Conductive waterborne ink and preparing method thereof

A technology of water-based inks and conductive fillers, applied in botany equipment and methods, inks, chemicals for biological control, etc., can solve the problems of ink adhesion, brightness reduction, poor printing effect, etc., to overcome poor conductivity Stable, good antibacterial effect, improved conductivity and stability

Inactive Publication Date: 2016-11-16
佛山市高明区尚润盈科技有限公司
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] During the printing process of ink, static electricity will easily lead to poor printing effect
In order to reduce the harm caused by static electricity, people usually add antistatic additives to the ink to suppress the generation of static charge and promote the leakage of static charge. Antistatic additives can reduce the resistance of the ink, but at the same time the adhesion and brightness of the ink will decrease. , the printing effect is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Conductive waterborne ink and preparing method thereof
  • Conductive waterborne ink and preparing method thereof
  • Conductive waterborne ink and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A kind of preparation method of antibacterial composite material, it comprises the following steps:

[0030] (1) Preparation of graphene quantum dot suspension: weigh 0.5g of C60 powder, measure 50ml of concentrated sulfuric acid with a mass fraction of 98%, mix C60 powder and concentrated sulfuric acid in a beaker, place the beaker in an ice-water bath, and simultaneously Stir at a speed of 500rpm to obtain a mixed solution; weigh 3g of potassium permanganate powder, and slowly add it to the above mixed solution; remove the ice-water bath and replace it with a water bath, keep the temperature of the water bath at 30~40°C, and react for 8 hours; quickly add 200ml of pure Water, filtered, and then dialyzed for 3 days with a dialysis bag with a molecular weight cut-off of 1000 to obtain a suspension of graphene quantum dots; the suspension of graphene quantum dots was stirred at a speed of 100 rpm, while laser irradiation was performed for 30 minutes, and the laser irradia...

Embodiment 2

[0039] A kind of preparation method of antibacterial composite material, it comprises the following steps:

[0040] (1) Preparation of graphene quantum dot suspension: Weigh 0.7g of C60 powder, measure 80ml of concentrated sulfuric acid with a mass fraction of 98%, mix C60 powder and concentrated sulfuric acid in a beaker, place the beaker in an ice-water bath, and simultaneously Stir at a speed of 500rpm to obtain a mixed solution; weigh 2g of potassium permanganate powder, and slowly add it to the above mixed solution; remove the ice-water bath and replace it with a water bath, keep the temperature of the water bath at 30-40°C, and react for 6 hours; quickly add 200ml of pure Water, filtered, and then dialyzed for 3 days with a dialysis bag with a molecular weight cut-off of 1000 to obtain a suspension of graphene quantum dots; the suspension of graphene quantum dots was stirred at a speed of 100 rpm, while laser irradiation was performed for 45 minutes, and the laser irradia...

Embodiment 3

[0049] A kind of preparation method of antibacterial composite material, it comprises the following steps:

[0050] (1) Preparation of graphene quantum dot suspension: Weigh 0.8g of C60 powder, measure 100ml of concentrated sulfuric acid with a mass fraction of 98%, mix C60 powder and concentrated sulfuric acid in a beaker, put the beaker in an ice-water bath, and simultaneously Stir at a speed of 500rpm to obtain a mixed solution; weigh 1g of potassium permanganate powder, and slowly add it to the above mixed solution; remove the ice-water bath and replace it with a water bath, keep the temperature of the water bath at 30-40°C, and react for 5 hours; quickly add 100ml of pure Water, filtered, and then dialyzed for 3 days with a dialysis bag with a molecular weight cut-off of 1000 to obtain a suspension of graphene quantum dots; the suspension of graphene quantum dots was stirred at a speed of 100 rpm, while laser irradiation was performed for 60 minutes, and the laser irradiat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparing method of conductive waterborne ink. The preparing method includes the following steps that 1, a half of waterborne polyurethane resin, a half of antibacterial composite materials and a half of conductive filler are added into a reaction kettle and stirred to be even, an emulsifying agent is dropwise added, heating, heat preservation and cooling are carried out, a dispersing agent and waterborne pigment are added, the mixture is stirred to be even, and then color paste is grinded, prepared and filtered; 2, the residual waterborne polyurethane resin, water, a neutralizing agent, a solubilizing assistant and an antifoaming agent are added into the color paste, the mixture is dispersed through a grinding miller, and when the fineness is 5 microns or below, packaging is carried out, and the waterborne ink is obtained. According to the preparing method, the conductive filler and the antibacterial composite materials are reasonably matched, and the ink has the conduction characteristic and further has the lasting antibacterial performance.

Description

technical field [0001] The invention relates to the technical field of ink, in particular to a conductive water-based ink and a preparation method thereof. Background technique [0002] With the enhancement of people's ecological awareness, the development and application of environmentally friendly materials have been paid more and more attention. Inks are developing in the direction of high-performance and environmentally friendly. Among them, water-based inks are mainly water-based and equipped with non-toxic water-based binders. Much favored by the printing industry. [0003] During the printing process of ink, static electricity will easily lead to poor printing effect. In order to reduce the harm caused by static electricity, people usually add antistatic additives to the ink to suppress the generation of static charge and promote the leakage of static charge. Antistatic additives can reduce the resistance of the ink, but at the same time the adhesion and brightness ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/102C09D11/03C09D11/52A01N59/16A01P1/00
CPCC09D11/102A01N59/16C09D11/03C09D11/52
Inventor 陆庚
Owner 佛山市高明区尚润盈科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap