A tire and new color technology, applied in the field of tires, can solve the problems of single tire color and wear resistance performance to be improved, and achieve the effects of low production cost, improved wear resistance performance and prolonging tire life

Inactive Publication Date: 2017-02-22
姚均甫
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Young people are more and more pursuing a personalized life, and cars are also a must for our generation. In the process of car modification, only the color of the tires has not changed, so this is a good personality for young people In the era, individuality is greater than money, the color of tires in the prior art is single, and the wear resistance performance needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A new color tire, its raw materials are as follows by weight: 120 parts of natural rubber, 50 parts of high cis-butadiene rubber, 20 parts of oil-extended styrene-butadiene rubber, 5 parts of zinc oxide, 4 parts of stearic acid, 2 parts of microcrystalline wax 2 parts, accelerator 2 parts, anti-aging agent 50 parts, tackifying resin 3 parts, carbon black 48 parts, silica lime 12 parts, pigment 4 parts, sulfur 2 parts.

[0014] The accelerator is mainly a mixture of nitrogen-containing and sulfur-containing organic compounds, wherein the proportion of vulcanization accelerator H is 20%, the proportion of vulcanization accelerator D is 15%, and the proportion of vulcanization accelerator TT is 35%. , the proportion of vulcanization accelerator M is 10%, the proportion of dithiocarbamate is 15%, and the proportion of vulcanization accelerator NA-22 is 5%.

[0015] The main function of the anti-aging agent can be divided into anti-thermal oxygen aging anti-aging agent, anti...

Embodiment 2

[0019] A new color tire, its raw materials are as follows by weight: 120-130 parts of natural rubber, 55 parts of high-cis butadiene rubber, 25 parts of oil-extended styrene-butadiene rubber, 6 parts of zinc oxide, 4-6 parts of stearic acid, 2.5 parts of microcrystalline wax, 3 parts of accelerator, 52.5 parts of anti-aging agent, 3.5 parts of tackifying resin, 20 parts of carbon black, 13 parts of silica lime, 5 parts of pigment, and 2.5 parts of sulfur.

[0020] The accelerator is mainly a mixture of nitrogen-containing and sulfur-containing organic compounds, wherein the proportion of vulcanization accelerator H is 20%, the proportion of vulcanization accelerator D is 15%, and the proportion of vulcanization accelerator TT is 35%. , the proportion of vulcanization accelerator M is 10%, the proportion of dithiocarbamate is 15%, and the proportion of vulcanization accelerator NA-22 is 5%.

[0021] The main function of the anti-aging agent can be divided into anti-thermal oxyg...

Embodiment 3

[0025] A new color tire, its raw materials are as follows by weight: 130 parts of natural rubber, 60 parts of high cis-butadiene rubber, 30 parts of oil-extended styrene-butadiene rubber, 7 parts of zinc oxide, 6 parts of stearic acid, 3 parts of microcrystalline wax 4 parts, accelerator 4 parts, anti-aging agent 55 parts, tackifying resin 4 parts, carbon black 52 parts, silica lime 14 parts, pigment 6 parts, sulfur 3 parts.

[0026] The accelerator is mainly a mixture of nitrogen-containing and sulfur-containing organic compounds, wherein the proportion of vulcanization accelerator H is 20%, the proportion of vulcanization accelerator D is 15%, and the proportion of vulcanization accelerator TT is 35%. , the proportion of vulcanization accelerator M is 10%, the proportion of dithiocarbamate is 15%, and the proportion of vulcanization accelerator NA-22 is 5%.

[0027] The main function of the anti-aging agent can be divided into anti-thermal oxygen aging anti-aging agent, anti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a novel colored tire, which is prepared from the following raw materials in parts by weight: 120 to 130 parts of natural rubber, 50 to 60 parts of high-cis butadiene rubber, 20 to 30 parts of oil-extended styrene butadiene rubber, 5 to 7 parts of zinc oxide, 4 to 6 parts of stearic acid, 2 to 3 parts of microcrystalline wax, 2 to 4 parts of an accelerant, 50 to 55 parts of an anti-aging agent, 3 to 4 parts of tackifying resin, 48 to 52 parts of carbon black, 12 to 14 parts of siliceous lime, 4 to 6 parts of a pigment and 2 to 3 parts of sulfur. According to the novel colored tire, components of the raw materials are strictly controlled, a conventional tire formula is changed, and the pigment is added into the raw materials to change the color of the formed tire, so that personal pursuits of the young for colors can be greatly met according to personal preferences; the tire formula is improved, and the siliceous lime is added into the formula, so that the wear resistance of the tire is greatly improved, and the service life of the tire is prolonged; moreover, the tire has relatively low production cost and is suitable for wide popularization.

Description

technical field [0001] The invention relates to the technical field of tires, in particular to a new-color tire. Background technique [0002] Tires are one of the important parts of the car. They are in direct contact with the road surface, and work together with the car suspension to ease the impact of the car while driving, ensuring that the car has good seating comfort and smooth driving; ensuring that the wheels and the road are in good condition Adhesion, improve the traction, braking and passability of the car. Young people are more and more pursuing a personalized life, and cars are also a must for our generation. In the process of car modification, only the color of the tires has not changed, so this is a good personality for young people In the era, personality is greater than money, and the color of the tire in the prior art is single, and the wear resistance needs to be improved. Contents of the invention [0003] The purpose of the present invention is to so...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L9/00C08L9/06C08K13/02C08K3/22C08K5/09C08K3/04C08K3/34
CPCC08L7/00C08L2205/035C08L9/00C08L9/06C08K13/02C08K2003/2296C08K5/09C08K3/04C08K3/34
Inventor 姚均甫李丛林许东尧
Owner 姚均甫
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap