Welding method of v-n microalloyed q550d plate without preheating before welding and without heat treatment after welding

A technology without heat treatment after welding and without preheating before welding, which is applied in welding equipment, arc welding equipment, metal processing equipment, etc., can solve the problem of unstable weldability of thick plates such as heat treatment, achieve small deformation and improve phase transition Speed, avoiding the effect of excessive growth

Active Publication Date: 2018-08-03
NORTHEASTERN UNIV LIAONING
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] Aiming at the problems of unstable weldability of V-N microalloyed Q550D medium-thick plates in the prior art and the need for corresponding heat treatment after welding, the present invention provides a V-N micro-alloyed Q550D medium-thick plate without preheating before welding and without heat treatment after welding The purpose of the welding method is to control the size of the welding line energy through reasonable selection of welding wire and optimization of welding process parameters, thereby avoiding the occurrence of welding cold cracks

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Welding method of v-n microalloyed q550d plate without preheating before welding and without heat treatment after welding
  • Welding method of v-n microalloyed q550d plate without preheating before welding and without heat treatment after welding
  • Welding method of v-n microalloyed q550d plate without preheating before welding and without heat treatment after welding

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] The welding method of the V-N microalloyed Q550D medium and thick plate of this embodiment without preheating before welding and without heat treatment after welding is carried out according to the following steps:

[0040] (1) Make a double V-shaped groove at the joint of the V-N microalloyed Q550D medium and thick plate to be welded, the groove angle is 30°, the blunt edge is 1mm, and the pair gap is 1.5mm; the thickness of the plate to be welded is 20mm, and the yield strength It is 651MPa, the tensile strength is 733MPa, and the elongation is 18.0%;

[0041] (2) Use 400CCR / R sandpaper to grind the groove and the surface of the plate to be welded on both sides to remove scale and rust;

[0042] (3) Fix the medium and thick plates to be welded with bolts, and then carry out Ar+CO 2 Mixed gas shielded tack welding, the welding voltage of tack welding is 20V, the welding current is 180A, the welding speed is 360mm / min, and the input energy is 6.0KJ / cm;

[0043] (4) Af...

Embodiment 2

[0047] The welding method of the V-N microalloyed Q550D medium and thick plate of this embodiment without preheating before welding and without heat treatment after welding is carried out according to the following steps:

[0048] (1) Make a double V-shaped groove at the joint of the V-N microalloyed Q550D medium and thick plate to be welded, the groove angle is 35°, the blunt edge is 2mm, and the pair gap is 2mm; the thickness of the plate to be welded is 20mm, and the yield strength is 651MPa, tensile strength 733MPa, elongation 18.0%;

[0049] (2) Use 400CCR / R sandpaper to grind the groove and the surface of the plate to be welded on both sides to remove scale and rust;

[0050] (3) Fix the medium and thick plates to be welded with bolts, and then carry out Ar+CO 2 Mixed gas shielded tack welding, the welding voltage of tack welding is 23.5V, the welding current is 196A, the welding speed is 390mm / min, and the input energy is 7.1KJ / cm;

[0051] (4) After the tack welding ...

Embodiment 3

[0055] The welding method of the V-N microalloyed Q550D medium and thick plate of this embodiment without preheating before welding and without heat treatment after welding is carried out according to the following steps:

[0056] (1) Make a double V-shaped groove at the joint of the V-N microalloyed Q550D medium and thick plate to be welded, the groove angle is 40°, the blunt edge is 2mm, and the pairing gap is 2mm; the thickness of the plate to be welded is 30mm, and the yield strength is 625MPa, tensile strength 724MPa, elongation 20.0%;

[0057] (2) Use 400CCR / R sandpaper to grind the groove and the surface of the plate to be welded on both sides to remove scale and rust;

[0058] (3) Fix the medium and thick plates to be welded with bolts, and then carry out Ar+CO 2 Mixed gas shielded tack welding, the welding voltage of tack welding is 24V, the welding current is 200A, the welding speed is 330mm / min, and the heat input=8.7KJ / cm;

[0059] (4) After the tack welding is c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of welding, and particularly relates to a welding method of non-preheating before welding and non-heat-treatment after welding of a V-N microalloying Q550D medium plate. Through selection of reasonable welding wires and optimization of welding parameters, the welding technology of non-preheating before welding and non-heat-treatment after welding is developed; a VN precipitated phase in austenite of V-N microalloying steel is used for promoting the acicular ferrite nucleation action, the toughness performance of a welding heat affected zone is improved, and the welding technology has the important significance in applying and popularizing of the V-N steel.

Description

technical field [0001] The invention belongs to the field of welding technology, and in particular relates to a welding method for a V-N microalloyed Q550D medium-thick plate without preheating before welding and without heat treatment after welding. Background technique [0002] Q550D steel is a low-alloy high-strength steel with a yield strength of 550MPa. Its components are mainly medium and thick plates. It is widely used in many fields such as oil and gas pipelines, construction machinery, bridges, ships, and coal mine hydraulic supports. At present, new production processes of Q550D hot-rolled steel plates are constantly emerging, but the related welding process lags behind the rolling process, which limits the practical application of Q550D medium and thick plates to a certain extent. [0003] The process of producing non-quenched and tempered high-strength steel by V-N microalloying combined with controlled rolling and controlled cooling (TMCP) has become increasingl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K9/16B23K33/00B23K9/235
CPCB23K9/16B23K9/235B23K33/00
Inventor 齐祥羽胡军张彬翁镭高秀华杜林秀
Owner NORTHEASTERN UNIV LIAONING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com