A kind of abrasive liquid for stainless steel mirror panel and preparation method thereof

A mirror plate and grinding fluid technology, applied in the field of grinding fluid, can solve the problems of unreasonable proportion of process components, scratches on the processing surface, low processing efficiency, etc., and achieve good use value, high processing efficiency and low defective rate. Effect

Active Publication Date: 2018-07-24
ANHUI BAOHENG ADVANCED MATERIAL TECH CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The 8K plate is polished on the surface of the stainless steel plate by polishing equipment with abrasive liquid. Therefore, the quality of the abrasive liquid determines the quality of the product to a large extent. However, most of the existing abrasive liquids are unreasonable due to the unreasonable ratio of process components. , easy to cause scratches on the processing surface, high scrap rate, and low processing efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A kind of abrasive liquid for stainless steel mirror panel, is made of the material of following parts by weight:

[0019] 75 parts of deionized water, 8 parts of boron nitride, 1 part of aluminum oxide, 1 part of cerium oxide, 1 part of zirconia, 1 part of silicon carbide, 3 parts of rust inhibitor, 2 parts of defoamer, 1 part of glycerin, 40 parts Modified treatment liquid; the substances in the modified treatment liquid and the corresponding weight percentages are: 6% methyl methacrylate, 3% acrylamide, 2% cetyltrimethylammonium chloride, 1% hexa Sodium metaphosphate, 4% triethanolamine, 1% levulinic acid, and the balance is water.

[0020] A preparation method for a polishing liquid for a stainless steel mirror panel, comprising the steps of:

[0021] (1) First take 92% of the total mass of boron nitride, grind and pulverize it until the particle size is 3~6μm, and make powder A for later use;

[0022] (2) Mix the untreated boron nitride in step (1) with alumina, ...

Embodiment 2

[0027] A kind of abrasive liquid for stainless steel mirror panel, is made of the material of following parts by weight:

[0028] 78 parts of deionized water, 9 parts of boron nitride, 1.5 parts of alumina, 1.5 parts of cerium oxide, 1.5 parts of zirconia, 1.5 parts of silicon carbide, 4 parts of rust inhibitor, 3 parts of defoamer, 1.5 parts of glycerin, 45 parts Modified treatment liquid; the substances and corresponding weight percentages in the modified treatment liquid are: 7% methyl methacrylate, 4% acrylamide, 3% cetyl trimethyl ammonium chloride, 1.5% hexa Sodium metaphosphate, 5% triethanolamine, 2% levulinic acid, and the balance is water. All the other method steps are the same as in Example 1.

Embodiment 3

[0030] A kind of abrasive liquid for stainless steel mirror panel, is made of the material of following parts by weight:

[0031] 80 parts of deionized water, 10 parts of boron nitride, 2 parts of aluminum oxide, 2 parts of cerium oxide, 2 parts of zirconia, 2 parts of silicon carbide, 5 parts of rust inhibitor, 4 parts of defoamer, 2 parts of glycerin, 50 parts Modified treatment liquid; the substances and corresponding weight percentages in the modified treatment liquid are: 8% methyl methacrylate, 5% acrylamide, 4% cetyl trimethyl ammonium chloride, 2% hexa Sodium metaphosphate, 6% triethanolamine, 3% levulinic acid, and the balance is water. All the other method steps are the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses grinding liquid for a stainless steel mirror plate, and relates to grinding liquid. The grinding liquid is concretely prepared from the following substances including de-ionized water, boron nitride, aluminum oxide, cerium oxide, zirconium dioxide, silicon carbide, anti-rusting agents, defoaming agents, glycerol and modified treatment liquid. The prepared grinding liquid has the advantages that during the processing treatment, the rejection rate is low; the processing efficiency is higher; good use values are realized.

Description

technical field [0001] The invention relates to a grinding liquid, in particular to a grinding liquid for a stainless steel mirror panel and a preparation method thereof. Background technique [0002] Stainless steel mirror panel is also commonly known as 8K plate. It is a very good decorative material with gorgeous colors. Using it to decorate is full of elegance and luxury. 8K plate has strong corrosion resistance, high mechanical performance, and durable color surface. Fade, color and luster will have the characteristics of color change with different light angles. The 8K plate is polished on the surface of the stainless steel plate by polishing equipment with abrasive liquid. Therefore, the quality of the abrasive liquid determines the quality of the product to a large extent. However, most of the existing abrasive liquids are unreasonable due to the unreasonable ratio of process components. , It is easy to cause scratches on the processing surface, the scrap rate is hi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09K3/14
CPCC09K3/1463
Inventor 洪功正潘永刚蔡永波
Owner ANHUI BAOHENG ADVANCED MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com