A kind of lithium-ion battery diaphragm and preparation method thereof

A technology for lithium-ion batteries and diaphragms, which is applied in secondary batteries, battery pack components, secondary battery repair/maintenance, etc. It can solve the problems of poor heat resistance of diaphragms, poor adhesion of battery pole pieces, and poor flame retardancy. Achieve good adhesion, prevent battery deformation, and improve the effect of flame retardant function

Active Publication Date: 2020-02-14
CHINA LUCKY FILM CORP +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of this, the present invention provides a lithium-ion battery separator co-modified by aromatic polyamide, gel polymer and metal hydroxide to solve the problem of poor heat resistance and poor flame retardancy of the current separator and the separation between battery pole pieces. The problem of poor fit

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of lithium-ion battery diaphragm and preparation method thereof
  • A kind of lithium-ion battery diaphragm and preparation method thereof
  • A kind of lithium-ion battery diaphragm and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0035] 3. Preparation method of functional coating modified lithium-ion battery separator

[0036] The invention adopts a wet coating method to prepare a functional coating modified lithium ion battery separator, and the wet coating method is a well-known method for preparing a microporous membrane or a microporous coating.

[0037] (1) Dissolving aromatic polyamide and gel polymer in a certain mass ratio in a solvent respectively, then mixing the two, adding metal hydroxide after mixing evenly, and obtaining a coating liquid after high-speed shearing and stirring. Wherein, the solid content of the coating liquid is 10%-25%.

[0038] (2) Using the polyolefin microporous membrane as the coating substrate, coating the coating solution prepared in step 1 on the surface of the polyolefin microporous membrane to obtain a film A containing a multifunctional coating.

[0039]The method of coating the coating liquid on the surface of the polyolefin microporous membrane is not particu...

Embodiment 1

[0050] (1) Dissolve 90 grams of meta-aramid fibers with a molecular weight of 200,000 and 10 grams of PVDF with a molecular weight of 150,000 in 473.67 grams of DMAc, then mix the two, add 5.26 grams of magnesium hydroxide after mixing, and use high-speed After shearing and stirring, a coating liquid was obtained. At this time, the solid content of the coating solution was 10%, and the mass ratio of inorganic particles to organic substances was 5:95.

[0051] (2) The coating solution was coated on the surface of the PE base film with a thickness of 9 μm by a micro-gravure coating method to obtain a double-sided coated film A.

[0052] (3) The film A was immersed in a coagulation bath with water:EG:DMAc ratio of 80:15:5 for 10 seconds to obtain a film B containing a microporous structure coating.

[0053] (4) Dip the film B into water, stay for 15 seconds, remove the organic solvent on the surface of the film, and dry at 70° C. to obtain the lithium-ion battery separator conta...

Embodiment 2

[0056] (1) 40 grams of meta-aramid fibers with a molecular weight of 300,000 and 60 grams of PVDF with a molecular weight of 150,000 are dissolved in 583.33 grams of DMF respectively, then the two are mixed, and 400 grams of magnesium hydroxide are added after mixing. After shearing and stirring, a coating liquid was obtained. At this time, the solid content of the coating solution was 30%, and the mass ratio of inorganic particles to organic substances was 80:20.

[0057] (2) The coating solution was coated on the surface of the PE base film with a thickness of 9 μm by a micro-gravure coating method to obtain a double-sided coated film A.

[0058] (3) The film A was immersed in a coagulation bath of water: EG: DMAc ratio of 60:25:15 for 10 seconds to obtain a film B containing a microporous structure coating.

[0059] (4) Dip the film B into water, stay for 15 seconds, remove the organic solvent on the surface of the film, and dry at 70° C. to obtain the lithium-ion battery ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a lithium-ion battery diaphragm, comprising a polyolefin microporous membrane and at least one side of a functional coating coated on the polyolefin microporous membrane, the functional coating is composed of aromatic polyamide, gel polymer, metal It is composed of hydroxides, and has the properties of high temperature resistance, combustion resistance, and easy bonding with battery pole pieces; the lithium-ion battery separator has a fusing temperature ≥ 210 ° C, and a limiting oxygen index ≥ 23%. During the battery hot pressing process, Good adhesion to the battery pole piece. The invention not only has a simple preparation method and is easy to operate, but also can remarkably improve the overall use stability of the battery.

Description

technical field [0001] The invention relates to the technical field of lithium ion batteries, in particular to a lithium ion battery diaphragm and a preparation method thereof. Background technique [0002] As one of the four major materials of lithium-ion batteries, the separator is a key inner layer component in lithium-ion batteries, although it does not participate in the electrochemical reactions in the battery. The main function of the separator is to isolate the positive and negative electrodes and prevent electrons from passing through, while allowing ions to pass through, thereby completing the rapid transmission of lithium ions between the positive and negative electrodes during charge and discharge. The performance of the separator determines the interface structure and internal resistance of the battery, which directly affects the capacity, cycle and safety performance of the battery. A separator with excellent performance plays an important role in improving the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M2/14H01M2/16H01M10/42H01M10/0525H01M50/403H01M50/417H01M50/437H01M50/443H01M50/489H01M50/491
CPCH01M10/4235H01M10/0525H01M50/403H01M50/446H01M50/411Y02E60/10
Inventor 高甲安曼胡素芳赵义丽赵伟建程媛
Owner CHINA LUCKY FILM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com