Flame-retardant glass flake daub

A glass flake and flame-retardant technology, which is applied in the field of flame-retardant glass flake cement, can solve the problems that remain unchanged, but the oxygen index and flame propagation speed slow down and increase, and achieve the effect of increasing the oxygen index

Active Publication Date: 2017-01-04
武汉博奇玉宇环保股份有限公司
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Flame-retardant glass flake cement is a flame-retardant upgraded version based on conventional glass flake cement. Compared with conventional glass flake cement, the mechanical properties and heat resistance of flame-retardant glass flake cement remain unchanged, but the oxygen index increases. Flame spreads slowly and is self-extinguishing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A flame-retardant glass flake cement, its raw materials are as follows by weight: 20 parts of flame-retardant epoxy vinyl ester resin, 10 parts of glass flakes, 5 parts of curing agent, 10 parts of flame retardant, 5 parts of charring agent, 2 parts of flame retardant fiber, 1 part of adhesive.

[0020] The binder is nitrocellulose.

[0021] The curing agent is formed by mixing methyl ethyl ketone peroxide and cobalt octanoate solution in a ratio of 2:1 by weight.

[0022] The char-forming agent is corn starch, and the particle size of the powder is between 800-1000.

[0023] The flame retardant is made of magnesium hydroxide and aluminum hydroxide according to the weight component ratio of 1:1, and they are all in powder form, and the powder mesh size is between 700-900.

[0024] The flame-retardant fiber is decabromodiphenylethane flame-retardant high-strength vinylon.

[0025] The binder is polyvinyl alcohol.

[0026] The flame-retardant glass flake cement reache...

Embodiment 2

[0029] A flame-retardant glass flake cement, its raw materials are as follows by weight: 23 parts of flame-retardant epoxy vinyl ester resin, 13 parts of glass flakes, 6 parts of curing agent, 12 parts of flame retardant, 6 parts of charring agent, 2.5 parts of flame retardant fiber, 1.5 parts of adhesive.

[0030] The binder is nitrocellulose.

[0031] The curing agent is formed by mixing methyl ethyl ketone peroxide and cobalt octanoate solution in a ratio of 2:1 by weight.

[0032] The char-forming agent is corn starch, and the particle size of the powder is between 800-1000.

[0033] The flame retardant is made of magnesium hydroxide and aluminum hydroxide according to the weight component ratio of 1:1, and they are all in powder form, and the powder mesh size is between 700-900.

[0034] The flame-retardant fiber is decabromodiphenylethane flame-retardant high-strength vinylon.

[0035] The binder is polyvinyl alcohol.

[0036] The flame-retardant glass flake cement r...

Embodiment 3

[0039] A flame-retardant glass flake cement, its raw materials are as follows by weight: 25 parts of flame-retardant epoxy vinyl ester resin, 15 parts of glass flakes, 8 parts of curing agent, 13 parts of flame retardant, 8 parts of charring agent, 3 parts of flame retardant fiber, 2 parts of adhesive.

[0040] The binder is nitrocellulose.

[0041] The curing agent is formed by mixing methyl ethyl ketone peroxide and cobalt octanoate solution in a ratio of 2:1 by weight.

[0042] The char-forming agent is corn starch, and the particle size of the powder is between 800-1000.

[0043] The flame retardant is made of magnesium hydroxide and aluminum hydroxide according to the weight component ratio of 1:1, and they are all in powder form, and the powder mesh size is between 700-900.

[0044] The flame-retardant fiber is decabromodiphenylethane flame-retardant high-strength vinylon.

[0045] The binder is polyvinyl alcohol.

[0046] The flame-retardant glass flake cement reach...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses flame-retardant glass flake daub. The flame-retardant glass flake daub is prepared from, by weight, 20-25 parts of flame-retardant epoxy vinyl ester resin, 10-15 parts of glass flake, 5-8 parts of curing agent, 10-13 parts of flame retardant, 5-8 parts of charring agent, 2-3 parts of flame-retardant fiber and 1-2 parts of adhesive. Compared with conventional glass flake daub, the mechanical property and heat resistance of the flame-retardant glass flake daub are unchanged, but the oxygen index is increased, the flame propagation velocity is reduced, and the flame-retardant glass flake daub has self-extinguishment performance.

Description

technical field [0001] The invention relates to the technical field of glass flake cement, in particular to a flame-retardant glass flake cement. Background technique [0002] The phenomenon that the glass phosphorus sheets used for anticorrosion in the anticorrosion project of the absorption tower of the power plant under construction or already built are burned frequently occurs. On the surface, it is caused by management reasons such as cross construction. The essential problem is that the glass flake cement has no flame retardant performance, the oxygen index is too low, and the burning speed is too fast. Once it is overfired, it has no self-extinguishing property, and it is easy to cause large-scale overfire and cause safety accidents. [0003] At present, vinyl ester resin is commonly used as the matrix resin of glass flake cement, which has excellent corrosion resistance and good processability. In addition to resin, glass flakes, curing agents, accelerators, pigmen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L63/10C08L1/18C08L3/02C08L29/04C08K13/04C08K7/00C08K3/40C08K3/22C08K5/03
CPCC08L63/10C08L2201/02C08L2201/08C08L2205/035C08L1/18C08L3/02C08L29/04C08K13/04C08K7/00C08K3/40C08K2003/2224C08K2003/2227C08K5/03
Inventor 贺朝铸周文清温韬
Owner 武汉博奇玉宇环保股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com