Screw acid pickling processing method

A processing method and technology of screw acid, applied in the coating process of metal materials, etc., can solve the problems of uneven screw thickness or thinness, affecting screw production efficiency, and uneven friction

Inactive Publication Date: 2017-04-05
明光市久鼎五金制品有限公司
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The friction is blackened, but some screw processing devices at this stage usually have different friction degrees because the grinding wheel is too cl...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] Below, the present invention will be further described in conjunction with examples.

[0016] A screw pickling processing method, comprising the steps of:

[0017] (1) Pickling: immerse the whole product in three hydrochloric acid tanks with a concentration of 20-25% at room temperature for 3-8 minutes;

[0018] (2) Clean water: Rinse with clean water to remove the corrosion products on the surface of the wire after hydrochloric acid treatment;

[0019] (3) Oxalic acid: Increase the activity of the metal to make the film formed in the next process more dense.

[0020] (4) Film treatment: The product is immersed in phosphate, the surface of the screw is in contact with the chemical treatment solution, and the screw dissolves to form an insoluble compound such as Zn 2 Fe(PO 4 ) 2 4H 2 O, attached to the steel surface to form a film;

[0021] (5) Clean water: Rinse the product treated by the film with clean water to remove the residue on the surface of the film;

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a screw acid pickling processing method. The screw acid pickling processing method comprises the steps of (1) feeding materials, wherein products needing treatment are lifted and placed in an annealing furnace, the annealing furnace is tightly covered with a furnace cover; (2) raising temperature, wherein the temperature in the annealing furnace is slowly raised to 680-760 DEG C from the normal temperature within 3-4 hours; (3) keeping the temperature, wherein if the materials are 1018 wires or 1022 wires, the temperature is kept for 4-6 hours at 680-715 DEG C, and if the materials are 10B21 wires or 1039 wires or CH38F wires, the temperature is kept for 5.5-7.5 hours at 740-760 DEG C; and (4) conducting cooling treatment, wherein the temperature in the annealing furnace is slowly lowered to 550 DEG C or below within 3-4 hours, and then the temperature of the products is lowered to the normal temperature through furnace cooling. According to the screw acid pickling processing method, the wires are heated to an appropriate temperature, the temperature is kept for a certain time, and then slow cooling is conducted; and in this way, the crystalline structure is adjusted, the hardness is lowered, and the normal temperature machining performance of the wires is improved.

Description

technical field [0001] The invention relates to a screw pickling processing method. Background technique [0002] Screws are usually blackened. For aesthetics, some screws are blackened while this is done with a grinding wheel. [0003] The friction is blackened, but some screw processing devices at this stage usually have different degrees of friction because the grinding wheel is too close or too far away from the screw, resulting in different coarse or fine specifications of the screw, which seriously affects the production efficiency of the screw. Contents of the invention [0004] The object of the present invention is to provide a screw pickling processing method, remove the oxide film on the surface of the wire, and form a layer of phosphate film on the metal surface, to reduce the damage to the tool and mold during the processing of wire drawing, cold pier or forming. scratches. [0005] In order to achieve the above object, the present invention adopts the follo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23G1/02C23C22/73
Inventor 朱功永
Owner 明光市久鼎五金制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap