Method for preparing photochromic corrugated board

A photochromic, corrugated cardboard technology, applied in paper, papermaking, paper coating, etc., can solve environmental pollution and other problems, achieve the effects of improving indoor air quality, smooth conductive channels, and reducing resistivity

Inactive Publication Date: 2017-01-04
佛山市高明区尚润盈科技有限公司
View PDF10 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, most of the existing coatings are solvent-based coatings, which seriously pollute the environment. With the strengthening of environmental protection awareness, more and more people begin to pay attention to environmentally friendly conductive, antibacterial and other functional types, but few reports have both Multifunctional coatings for corrugated board

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing photochromic corrugated board
  • Method for preparing photochromic corrugated board
  • Method for preparing photochromic corrugated board

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A kind of preparation method of antibacterial composite material, it comprises the following steps:

[0032] (1) Preparation of graphene quantum dot suspension: weigh 0.5g of C60 powder, measure 50ml of concentrated sulfuric acid with a mass fraction of 98%, mix C60 powder and concentrated sulfuric acid in a beaker, place the beaker in an ice-water bath, and simultaneously Stir at a speed of 500rpm to obtain a mixed solution; weigh 3g of potassium permanganate powder, and slowly add it to the above mixed solution; remove the ice-water bath and replace it with a water bath, keep the temperature of the water bath at 30~40°C, and react for 8 hours; quickly add 200ml of pure Water, filtered, and then dialyzed for 3 days with a dialysis bag with a molecular weight cut-off of 1000 to obtain a suspension of graphene quantum dots; the suspension of graphene quantum dots was stirred at a speed of 100 rpm, while laser irradiation was performed for 30 minutes, and the laser irradia...

Embodiment 2

[0041] A kind of preparation method of antibacterial composite material, it comprises the following steps:

[0042] (1) Preparation of graphene quantum dot suspension: Weigh 0.7g of C60 powder, measure 80ml of concentrated sulfuric acid with a mass fraction of 98%, mix C60 powder and concentrated sulfuric acid in a beaker, place the beaker in an ice-water bath, and simultaneously Stir at a speed of 500rpm to obtain a mixed solution; weigh 2g of potassium permanganate powder, and slowly add it to the above mixed solution; remove the ice-water bath and replace it with a water bath, keep the temperature of the water bath at 30-40°C, and react for 6 hours; quickly add 200ml of pure Water, filtered, and then dialyzed for 3 days with a dialysis bag with a molecular weight cut-off of 1000 to obtain a suspension of graphene quantum dots; the suspension of graphene quantum dots was stirred at a speed of 100 rpm, while laser irradiation was performed for 45 minutes, and the laser irradia...

Embodiment 3

[0051] A kind of preparation method of antibacterial composite material, it comprises the following steps:

[0052] (1) Preparation of graphene quantum dot suspension: Weigh 0.8g of C60 powder, measure 100ml of concentrated sulfuric acid with a mass fraction of 98%, mix C60 powder and concentrated sulfuric acid in a beaker, put the beaker in an ice-water bath, and simultaneously Stir at a speed of 500rpm to obtain a mixed solution; weigh 1g of potassium permanganate powder, and slowly add it to the above mixed solution; remove the ice-water bath and replace it with a water bath, keep the temperature of the water bath at 30-40°C, and react for 5 hours; quickly add 100ml of pure Water, filtered, and then dialyzed for 3 days with a dialysis bag with a molecular weight cut-off of 1000 to obtain a suspension of graphene quantum dots; the suspension of graphene quantum dots was stirred at a speed of 100 rpm, while laser irradiation was performed for 60 minutes, and the laser irradiat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Concentrationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing a photochromic corrugated board. The method comprises the following steps: (1) preparing an antibacterial / negative ion solution; (2) preparing a conductive / photochromic solution; (3) mixing the antibacterial / negative ion solution with the conductive / photochromic solution, adding a defoaming agent, a thickening agent and a modifier in turn, and carrying out high-speed dispersion to obtain an antibacterial antistatic coating; and (4) coating the antibacterial antistatic coating on a corrugated board to prepare the photochromic corrugated board. According to the method disclosed by the invention, conductive fillers, a negative ion complex, a photochromic compound and an antibacterial composite material are reasonably matched for the corrugated board, so that the corrugated board has antistatic properties and durable antibacterial properties, and has characteristics of photochromism and air purification.

Description

technical field [0001] The invention relates to a preparation method of photochromic corrugated cardboard. Background technique [0002] In recent years, the electrostatic protection packaging market has been expanding, but the form of packaging materials is very single, that is, using anti-static plastic bags as inner packaging, and then using cartons or plastic boxes as transportation packaging is the main packaging form at present, but for the protection of large and medium-sized products The packaging is not suitable, and the cost is high and the operation is complicated. It is of great engineering value to research and develop new corrugated cardboard and cartons with static conduction function, and its industrialization prospect is very broad at the same time. At present, it is convenient and quick to apply conductive paint on the surface of corrugated cardboard, and the cost is low. [0003] However, most of the existing coatings are solvent-based coatings, which se...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D21H19/10D21H21/36D21H21/14D21H21/08D21H21/12
CPCD21H19/10D21H21/08D21H21/12D21H21/14D21H21/36
Inventor 陆庚
Owner 佛山市高明区尚润盈科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com