Thickening styrene-acrylic emulsion for ammonification reaction and preparation method thereof

A technology of styrene-acrylic emulsion and ammoniation reaction, applied in the direction of coating, etc., can solve the problems of many ingredients, high cost, and poisonous tert-butyl hydroperoxide, etc., and achieve simple and easy-to-obtain raw materials, low production cost, and simple preparation process easy effect

Inactive Publication Date: 2016-12-07
SHANGHAI UNIV
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Chinese patent application number is 200810117667.4 patent document discloses a kind of benzene-acrylic emulsion, relates to a kind of styrene, methyl methacrylate, methacrylic acid, butyl acrylate, ammonium persulfate, tert-butyl hydroperoxide, Non-toxic, safe, and waterproof styrene-acrylic emulsion prepared from sodium polyacrylate and other raw materials, but the tert-butyl hydroperoxide in the raw material is toxic and flammable, and there is a greater danger
Chinese patent application number 201010531412.X discloses a patented styrene-acrylic emulsion with carboxylic acid groups and a styrene-acrylic emulsion interior wall paint and its preparation method, and discloses a styrene-acrylic emulsion with carboxylic acid groups , the coating prepared by the emulsion can react with the epoxy groups, carboxylic acid groups and multivalent metal ions carried in the coating with the evaporation of water and the drop of pH value under medium and low temperature conditions, and finally Form a coating film with water resistance, washing resistance and stain resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0042] Embodiment one:

[0043] In the present embodiment, a method for preparing thickened styrene-acrylic emulsion by ammoniation reaction comprises the following steps:

[0044] a. Preparation of raw materials and ingredients:

[0045] The raw material components and mass percentages of the ammoniated reaction thickened styrene-acrylic emulsion to be prepared are respectively:

[0046] Styrene 19.9%;

[0047] Butyl Acrylate 13.2%;

[0048] Acrylic acid 1.2%;

[0049] Emulsifier A 0.48%;

[0050] Emulsifier B 0.48%;

[0051] Initiator 0.2%;

[0052] Buffer 0.36%;

[0053] Defoamer 0.048%;

[0054] The remaining amount of deionized water;

[0055] Described emulsifier A is sodium lauryl sulfate, belongs to anionic surfactant;

[0056] The emulsifier B is an alkylphenol polyoxyethylene ether, which belongs to a nonionic surfactant;

[0057] Described initiator is ammonium persulfate;

[0058] The defoamer is a general-purpose water-based defoamer;

[0059] Describ...

Example Embodiment

[0072] Embodiment two:

[0073] This embodiment is basically the same as Embodiment 1, especially in that:

[0074] In the present embodiment, a method for preparing thickened styrene-acrylic emulsion by ammoniation reaction comprises the following steps:

[0075] a. Preparation of raw materials and ingredients:

[0076] The raw material components and mass percentages of the ammoniated reaction thickened styrene-acrylic emulsion to be prepared are respectively:

[0077] Styrene 18.6%;

[0078] Butyl Acrylate 13.2%;

[0079] Acrylic acid 2.38%;

[0080] Emulsifier A 0.48%;

[0081] Emulsifier B 0.48%;

[0082] Initiator 0.2%;

[0083] Buffer 0.6%;

[0084] Defoamer 0.048%;

[0085] The remaining amount of deionized water;

[0086] Described emulsifier A is sodium lauryl sulfate, belongs to anionic surfactant;

[0087] The emulsifier B is an alkylphenol polyoxyethylene ether, which belongs to a nonionic surfactant;

[0088] Described initiator is ammonium persulfate...

Example Embodiment

[0103] Embodiment three:

[0104] This embodiment is basically the same as the previous embodiment, and the special features are:

[0105] In the present embodiment, a method for preparing thickened styrene-acrylic emulsion by ammoniation reaction comprises the following steps:

[0106] a. Preparation of raw materials and ingredients:

[0107] The raw material components and mass percentages of the ammoniated reaction thickened styrene-acrylic emulsion to be prepared are respectively:

[0108] Styrene 17.4%;

[0109] Butyl Acrylate 13.2%;

[0110] Acrylic acid 3.58%;

[0111] Emulsifier A 0.48%;

[0112] Emulsifier B 0.48%;

[0113] Initiator 0.20%;

[0114] Buffer 0.83%;

[0115] Defoamer 0.048%;

[0116] The remaining amount of deionized water;

[0117] Described emulsifier A is sodium lauryl sulfate, belongs to anionic surfactant;

[0118] The emulsifier B is an alkylphenol polyoxyethylene ether, which belongs to a nonionic surfactant;

[0119] Described initiator...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a thickening styrene-acrylic emulsion for ammonification reaction and a preparation method thereof. The styrene-acrylic emulsion comprises the following components in percentage by mass: 15-22% of styrene, 10-15% of butyl acrylate, 1-6% of acrylic acid, 0.2-0.6% of emulsifier A, 0.2-0.6% of emulsifier B, 0.1-0.5% of initiator, 0.02-0.07% of defoamer, 0.2-1% of buffering agent and the balance of deionized water. The adopted raw materials are simple and accessible; and the preparation technique is simple and easy to implement, and is low in production cost. The styrene-acrylic emulsion has certain thickness; and the coated film of the emulsion has certain binding strength, and can satisfy the requirements for application in the field of paints. The styrene-acrylic emulsion has certain glass transition temperature; and the glass transition temperature can also be designed according to the demands of the enterprise to obtain the styrene-acrylic emulsion with certain glass transition temperature. The adopted raw materials are green, environment-friendly and pollution-free, and thus, the prepared product is free of toxic and harmful substances and is green and environment-friendly.

Description

technical field [0001] The invention relates to a water-based paint and a preparation method thereof, in particular to a styrene-acrylic emulsion and a preparation method thereof, which are applied in the technical field of paint. Background technique [0002] With the strengthening of environmental protection regulations, water-based coatings are gradually replacing traditional oil-based coatings, which can not only reduce pollution, improve the operation and construction environment, but also reduce costs and save a lot of organic solvents. It has become one of the development directions of the coatings industry. Styrene-acrylic latex paint is one of the main varieties of water-based paint, which is widely used in buildings and rail transit systems. The thickener is one of the important additives for emulsion coatings and adhesives. After using it, it can not only significantly improve the apparent viscosity and thixotropy of the polymer emulsion, but also improve the cons...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08F212/08C08F220/18C08F220/06C08F2/26C08F2/30C08F8/44C09D125/14
CPCC08F8/44C08F212/08C08F2800/20C08F2810/50C09D125/14C08F220/1804C08F220/06
Inventor 周婕陈来张乃超
Owner SHANGHAI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com