POM flame retardant plastic and preparation method thereof

A technology of flame-retardant plastics and flame-retardant fibers, which is applied in the field of POM flame-retardant plastics and its preparation, can solve the problems of hydrogen halide hazards and the performance of POM flame-retardant plastics that cannot meet the requirements, and achieve low product cost, protection of human health, and durability. Excellent heat resistance and flame retardancy

Inactive Publication Date: 2017-05-31
ZHENGZHOU RENHONG PHARMA CO LTD
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the performance of the currently used POM flame retardant plastics cannot meet the requirements, and more halogen flame retardants are used, and hydrogen halides will be released during the combustion process, which will cause serious harm to the human body.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • POM flame retardant plastic and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A POM flame-retardant plastic, consisting of the following raw materials in parts by weight: 150 parts of POM resin, 25 parts of melamine, 10 parts of sodium silicate, 2 parts of bis(triphenylphosphine)palladium dichloride, and 2 parts of aluminum hydroxide , 2 parts of talcum powder, 2 parts of triallyl isocyanurate, 3 parts of potassium perrhenate, 1 part of kaolin, 0.5 part of tantalum pentoxide, 0.1 part of lanthanum hexaboride, and 2 parts of flame-retardant fiber.

[0017] A kind of preparation method of POM flame-retardant plastics, concrete steps are: (1) weigh POM resin, melamine, sodium silicate, bis(triphenylphosphine) palladium dichloride, aluminum hydroxide, talcum powder by weight parts , triallyl isocyanurate, potassium perrhenate, kaolin, tantalum pentoxide, lanthanum hexaboride, flame retardant fiber, standby; (2) put the POM resin into the vacuum granulation kneader, add Melamine, triallyl isocyanurate, sodium silicate, aluminum hydroxide and flame-ret...

Embodiment 2

[0019] A POM flame-retardant plastic, consisting of the following raw materials in parts by weight: 200 parts of POM resin, 30 parts of melamine, 15 parts of sodium silicate, 8 parts of bis(triphenylphosphine) palladium dichloride, and 5 parts of aluminum hydroxide , 5 parts of talcum powder, 8 parts of triallyl isocyanurate, 5 parts of potassium perrhenate, 3 parts of kaolin, 2 parts of tantalum pentoxide, 1 part of lanthanum hexaboride, and 10 parts of flame-retardant fiber.

[0020] A kind of preparation method of POM flame-retardant plastics, concrete steps are: (1) weigh POM resin, melamine, sodium silicate, bis(triphenylphosphine) palladium dichloride, aluminum hydroxide, talcum powder by weight parts , triallyl isocyanurate, potassium perrhenate, kaolin, tantalum pentoxide, lanthanum hexaboride, flame retardant fiber, standby; (2) put the POM resin into the vacuum granulation kneader, add Melamine, triallyl isocyanurate, sodium silicate, aluminum hydroxide and flame-ret...

Embodiment 3

[0022] A POM flame-retardant plastic, consisting of the following raw materials in parts by weight: 182 parts of POM resin, 27 parts of melamine, 12 parts of sodium silicate, 5 parts of bis(triphenylphosphine) palladium dichloride, and 3.5 parts of aluminum hydroxide , 4 parts of talcum powder, 2.8 parts of triallyl isocyanurate, 4.6 parts of potassium perrhenate, 2.8 parts of kaolin, 0.9 part of tantalum pentoxide, 0.4 part of lanthanum hexaboride, and 4 parts of flame-retardant fiber.

[0023] A kind of preparation method of POM flame-retardant plastics, concrete steps are: (1) weigh POM resin, melamine, sodium silicate, bis(triphenylphosphine) palladium dichloride, aluminum hydroxide, talcum powder by weight parts , triallyl isocyanurate, potassium perrhenate, kaolin, tantalum pentoxide, lanthanum hexaboride, flame retardant fiber, standby; (2) put the POM resin into the vacuum granulation kneader, add Melamine, triallyl isocyanurate, sodium silicate, aluminum hydroxide and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a POM flame retardant plastic and a preparation method thereof, and the POM flame retardant plastic is prepared from the following materials in parts by weight: 150 to 200 parts of POM resin, 25 to 30 parts of melamine, 10 to 15 parts of sodium silicate, 2 to 8 parts of palladium dichloride (triphenylphosphine), 2 to 5 parts of aluminium hydroxide, 2 to 5 parts of talcum powder, 2 to 8 parts of triallyl isocyanurate, 3 to 5 parts of potassium perrhenate, 1 to 3 parts of kaolin, 0.5 to 2 parts of tantalum pentoxide, 0.1 to 1 part of lanthanum hexaboride and 2 to 10 parts of fire resistant fibre. The POM flame retardant plastic provided by the invention has excellent heat resistance and flame resistance and higher tensile strength, breaking elongation, impact strength, bending strength and oxygen index; the preparation process is simple, the cost of a product is low, the comprehensive performance of the product is excellent, a halogen-flame retardant is not adopted, hydrogen halide is not emitted in a burning process, the human health is protected and the promotion value is good.

Description

technical field [0001] The invention relates to a plastic, in particular to a POM flame-retardant plastic and a preparation method thereof. Background technique [0002] With the continuous development of science and technology and economy, daily necessities made of plastics play an increasingly important role in daily life. However, plastics are easy to burn, and the burning speed is fast, and a large amount of toxic gases will be produced. With the wide application of plastics in construction, furniture, transportation, aviation, aerospace, electrical appliances, etc., at the same time, there are countless fires caused by plastic products. The fire situation is not optimistic. Some major fire accidents occur frequently, and many of them are nylon mesh, Flammable materials such as polyurethane foam burn rapidly, causing death, injury and property damage. The vast majority of plastics are flammable substances, but in plastic construction materials, transportation materials...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L59/00C08K13/04C08K5/3492C08K3/34C08K3/22C08K3/38
CPCC08L59/00C08K3/22C08K3/34C08K3/346C08K3/38C08K5/34922C08K5/34924C08K13/04C08K2003/2227C08L2201/02C08L2201/08C08L2201/22C08L2205/16
Inventor 不公告发明人
Owner ZHENGZHOU RENHONG PHARMA CO LTD
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com