Light brick and manufacturing method thereof
A lightweight brick and cement technology, applied in the field of building materials, can solve problems such as the strength of lightweight bricks not meeting the compressive standard, the product quality not meeting the standard for use, and the difference in raw materials and proportioning, etc., achieving significant economic benefits and social benefits, low cost, and small bulk density
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0024] A lightweight brick, which includes the following raw materials in parts by weight: 10 parts of olivine, 30 parts of glass, 30 parts of cloth, 30 parts of kitchen waste, 30 parts of weeds, 10 parts of waste batteries, 10 parts of fly ash, cement 40 servings.
[0025] The kitchen waste is a mixture of leftovers, bones, vegetables and leaves. Described cement selects 325# ordinary Portland cement for use.
[0026] A method for manufacturing lightweight brick of the present invention, it comprises the following steps:
[0027] A. Crush the above weight parts of glass, cloth, weeds, kitchen waste and waste batteries to below 200 mesh, mix with the above weight parts of olivine powder, granulate, bake at 1000°C for 60 minutes, and cool to get roasted particles;
[0028] B. Stir the calcined particles obtained in step A with the cement and fly ash of the above weight parts in a mixer to obtain a mixed material;
[0029] C. Add water accounting for 5% by weight of the mixe...
Embodiment 2
[0033] A lightweight brick, which includes the following raw materials in parts by weight: 20 parts of olivine, 40 parts of glass, 40 parts of cloth, 40 parts of kitchen waste, 40 parts of weeds, 20 parts of waste batteries, 30 parts of fly ash, cement 50 servings.
[0034] The kitchen waste is a mixture of peel and shell. Described cement selects the ordinary portland cement of 425# for use.
[0035] A method for manufacturing lightweight brick of the present invention, it comprises the following steps:
[0036] A. Crush the above weight parts of glass, cloth, weeds, kitchen waste and waste batteries to less than 200 meshes, mix with the above weight parts of olivine powder, granulate, bake at 1500°C for 120 minutes, and cool to get roasted particles;
[0037] B. Stir the calcined particles obtained in step A with the cement and fly ash of the above weight parts in a mixer to obtain a mixed material;
[0038] C. Add water accounting for 20% by weight of the mixed material...
Embodiment 3
[0042] A lightweight brick, which includes the following raw materials in parts by weight: 15 parts of olivine, 35 parts of glass, 35 parts of cloth, 35 parts of kitchen waste, 35 parts of weeds, 15 parts of waste batteries, 20 parts of fly ash, cement 45 servings.
[0043] The kitchen waste is a mixture of leftovers, bones, vegetable roots and leaves, peels and shells.
[0044] Described cement selects the ordinary portland cement of 325# for use.
[0045] A method for manufacturing lightweight bricks of the present invention, it comprises the following steps:
[0046] A. Crush the glass, cloth, weeds, kitchen waste, and waste batteries in the above parts by weight to less than 200 meshes, mix them with the olivine powder in the above parts by weight, and then granulate them, bake them at 1200°C for 90 minutes, and cool them down to get roasted particles;
[0047] B. Stir the calcined particles obtained in step A with the cement and fly ash of the above weight parts in a m...
PUM
Property | Measurement | Unit |
---|---|---|
density | aaaaa | aaaaa |
compressive strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction