Anti-corrosive steel ball and preparation method thereof

A corrosion-resistant steel and corrosion-resistant technology, which is applied in the field of corrosion-resistant steel balls and their preparation, can solve the problems of harsh working environment of wear-resistant steel balls, and the corrosion resistance of ordinary steel balls cannot meet the requirements of wear-resistant steel balls, so as to increase the resistance Impact resistance, increased corrosion resistance and wear resistance, effect of increased corrosion resistance and wear resistance

Inactive Publication Date: 2016-12-07
ANHUI RUITAI NEW MATERIALS TECH
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the rapid development of domestic and foreign mining, construction, metallurgy, chemical industry, power plant, cement and other industries, the demand for wear-resistant steel balls is increasing, and the working environment of wear-resistant steel balls is getting worse and worse. The corrosion resistance of the ball can no longer meet the requirements of the above industries for wear-resistant steel balls, so it is necessary to provide a new corrosion-resistant steel ball

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A corrosion-resistant steel ball, the weight percentage of each component is as follows: C: 0.1%; Cr: 16%; Si: 0.8%; Mn: 2%; B: 0.02%; Ni: 1.5%; Cu: 0.05% ; Y: 2%; P: 0.02%; S: 0.01%; the remainder is Fe.

[0018] The preparation method of the above-mentioned corrosion-resistant steel ball includes the following steps: after melting the scrap steel, inspecting, adjusting the composition, performing rough refining, refining, and casting out of the furnace to obtain a casting whose composition meets the above range; heating the casting to 1300° C., and keeping it warm for 1.5 hours, Carry out rolling, cool to room temperature at a rate of 8°C / s, heat up to 800°C, hold for 60 minutes, quench with water at a temperature of 80°C for 20s, adjust the temperature to 180°C, hold for 6 hours, and air cool to room temperature to obtain the intermediate steel ball; Grind the middle steel ball, clean it ultrasonically with ethanol, add it to the coating solution, raise the temperatu...

Embodiment 2

[0021] A corrosion-resistant steel ball, the weight percentage of each component is as follows: C: 0.2%; Cr: 14%; Si: 1.5%; Mn: 1.5%; B: 0.03%; Ni: 0.5%; Cu: 0.07% ; Y: 1%; P: 0.018%; S: 0.009%; the remainder is Fe.

[0022] The preparation method of the above-mentioned corrosion-resistant steel ball includes the following steps: after melting the scrap steel, inspecting, adjusting the composition, performing rough smelting, refining, and casting out of the furnace to obtain a casting whose composition meets the above range; heating the casting to 1200° C., and keeping it warm for 2.5 hours, Carry out rolling, cool to room temperature at a rate of 5°C / s, heat up to 850°C, hold for 30 minutes, quench with water at a temperature of 100°C for 10s, adjust the temperature to 200°C, hold for 5 hours, and air cool to room temperature to obtain the intermediate steel ball; Grind the middle steel ball, clean it ultrasonically with ethanol, add it to the coating solution, raise the temp...

Embodiment 3

[0025] A corrosion-resistant steel ball, the weight percentage of each component is as follows: C: 0.12%; Cr: 15.5%; Si: 1%; Mn: 1.9%; B: 0.023%; Ni: 1.3%; Cu: 0.055% ; Y: 1.8%; P: 0.015%; S: 0.008%; the remainder is Fe.

[0026] The preparation method of the above-mentioned corrosion-resistant steel ball includes the following steps: after melting the scrap steel, inspecting, adjusting the composition, performing rough smelting, refining, and casting out of the furnace to obtain a casting whose composition meets the above range; heating the casting to 1270° C., and keeping it warm for 1.8 hours, Carry out rolling, cool to room temperature at a rate of 7°C / s, heat up to 810°C, hold for 50 minutes, quench with water at a temperature of 85°C for 17s, adjust the temperature to 185°C, hold for 5.8 hours, and air cool to room temperature to obtain an intermediate steel ball ; Grind the middle steel ball, ultrasonically clean it with ethanol, add it to the coating solution, raise th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an anti-corrosive steel ball. The anti-corrosive steel ball comprises, by weight, 0.1-0.2% of C, 14-16% of Cr, 0.8-1.5% of Si, 1.5-2% of Mn, 0.02-0.03% of B, 0.5-1.5% of Ni, 0.05-0.07% of Cu, 1-2% of Y, 0-0.02% of P, 0-0.01% of S, and the balance Fe. The invention further discloses a preparation method of the anti-corrosive steel ball. The anti-corrosive steel ball is good in corrosion resistance, high in wear resistance and good in mechanical property.

Description

technical field [0001] The invention relates to the technical field of steel balls, in particular to a corrosion-resistant steel ball and a preparation method thereof. Background technique [0002] With the rapid development of domestic and foreign mining, construction, metallurgy, chemical industry, power plant, cement and other industries, the demand for wear-resistant steel balls is increasing, and the working environment of wear-resistant steel balls is getting worse and worse. The corrosion resistance of the ball can no longer meet the requirements of the above-mentioned industries for wear-resistant steel balls, so it is necessary to provide a new corrosion-resistant steel ball. Contents of the invention [0003] Based on the technical problems in the background technology, the invention proposes a corrosion-resistant steel ball and a preparation method thereof. The invention has good corrosion resistance, high wear resistance and good mechanical properties. [0004...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/58C22C38/54C22C38/42C09D163/00C09D183/08C09D7/12C09D5/08
CPCC22C38/58C09D4/06C09D5/08C22C38/005C22C38/42C22C38/54
Inventor 唐荣朱冬祥阮和平赵娜娜吴玢
Owner ANHUI RUITAI NEW MATERIALS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com