B2235/442C04B2235/447C04B2235/96
Inventor 万红旗
Owner NANTONG TAIYING NEW MATERIAL SCI & TECH CO LTD