Continuous sacrificial anode casting technology

A sacrificial anode and process technology, which is applied to equipment for feeding molten metal into molds, manufacturing tools, casting equipment, etc., can solve problems such as inability to realize continuous production, low production efficiency of sacrificial anodes, and uneven composition of sacrificial anodes , to achieve the effect of improving casting efficiency, increasing smelting time and ensuring internal quality

Inactive Publication Date: 2017-05-31
SHANDONG DERUI ANTI-CORROSION MATERIAL CO LTD
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] 1. The production efficiency of the sacrificial anode is low, and continuous production cannot be realized;
[0004] 2. The sacrificial anode obtained by the traditional process often has defects such as uneven composition and cracks. When it is put into use later, it is prone to the problem of poor cathodic protection performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Continuous sacrificial anode casting technology

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0032] Embodiments of the present invention are further described below:

[0033] Among the present invention, adopt continuous smelting furnace 1, holding furnace 5 and casting mold 12 to prepare sacrificial anode, specifically as figure 1 As shown, the upper end of the furnace body of the continuous smelting furnace 1 has a feeding port 2, and an automatic feeding mechanism is arranged corresponding to the feeding port 2. Launder 4, the other end of launder 4 is located at the material inlet of holding furnace 5; from one side of continuous melting furnace 1 to one side of holding furnace 5, launder 4 is inclined downward; holding furnace 5 is equipped with automatic weighing and a weighing display matched with the automatic weighing device; a permanent magnetic stirrer 6 is provided below the holding furnace 5, a feeding door is provided on the furnace body of the holding furnace 5, and a downwardly inclined casting flow is set at the outlet of the holding furnace 5 The lo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of sacrificial anode casting, and particularly relates to a continuous sacrificial anode casting technology. The technology comprises following steps: before-furnace preparing is carried out; base stocks are continuously put in a continuous casting furnace, casting is carried out, and a base stock melt is obtained; when the weight of the base stock melt entering a heat preservation furnace reaches the set value, melt supply is stopped; an alloy element and an aluminum beryllium alloy are added in the base stock melt successively, permanent magnet stirring is carried out, and molten alloy is obtained; standing and sampling are carried out, after it is analyzed that qualification is achieved, the molten alloy is poured into a casting mold, cooling is carried out, and a finished product is obtained. Continuous putting of the base stocks can be achieved, meanwhile, the amount of the base stock melt needed by casting of one sacrificial anode in the heat preservation furnace can be effectively controlled, and therefore continuous production is achieved, and the traditional sacrificial anode casting efficiency is improved; through the manner that the alloy is element is firstly added, and after the alloy element and the base stock melt are melted, the aluminum beryllium alloy is added, crystalline grains are refined, and the produced sacrificial anode is uniform in component and free of cracks.

Description

technical field [0001] The invention relates to a sacrificial anode continuous melting and casting process, which belongs to the field of sacrificial anode melting and casting. Background technique [0002] At present, when traditional sacrificial anodes are smelted, a melting furnace is used to melt the base material required for a sacrificial anode, and then the resulting base material melt flows into the holding furnace to stir and obtain an alloy melt, and finally casts to obtain a sacrificial anode product . But there are following two main problems in traditional craft: [0003] 1. The production efficiency of the sacrificial anode is low, and continuous production cannot be realized; [0004] 2. The sacrificial anode obtained by the traditional process often has defects such as uneven composition and cracks. When it is put into use later, it is prone to the problem of poor cathodic protection performance. Contents of the invention [0005] The technical problem t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C1/03B22D35/04B22D35/06
CPCC22C1/03B22D35/04B22D35/06
Inventor 逯彦伟逯颜军周家明王叶臻逯纪德
Owner SHANDONG DERUI ANTI-CORROSION MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products