Blended yarn containing polytetrafluoroethylene fiber and preparation method of blended yarn
A technology of polytetrafluoroethylene and blended yarn, applied in yarn, textile and papermaking, etc., can solve the problems of easy generation of hair balls, poor fabric drape performance, poor anti-pilling performance, etc., to ensure yarn quality, Overcome the effect of strong rigidity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0061] Example 1 Preparation of blended yarn containing polytetrafluoroethylene fiber
[0062] 1. Each component formula: (weight percentage)
[0063] Aramid fiber 85%
[0064] PTFE fiber 13%
[0065] Conductive fiber 2%
[0066] 2% antistatic agent based on the total weight of PTFE fiber, aramid fiber and conductive fiber;
[0067] The yarn count is 21tex;
[0068] The PTFE fiber is selected from the JUSF-WN-S1 fiber of Shanghai Jinyou Fluorine Material Co., Ltd.;
[0069] The conductive fiber is nylon with graphite carbon inner core, and adopts P140 product of DuPont;
[0070] The antistatic agent is selected from the TS-YK3 type antistatic agent of Dongguan Tiansheng Chemical Technology Co., Ltd.
[0071] 2. The specific preparation method is as follows:
[0072] (1) Raw material pretreatment:
[0073] Spray the antistatic agent evenly on the aramid fiber and polytetrafluoroethylene fiber, and let it stand for 24 hours for health treatment;
[0074] (2) Blending step: send the pretreated raw...
Example Embodiment
[0094] Example 2 Preparation of blended yarn containing polytetrafluoroethylene fiber
[0095] 1. Each component formula: (weight percentage)
[0096] Aramid fiber 40%
[0097] PTFE fiber 10%
[0098] Flame retardant viscose fiber 48%
[0099] Conductive fiber 2%
[0100] 1.5% antistatic agent based on the total weight of aramid fiber, polytetrafluoroethylene fiber, flame-retardant viscose and conductive fiber;
[0101] The yarn count is 37tex;
[0102] The PTFE fiber is selected from the JUSF-WN-S1 fiber of Shanghai Jinyou Fluorine Material Co., Ltd.;
[0103] The conductive fiber is nylon with graphite carbon inner core, and adopts P140 product of DuPont;
[0104] The flame-retardant viscose fiber is 1.5dtex*38mm staple fiber produced by Jilin Chemical Fiber Co., Ltd.;
[0105] The antistatic agent is selected from the TS-YK3 type antistatic agent of Dongguan Tiansheng Chemical Technology Co., Ltd.
[0106] 2. The specific preparation method is as follows:
[0107] (1) Raw material pretreatme...
Example Embodiment
[0127] Example 3 Preparation of blended yarn containing polytetrafluoroethylene fiber
[0128] 1. Each component formula: (weight percentage)
[0129] Aramid fiber 48%
[0130] Flame retardant acrylic fiber 30%
[0131] PTFE fiber 20%
[0132] Conductive fiber 2%
[0133] Aramid, flame-retardant viscose fiber, polytetrafluoroethylene fiber and conductive fiber are 2% antistatic agent;
[0134] The yarn count is 14.6tex;
[0135] The PTFE fiber is selected from the JUSF-WN-S1 fiber of Shanghai Jinyou Fluorine Material Co., Ltd.;
[0136] The conductive fiber is nylon with graphite carbon inner core, and adopts P140 product of DuPont;
[0137] The flame-retardant acrylic fiber is selected from the Protex-C variety produced by Japan Carnecaron;
[0138] The antistatic agent is selected from the TS-YK3 type antistatic agent of Dongguan Tiansheng Chemical Technology Co., Ltd.
[0139] 2. The specific preparation method is as follows:
[0140] (1) Raw material pretreatment: spray the antistatic agent...
PUM
Property | Measurement | Unit |
---|---|---|
Fineness | aaaaa | aaaaa |
Length | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap