One-component acrylic ester matte core-shell emulsions with good anti-water-white performance and preparation method and application thereof

An acrylate, core-shell emulsion technology, applied in the direction of biocide-containing paints, antifouling/underwater coatings, coatings, etc., can solve problems such as poor stability, achieve improved stability, simple and feasible process, and simple and easy raw materials the effect

Active Publication Date: 2017-05-03
佛山市顺德区巴德富实业有限公司
View PDF4 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the problems of two-component matte emulsion and the poor stability of the polymer after adding matting powder, the present invention provides a one-component acrylate matte core-shell emulsion with microphase separation structure, which does not need to add matting powder Powder, without mixing with other polymers, can control the gloss of the film after film formation. In practical industrial applications, the cost is low, the formation stability and storage stability are high, and it has broad application prospects.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • One-component acrylic ester matte core-shell emulsions with good anti-water-white performance and preparation method and application thereof
  • One-component acrylic ester matte core-shell emulsions with good anti-water-white performance and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A kind of one-component acrylate matte core-shell emulsion with excellent water whitening resistance, its raw material includes the following components in parts by weight: 20 parts of alkyl methacrylate (including methyl methacrylate and butyl methacrylate ester); 12 parts of alkyl acrylate (including isooctyl acrylate and butyl acrylate); 6.5 parts of vinyl monomers without -COOH groups (including styrene and acrylamide); vinyl monomers containing -COOH groups 1 part of base monomer (acrylic acid); 0.5 part of silicone monomer (vinyltrimethylsilane); 1 part of crosslinking monomer (including ethylene glycol dimethacrylate and trimethylolpropane triacrylate) 0.03 part of pH regulator (sodium hydroxide); 0.8 part of emulsifier (comprising sodium lauryl sulfate, alkyl polyoxyethylene ether (EO=10) and allyl ether sodium hydroxypropyl sulfonate); 1 part of agent (ammonium persulfate); 40 parts of deionized water.

[0039] The preparation method of the above-mentioned one...

Embodiment 2

[0050] A kind of single-component acrylate matte core-shell emulsion with excellent water whitening resistance, its raw materials include the following components in parts by weight: 15 parts of alkyl methacrylate (including methyl methacrylate and butyl methacrylate ester); 15 parts of alkyl acrylate (including ethyl acrylate and butyl acrylate); 5 parts of vinyl monomers without -COOH groups (including styrene and methacrylamide); 2 parts of vinyl monomer (methacrylic acid); 1 part of silicone monomer (methacryloxypropyl trimethoxysilane); 0.5 parts of crosslinking monomer (including allyl methacrylate and trihydroxy Methylpropane triacrylate); 0.05 parts of pH regulator (ammonia); 0.3 parts of emulsifier (including alkyl polyoxyethylene ether sodium sulfate, alkyl polyoxyethylene ether (EO=40), allyl ether hydroxypropyl Sodium sulfonate and sodium lauryl sulfate); 0.05 parts of initiator (sodium persulfate); 45 parts of deionized water.

[0051] The preparation method of t...

Embodiment 3

[0062] A one-component acrylate matte core-shell emulsion with excellent water whitening resistance, its raw materials include the following components in parts by weight: 25 parts of alkyl methacrylate (including ethyl methacrylate, butyl methacrylate esters and isooctyl methacrylate); 10 parts of alkyl acrylates (including methyl acrylate and butyl acrylate); 10 parts of vinyl monomers without -COOH groups (including styrene and N-isopropyl acrylamide); 3 parts of vinyl monomers containing -COOH groups (methacrylic acid and maleic anhydride); 2 parts of silicone monomers (vinyl tris(β-methoxyethoxy)silane); 2 parts of monomers (including allyl methacrylate and hydroxyethyl methacrylate); 0.01 parts of pH regulator (potassium hydroxide); 1.5 parts of emulsifier (including sodium dodecylbenzenesulfonate, alkyl Polyoxyethylene ether (EO=10), allyl ether sodium hydroxypropyl sulfonate and the SR-10 emulsifier of Japan Addico Corporation); 2 parts of initiator (potassium persulfa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
solid contentaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of organic macromolecular polymerization, aims to solve the problems that operation is difficult, storage is unstable, and the water resistance is poor due to the fact that overcoat varnish for conventional architectural coatings is subjected to extinction often by adding fumed silica or wax emulsion, and provides one-component acrylic ester matte core-shell emulsions with good anti-water-white performance and a preparation method and application thereof. The raw material components of the emulsions comprise alkyl methacrylate, alkyl acrylate, vinyl monomers without -COOH groups, vinyl monomers containing -COOH groups, organosilicone monomers, crosslinking monomers, a pH modifier, an emulsifier, an initiating agent and deionized water. The one-component acrylic ester matte core-shell emulsions are characterized in that after forming into films, the emulsions have a coarse structure with separated surface micro-phases through a core layer part along with the difference of the neutralization degree of the gadoleic acid functional monomer of 3-10 carbon atoms, and the emulsions with the different matte degrees are obtained. Water-based overcoat varnish prepared through the one-component acrylic ester emulsions has the advantages of good water-white resistance, storage stability, good weather resistance, low cost and the like.

Description

technical field [0001] The invention relates to the technical field of organic polymer polymerization, in particular to a one-component acrylate matte core-shell emulsion with excellent water whitening resistance and its preparation method and application. Background technique [0002] With the improvement of national living standards, there is a higher demand for architectural coatings, and exterior wall coatings have always been the focus of attention in the industry. The current exterior wall coatings are ordinary flat paint, brushed paint, and exterior wall elastic paint. , real stone paint and colorful paint. In recent years, because the decorative effect of real stone paint and granite is similar to marble and granite, it has natural and real natural color, which gives people an elegant, harmonious and solemn aesthetic feeling, and its cost is lower than that of marble, and there is no danger of falling off similar to marble; Colorful paint is a kind of colorful paint...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F220/18C08F220/14C08F212/08C08F220/56C08F220/06C08F230/08C08F222/14C08F220/54C08F220/40C08F222/06C08F220/28C09D133/10C09D133/12C09D5/16
CPCC09D133/10C09D133/12C08F220/14C08F220/18C09D5/1662C08F220/1808C08F220/1804C08F220/40C08F222/103C08F212/08C08F220/54C08F220/06C08F230/08C08F222/102C08F220/56C08F222/06C08F220/281
Inventor 张城平彭妃湛杨文涛
Owner 佛山市顺德区巴德富实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap