Soft and scratch-resistant fixed island ultrafine fiber suede leather and preparation method thereof

A technology of superfine fiber and suede, applied in the direction of improved handle fiber, fiber treatment, fabric kneading/softening treatment, etc., can solve the problem of velvet shedding, etc., and achieve the effect of good effect, beautiful appearance and high added value

Active Publication Date: 2016-12-21
HUAFON MICROFIBER SHANGHAI
View PDF9 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this method is only used for indefinite island products, and the suede leather of indeterminate island products will fall off seriously after softening.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] (1) Padding finishing agent: Dingdao superfine fiber suede leather is dipped in the finishing agent, one dipping and one padding, the liquid retention rate is 40%, and it is dried at 110°C to set the shape.

[0028] The finishing agent is composed of the following components in parts by weight:

[0029] Softener LS06 (30%) 1 part (Suzhou Liansheng Chemical Co., Ltd.)

[0030] Auxiliary DA101 1 part

[0031] Auxiliary U-100 3 parts

[0032] Deionized water···························· 100 parts

[0033] (2) Kneading: kneading the suede leather treated in step (1) in a kneading machine at a speed of 4m / min and a temperature of 25°C to obtain the soft and scratch-resistant Dingdao Microfiber suede.

Embodiment 2

[0035] (1) Padding finishing agent: Dingdao superfine fiber suede is dipped in the finishing agent, one dipping and one padding, the liquid retention rate is 50%, and it is dried at 130°C to set the shape.

[0036] The finishing agent is composed of the following components in parts by weight:

[0037] Softener 2264 (30%) 2.5 parts (Suzhou Liansheng Chemical Co., Ltd.)

[0038] Auxiliary IM6····················································· 1.5 parts (Shandong Weifang Lite Composite Materials Co., Ltd.)

[0039] Auxiliary U-100 1 part

[0040] Deionized water························ 100 parts

[0041] (2) Kneading: kneading the suede leather treated in step (1) in a kneading machine at a speed of 6m / min and a temperature of 60°C to obtain the soft and scratch-resistant Dingdao Microfiber suede.

Embodiment 3

[0043] (1) Padding finishing agent: Dingdao superfine fiber suede is dipped in the finishing agent, one dipping and one padding, the liquid retention rate is 60%, and it is dried at 110°C to set the shape.

[0044] The finishing agent is composed of the following components in parts by weight:

[0045] Softener S500...3 parts

[0046] Additive 1799L········································································································· 1.5 parts (Shanxi Sanwei Group Co., Ltd.)

[0047] Auxiliary APUD-1419B 5 parts

[0048] Deionized water··························· 100 parts

[0049] (2) Kneading: Knead the suede leather treated in step (1) in a kneading machine at a speed of 10m / min and a temperature of 80°C to obtain the soft and scratch-resistant Dingdao Microfiber suede.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses soft and scratch-resistant fixed island ultrafine fiber suede leather and a preparation method thereof. The preparation method includes the following steps that 1, fixed island ultrafine fiber suede leather is soaked in a finishing agent, padding is carried out, and then dry-shaping is carried out, wherein the finishing agent is prepared from, by weight, 0.5-10 parts of softener, 0.1-8 parts of assistant A, 1-10 parts of assistant B and 100 parts of water, the softener is one or more of organosilicone softeners and films, the assistant A is one or more of ethylene-vinyl acetate copolymer emulsion, hydroxyethyl cellulose, polyvinyl alcohol and carboxymethylcellulose, and the assistant B is waterborne polyurethane emulsion; 2, the product obtained in the step 1 is subjected to grain kneading in a grain kneading machine or an air kneading machine, and the product can be obtained. Fine hair of the suede leather is denser and full in hand feeling, and the prepared ultrafine fiber suede leather has the advantages of being soft, resistant to scratches, attractive in appearance, good in leather imitation effect and high in added value.

Description

technical field [0001] The invention relates to a superfine fiber suede, in particular to a preparation method of Dingshima superfine fiber suede. Background technique [0002] At present, the sea-island microfibers used in domestic production are divided into indeterminate island-type sea-island microfibers and fixed-island-type sea-island microfibers according to the production technology adopted. The islands in the indeterminate island-type sea-island microfibers are uncontrollable and discontinuous on the longitudinal axis. After solvent treatment, ultrafine fibers with thick and thin, irregular lengths and short lengths are formed; while the fixed-island-type sea-island ultrafine fibers The fiber is continuous on the longitudinal axis, and it is a uniform ultrafine fiber with a fixed number of islands, a uniform fineness, and a consistent length. The number of islands in the fixed island type sea island microfiber generally has several specifications such as 16 islands...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/643D06M13/50D06M15/333D06M15/09D06M15/564D06B3/18D06B15/00D06C19/00
CPCD06B3/18D06B15/00D06C19/00D06M13/50D06M15/09D06M15/333D06M15/564D06M15/643D06M2200/50
Inventor 杜明兵张其斌杨银龙胡忠杰吴勇诸葛磊韩芹彭超豪胡雪丽梁柱
Owner HUAFON MICROFIBER SHANGHAI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap