Blade installation seat heat treatment method

A heat treatment method and blade installation technology, which is applied in the field of heat treatment of 18Cr2Ni4WA workpieces, can solve the problems of oxidative decarburization, formation of tempered sorbite in the carburized layer, and the surface hardness of the carburized surface cannot meet the requirements, so as to control carburizing quality and production high efficiency effect

Active Publication Date: 2017-04-05
CHINA HANGFA CHANGZHOU LANXIANG MACHINERY CO LTD
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The surface hardness of the blade mounting seat used in the aero-engine has special requirements. Due to its use characteristics, local carburization is required, such as figure 1 As shown, a blade mounting seat is made of 18Cr2Ni4WA, and the Q, R, H, and G areas in the figure are required to be carburized. The surface hardness is not less than 58HRC. For the non-carburized area, the hardness requirement is not less than 33-37HRC. In the quenching process after carburizing treatment, the surface is prone to oxidative decarburization and the formation of tempered sorbite in the carburized layer, and the surface hardness of the carburized surface of the blade mounting seat cannot meet the requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Blade installation seat heat treatment method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] In the heat treatment method of the blade mounting seat in this embodiment, the blade mounting seat after quenching and tempering treatment is mechanically processed to remove the surface scale; the surface of the blade mounting seat workpiece is copper-plated to ensure that the surface of the workpiece is completely covered with a copper-plated protective film; The mounting seat is machined to remove the copper-plated protective film attached to the surface of the Q, R, H, and G areas, which is convenient for subsequent carburizing.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a blade installation seat heat treatment method. The method is characterized in that coppering treatment is carried out on the whole surface of a blade installation seat workpiece, machining is used for remove a copper layer of an area surface to be carburized, then carburizing processing is carried out, and a carburizing purpose only in a local area can be reached. While quenching heating, a solid gas carburizer is employed for protection, oxidation and decarbonization on the surface of a carburizing layer are avoided, after quenching, a moveable constant-temperature oil groove is used for substituting an original salt bath heat treatment furnace, interprocess connection time is saved, contact of the workpiece and air at high temperature is reduced, decarburization on the surface of the carburizing layer is avoided; the condition that during a quenching transfer process, the temperature of workpiece surface is reduced to lower than Ms point (180 DEG C) can be avoided; the workpiece after isothermal quenching is placed into a tempering tool case equipped with a protection medium, insulation is carried out, the condition that the temperature of workpiece surface is reduced to lower than Ms point (180 DEG C) can be avoided; at the same time, thermal conduction can be accelerated in subsequent tempering, and energy loss is reduced.

Description

technical field [0001] The invention relates to the technical field of heat treatment of 18Cr2Ni4WA workpieces, in particular to a method for heat treatment of blade mounting seats made of 18Cr2Ni4WA material. Background technique [0002] 18Cr2Ni4WA has good processability and fatigue resistance, and has relatively ideal hardenability, toughness and good carburization controllability. It is an irreplaceable material for the production of heavy-duty transmission parts. It has a wide range of applications in the aviation industry. Uses, carburizing and nitriding the surface during manufacture is a conventional method to improve the surface hardness of the workpiece. [0003] The surface hardness of the blade mounting seat used in the aero-engine has special requirements. Due to its use characteristics, local carburization is required, such as figure 1 As shown, a blade mounting seat is made of 18Cr2Ni4WA, and the Q, R, H, and G areas in the figure are required to be carburiz...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C8/04C23C8/22C21D1/22
CPCC21D1/22C21D2211/008C23C8/04C23C8/22
Inventor 利淑琴吉宜勇
Owner CHINA HANGFA CHANGZHOU LANXIANG MACHINERY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products