Antistatic sheet and preparation method thereof

An antistatic and antistatic liquid technology, applied in conductive coatings, coatings, etc., can solve problems such as the influence of environmental humidity, the risk of carbon powder dropping, and low surface resistivity, and achieve long-lasting and effective antistatic effects and good antistatic effects , the effect of high heat deformation temperature

Inactive Publication Date: 2016-11-23
GUANGDONG ZHENGYE TECH
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] In view of the above-mentioned deficiencies in the prior art, the purpose of the present invention is to provide an antistatic sheet and a preparation method thereof, so as to solve the problem of poor antistatic effect of the plastic sheet produced by the current surfactant-based antistatic agent, and relatively low influence of environmental humidity. Large, poor antistatic durability, easy to contaminate products in contact with it, and the surface resistivity of plastic sheets made of intrinsically conductive or static dissipative polymers is not low enough and the cost is high, and the film made of conductive carbon black The strength and toughness are poor, there is a risk of falling off the charcoal powder and it can only be made into black.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antistatic sheet and preparation method thereof
  • Antistatic sheet and preparation method thereof
  • Antistatic sheet and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] An antistatic sheet, comprising a polyolefin sheet, and a permanent polymer antistatic layer coated on one side of the polyolefin sheet; the total thickness of the antistatic sheet is 0.15mm, and the permanent The thickness of the polymer antistatic layer is 0.5um. The following are all by mass, the polyolefin sheet contains polypropylene, and also contains 5% calcium carbonate filler masterbatch and 0.2% toner; the permanent polymer antistatic layer is a permanent antistatic polymer layer containing The antistatic liquid of the antistatic agent is formed after drying and curing; the permanent polymer antistatic agent is polyaniline, and the content of polyaniline in the antistatic liquid is 5%, and the antistatic liquid contains polyaniline and thermosetting A water-based coating solution of resin; the antistatic solution contains an adhesion promoter, and the adhesion promoter contains an amino-modified silane compound.

Embodiment 2

[0047] An antistatic sheet, comprising a polyolefin sheet, and a permanent polymer antistatic layer coated on one side of the polyolefin sheet; the total thickness of the antistatic sheet is 1.5mm, and the permanent The thickness of the polymer antistatic layer is 5um. The following are all based on mass, the polyolefin sheet contains polyethylene, and also contains 10% talcum powder filler masterbatch, 2% pigment, and a total of 1% of known lubricants, antioxidants, toughening The processing aid of the agent; the permanent macromolecular antistatic layer is formed after the antistatic liquid containing the macromolecule permanent antistatic agent is dried and solidified; the macromolecule permanent antistatic agent is polypyrrole, and polypyrrole is in The content in the antistatic liquid is 10%, and the antistatic liquid is a solvent-based coating liquid containing polypyrrole and a thermosetting resin; the antistatic liquid does not contain an adhesion promoter, and the pol...

Embodiment 3

[0049] A kind of antistatic sheet material, comprises polyolefin sheet material, and the permanent macromolecule antistatic layer that is coated on described polyolefin sheet material both sides; The total thickness of described antistatic sheet material is 2.5mm, and described permanent The thickness of the polymer antistatic layer is 8um. The following are all based on mass, the polyolefin sheet contains a mixture of polypropylene and polyethylene, and also contains 15% calcium carbonate and talcum powder filler masterbatch, 1% color masterbatch, and a total of 2.5% known A processing aid comprising a lubricant, an antioxidant, and a toughening agent; the permanent polymer antistatic layer is formed after drying and curing of an antistatic liquid containing a permanent polymer antistatic agent; the permanent polymer antistatic layer The antistatic agent is polythiophene, and the content of polythiophene in the antistatic liquid is 15%, and the antistatic liquid is a solvent-...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to view more

Abstract

The invention discloses an antistatic sheet and preparation method thereof. The antistatic sheet comprises a polyolefin sheet and permanent macromolecule antistatic layers coated on one surface or two surfaces of the polyolefin sheet, and antistatic liquid containing the permanent macromolecule antistatic agents is coated on the surface of the polyolefin sheet and then dried and solidified to form the permanent macromolecule antistatic layers. The antistatic sheet is suitable for mass industrial production, low in cost, durable, effective and good in antistatic effect, low in environment temperature-humidity influence, high in heat-resisting deformation temperature, good in mechanical property and wide in application, and surface electrical resistivity is 105-1010ohm/o.

Description

technical field [0001] The invention relates to the field of antistatic polymer materials and products, in particular to an antistatic sheet and a preparation method thereof. Background technique [0002] PP and PE polyolefin sheets have low density, good temperature resistance, high heat distortion temperature, good chemical compatibility, good tensile strength and wear resistance, balanced hardness and impact resistance, easy to obtain raw materials, and low price. Low and widely used as packaging materials in various industries, but because PP and PE are non-polar polymer materials with high crystallinity and small surface energy, they are good insulators with a surface resistivity of up to 10 14 Ω / □ (ohm / square) or more, it is easy to accumulate static electricity and damage electronic products, and it is easy to absorb dust. It is not suitable for purification and clean workshops, so generally it cannot be directly applied to electronic components and printed circuit bo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08J7/04C09D179/04C09D179/02C09D165/00C09D5/24C09D7/12C08L23/12C08L23/06C08K3/26C08K3/34B29C71/00
CPCB29C71/0081C08J7/0427C08J2323/06C08J2323/12C08J2465/00C08J2479/02C08J2479/04C08K3/26C08K3/34C08K2003/265C08L23/06C08L23/12C08L2201/04C08L2201/08C08L2205/02C08L2310/00C09D5/24C09D7/65C09D165/00C09D179/02C09D179/04C08L65/00C08L79/04
Inventor 曹四峰徐地明许折云苏华弟刘佳鑫李磊桂礼家
Owner GUANGDONG ZHENGYE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap