Porous concrete vegetation brick, preparation method thereof and application

A technology of porous concrete and vegetation, applied in the field of building decoration, can solve the problems of inconvenient implementation and poor effect of wall greening, and achieve the effects of excellent promotion prospects, excellent air permeability and long service life.

Inactive Publication Date: 2017-01-04
广州市绿风生物技术有限公司
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The present invention aims at the technical defects of the prior art, and provides a porous concrete vegetation brick to solve the technical problems of inconvenient implementation and poor effect of wall greening in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A kind of porous concrete vegetation brick, the raw material includes ceramsite and cement, the raw material does not contain sand, the volume ratio of aggregate and cementitious material in the raw material is 2.25, the mass ratio of water in the raw material and cementitious material is 0.25; the pH of the concrete porous brick The pH is 7.5, the porosity is 30%, the 7d compressive strength is 1.70Mpa, and the 7d flexural strength is 1.25Mpa.

[0034] On this basis, the following conditions are met:

[0035] The diameter range of the ceramsite is 5-10mm.

[0036] The holes are filled with soil for cultivation, and the thickness of the soil is 0.8 cm.

[0037] The raw material also includes coconut palm flakes.

[0038] The porous concrete vegetation brick contains plant growth fertilizer.

[0039] The present invention also provides a kind of preparation method of above-mentioned porous concrete vegetation brick, comprises the following steps:

[0040] 1) Take the...

Embodiment 2

[0046] A kind of porous concrete vegetation brick, raw material comprises ceramsite and cement, and raw material does not contain sand, and the volume ratio of aggregate and cementitious material in raw material is 2.5, and the mass ratio of water in raw material and cementitious material is 0.28; Described porous concrete vegetation brick The pH is pH7.0, the porosity is 22%, the 7d compressive strength is 2.5Mpa, and the 7d flexural strength is 1.53Mpa.

[0047] On this basis, the following conditions are met:

[0048] The diameter range of the ceramsite is 10-15mm.

[0049]The holes are filled with soil for cultivation, and the thickness of the soil is 1.2 cm.

[0050] The present invention also provides a kind of preparation method of above-mentioned porous concrete vegetation brick, comprises the following steps:

[0051] 1) Take the raw materials for the preparation of porous concrete vegetation bricks, which contain ceramsite and cement, and do not contain sand. The ...

Embodiment 3

[0057] A kind of porous concrete vegetation brick, raw material comprises ceramsite and cement, and raw material does not contain sand, and the volume ratio of aggregate and cementitious material in raw material is 2.6, and the mass ratio of water in raw material and cementitious material is 0.28; Described porous concrete vegetation brick The pH is pH7.2, the porosity is 24%, the 7d compressive strength is 2.1Mpa, and the 7d flexural strength is 1.47Mpa.

[0058] The present invention also provides a kind of preparation method of above-mentioned porous concrete vegetation brick, comprises the following steps:

[0059] 1) Take the raw materials for the preparation of porous concrete vegetation bricks. The raw materials contain ceramsite and cement and do not contain sand. The diameter range of the ceramsite shown is 5-10mm, the volume ratio of aggregate to cementitious material is 2.6, water and cementitious The material mass ratio is 0.28, and the rough product of the porous ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a porous concrete vegetation brick, a preparation method thereof and application. The product is excellent in breathability, has a certain nutritional ingredients and appropriate pH conditions and is filled with nutrient soil to plant plants. The plants completely cover a brick base frame, root systems of the plants go deep into the porous concrete brick base frame, and a decoration building material similar to a tile or cultured stone is formed. According to three-dimensional greening environmental characteristics, the prefabricated vegetation brick which can be applied to wall greening construction can be manufactured, and a convenient, quick and low-cost construction mode is provided for wall greening. In sum, the porous concrete vegetation brick is simple and practical, does not need to be fixed through a welding steel frame and is cheap in cost, economical, quick in greening effect and long in service life, the convenient, quick and low-cost construction mode can be provided for wall greening, and the porous concrete vegetation brick has an excellent popularization prospect.

Description

technical field [0001] The invention relates to the technical field of architectural decoration, in particular to a porous concrete vegetation brick, its preparation method and application. Background technique [0002] While concrete has made great contributions to my country's urbanization process, it has also created countless gray and monotonous buildings and impermeable ground, forming an urban landscape of "gray forest". Traditional concrete is neither permeable nor air permeable, which blocks the exchange of water and air on the surface, causing frequent urban waterlogging and strengthening of the heat island effect. Both at home and abroad are studying how to improve these urban problems in order to reduce environmental damage and energy waste. [0003] Wall greening is a measure for people to carry out vertical greening on building walls, walls, bridge columns, balconies, window sills, etc., so as to improve the urban ecological environment; It is a technology dev...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/00C04B28/00C05G3/00E04C1/39A01G9/02
Inventor 李晓东张俊涛阮琳刘连海吴俭峰
Owner 广州市绿风生物技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap