High impact resistant mobile phone glass cover-plate and manufacturing technology thereof

A glass cover plate and manufacturing process technology, applied in glass manufacturing equipment, manufacturing tools, glass tempering and other directions, can solve the problems of inability to recycle, poor brightness of the cover plate, weak color resistance, etc., and achieve good curing effect. , Fast curing speed, good color saturation

Inactive Publication Date: 2016-12-07
DONGGUAN JINGBO PHOTOELECTRIC BIT CO
View PDF8 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the rapid development of the communication field, electronic products have become an indispensable entertainment and communication tool for people. Electronic product covers are also full of tricks, but traditional electronic product covers are mostly printed with ordinary solvent-based inks. These electronic products The brightness of the cover plate is too poor, the color resistance is not strong, it is easy to age, and it is not conducive to environmental protection, so it cannot be recycled. UV ink is ultraviolet curing ink, which refers to the use of ultraviolet light of different wavelengths and energies under ultraviolet irradiation. The monomer in the ink binder is polymerized into a polymer to make the ink film-forming and drying ink. This kind of UV ink has a significant development prospect from the perspective of environmental protection, quality, color and technological development.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High impact resistant mobile phone glass cover-plate and manufacturing technology thereof
  • High impact resistant mobile phone glass cover-plate and manufacturing technology thereof
  • High impact resistant mobile phone glass cover-plate and manufacturing technology thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0061] (1) Cutting: Select raw white glass and cut it into small pieces of white glass;

[0062] (2) Finishing: finishing the cut glass white sheet to the required appearance size;

[0063] (3) One-time flat grinding: frosting the surface of the finished glass white sheet;

[0064] (4) Strengthening: high-temperature strengthening of the frosted glass white sheet;

[0065] (5) Secondary flat grinding: frosting the edge of the strengthened glass white sheet;

[0066] (6) One-time cleaning: clean the flat-ground glass white flakes to obtain a glass cover;

[0067] (7) Silk screen printing: multiple screen printing is performed on the surface of the glass cover, including the following steps in turn:

[0068] A manufacturing process for a high-impact mobile phone glass cover, comprising the steps of:

[0069] A. The first mirror silver printing: use screen printing technology to scrape the first mirror silver printing layer on the LOGO 1 of the glass cover, and dry and solidi...

Embodiment 2

[0089] The difference between this embodiment and the above-mentioned embodiment 1 is that in the step A, the materials required for printing are composed of mirror silver ink, hardener and thinner in a weight ratio of 10:0.45:0.15, and the printed screen is steel The hardness of the net and squeegee rubber is 75A, the curing temperature is 145°C, and the curing time is 18 minutes.

[0090] In the step B, the materials required for printing are composed of black ink, hardener and thinner in a weight ratio of 10:0.9:0.15, the printed screen is 165T, the hardness of the squeegee is 75A, and the overall thickness of the printing ink is 4.5 μm.

[0091] In the step C, the materials required for printing are composed of golden ink and hardener in a weight ratio of 10:0.9, the golden ink is a mixture of varnish, golden powder and silver powder in a weight ratio of 25:2.6:2.8, and the printed screen It is 140T, the hardness of the squeegee is 75A, and the overall thickness of the pr...

Embodiment 3

[0099] The difference between this embodiment and the above-mentioned embodiment 1 is that in the step A, the materials required for printing are composed of mirror silver ink, hardener and thinner in a weight ratio of 10:0.5:0.2, and the printed screen is steel The hardness of the net and squeegee rubber is 80A, the curing temperature is 150°C, and the curing time is 15 minutes.

[0100] In the step B, the materials required for printing are composed of black ink, hardener and thinner in a weight ratio of 10:1:0.2, the printed screen is 165T, the hardness of the squeegee is 80A, and the overall thickness of the printing ink is 5 μm .

[0101] In the step C, the materials required for printing are composed of golden ink and hardener in a weight ratio of 10:1, the golden ink is a mixture of varnish, golden powder and silver powder in a weight ratio of 25:2.8:3, and the printed screen The hardness of the squeegee is 140T, the hardness of the squeegee is 80A, and the overall thi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of a mobile phone glass cover-plate, in particular to a high impact resistant mobile phone glass cover-plate and manufacturing technology thereof. The manufacturing technology comprises the following steps of (1) cutting; (2) fine machining; (3) grinding, that is, conducting sanding treatment on the surface of a fine machined plate glass; (4) reinforcing; (5) plane grinding; (6) the first time of cleaning; (7) silk printing, specifically, silk printing comprises the following steps of the first time of mirror-like silver printing, the second time of black printing, the third time of gold printing, the fourth time of gold printing, the fifth time of bluish violet printing, the sixth time of black printing, the seventh time of white printing, and the eighth time of gloss oil printing; and (8) the second time of cleaning, that is, the glass cover-plate is cleaned neatly after being subjected to the silk printing treatment, and then the high impact resistant mobile phone glass cover-plate is obtained. The obtained high impact resistant mobile phone glass cover-plate has the advantages that impact resistance is good; abrasive resistance is high; brightness is good; color stability is high; the effect of environment protection is achieved; and water resistant performance, acid and alkali resistant performance and ageing resistant performance are better.

Description

Technical field: [0001] The invention relates to the technical field of mobile phone glass cover plates, in particular to a high-impact mobile phone glass cover plate and a manufacturing process thereof. Background technique: [0002] With the rapid development of the communication field, electronic products have become an indispensable entertainment and communication tool for people. Electronic product covers are also full of tricks, but traditional electronic product covers are mostly printed with ordinary solvent-based inks. These electronic products The brightness of the cover plate is too poor, the color resistance is not strong, it is easy to age, and it is not conducive to environmental protection, so it cannot be recycled. UV ink is ultraviolet curing ink, which refers to the use of ultraviolet light of different wavelengths and energies under ultraviolet irradiation. The monomer in the ink binder is polymerized into a polymer to make the ink film-forming and drying ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B41M1/12C03B27/012C03C17/34H04M1/02
CPCB41M1/12C03B27/012C03C17/007C03C17/009C03C17/34C03C2217/43C03C2218/119H04M1/026
Inventor 徐贤德
Owner DONGGUAN JINGBO PHOTOELECTRIC BIT CO
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap